Evaluation of aminoalkylmethacrylate nanoparticles as colloidal drug carrier systems. Part I: Synthesis of monomers, dependence of the physical properties on the polymerization methods.

Conventional nanoparticles based on acrylic compounds are lipophilic and possess a negative surface charge. This is due to their manufacturing process and to the chemical structure of the polymer. Hence, these particles are not suitable for the adsorption of hydrophilic anionic drugs. In the present investigation, positively charged copolymer nanoparticles prepared from aminoalkyl- and methylmethacrylates were evaluated, with regard to their physical properties. This report provides a detailed description of the synthesis of the non-commercially available monomers and their polymerization procedure. Various parameters were investigated, such as comonomer content, total amount of monomer, concentration of the radical initiator, and the composition of the polymerization medium. The resulting particle diameter and the surface charge were found to be strongly dependent on the polymerization conditions and on the pH. Optimization of the polymerization procedure yielded nanoparticles of about 200 nm exhibiting a positive surface charge. The charges of the different copolymer particles were then compared at different pH values. N-trimethylaminoethylmethacrylate (TMAEMC) nanoparticles with quaternary ammonium groups located at their surfaces, possessed a nearly constant positive zeta potential at various pH values and, consequently, pH-independent particle diameters. The physical characteristics of the other aminoalkyl copolymers correlated with the basicity of the monomers employed and were found to be strongly dependent on the pH of the dispersion medium. Aminoethylmethacrylate (AEMC), methylaminoethylmethacrylate (MMAEMC), and aminohexylmethacrylate (AHMC) as well as aminoethylmethacrylamide (AHMAC) copolymer nanoparticles exhibited a strong positively charged surface even at physiological pH and, therefore, are useful candidates for the adsorption of anionic drugs.

Enhanced antisense efficacy of oligonucleotides adsorbed to monomethylaminoethylmethacrylate methylmethacrylate copolymer nanoparticles.

The purpose of this study was the investigation of cationic nanoparticles as drug delivery systems for antisense oligonucleotides. Cationic monomethylaminoethylmethacrylate (MMAEMA) copolymer nanoparticles were prepared from N-monomethylaminoethylmethacrylate hydrochloride and methylmethacrylate. Oligonucleotides were adsorbed onto MMAEMA nanoparticles. Cell penetration was investigated in vitro with fluorescently labeled oligonucleotides and nanoparticles. Antisense effects of oligonucleotides adsorbed to MMAEMA nanoparticles were evaluated by sequence specific inhibition of ecto-5'-nucleotidase expression. The amount of enzyme expressed in PC12 cells was detected and quantified by immunocytochemistry using fluorescein isothiocyanate-labeled antibodies. Oligonucleotides were adsorbed to MMAEMA nanoparticles by the formation of ion-pairs between the positively charged secondary amino groups located on the particle surface and the anionic phosphodiester or phosphorothioate backbones of the oligonucleotides. Adsorption to nanoparticles led to an increased cellular uptake of oligonucleotides and to a significantly enhanced antisense efficacy of unmodified phosphodiester oligonucleotides as well as phosphorothioates. The results of the cell penetration and the antisense assay demonstrated that MMAEMA nanoparticles are promising carriers for oligonucleotide administration.

Evaluation of aminoalkylmethacrylate nanoparticles as colloidal drug carrier systems. Part II: characterization of antisense oligonucleotides loaded copolymer nanoparticles.

Aminoalkylmethacrylate methylmethacrylate copolymer nanoparticles were evaluated for their use as potential drug carrier systems. Their cytotoxicity, as well as the loading of antisense oligonucleotides that were employed as anionic model drugs depended on the substitution of the basic aminoalkyl copolymer. Toxic influences on the integrity of cell membranes depended on aminoalkyl groups located on the particle surfaces. Toxicity was observed either by 3-[4,5-dimethylthiazol-2-yl]-2,5-diphenyltetrazolium bromide (MTT) assays using African green monkey kidney (AGMK) cells or by a hemolysis test, where the efflux of haemoglobin from disrupted erythrocytes was measured. The cytotoxic effects were increased by the elongation of the N-alkyl chain by four additional methylene groups. Lipophilic polymethylmethacrylate (PMMA) homopolymer nanoparticles showed a negative surface charge and, therefore, were not suitable for the adsorption of anionic drugs. The surface charge was changed to positive values by the incorporation of basic monomers. Consequently, the loading efficacy was increased by raising the basic copolymer portion. Additionally, a pH-dependent loading behaviour of oligonucleotides was observed. Substitution of the amino nitrogen protons by methyl groups led to a decreased oligonucleotide loading and to a reduced cytotoxicity. Nanoparticles with permanent positively charged quarternary ammonium groups showed a high pH-independent loading efficacy, but also possessed a high cytotoxic potential. In this study, cationic copolymer nanoparticles containing 30% (w/w) methylaminoethyl-methacrylate (MMAEMC) were found to be optimal with regard to biocompatibility and carrier properties for hydrophilic anionic antisense oligonucleotides. A significant portion of adsorbed oligonucleotides were protected from enzymatic degradation. The cellular uptake of oligonucleotides into Vero cells was significantly enhanced by this methylaminoethyl-methacrylate derivative.

Cationic polyhexylcyanoacrylate nanoparticles as carriers for antisense oligonucleotides.

After antisense oligodeoxynucleotides (ODNs) were suggested for therapeutic use in 1978, major advances were made in developing modified oligonucleotides with increased nuclease resistance and improved cellular uptake. In the present report, positively charged nanoparticles prepared from diethylaminoethyl (DEAE)-dextran and polyhexylcyanoacrylate (PHCA) were evaluated as carriers for ODNs. The oligonucleotides were analyzed by anion-exchange HPLC. The nanoparticles exhibited a high loading capacity, with approximately 35 mumol ODNs adsorbed per gram of polymeric material. The adsorption efficacy was found to be dependent on the pH, on the ionic strength of the medium, and on the amount of DEAE-dextran. Highest loading for ODNs was achieved at pH 5.5, using a 10 mM phosphate buffer. Oligonucleotides adsorbed to the surface of the nanoparticles were nearly completely protected against degradation by the endonuclease DNase I and under in vitro cell culture conditions, whereas unprotected ODNs were totally digested under these conditions. Nanoparticles led to a 20-fold increase in cellular uptake of FITC-oligonucleotides. The internalized oligonucleotides were frequently localized as vesicular structures in the cytoplasmatic compartment. Because of their temperature-dependent uptake, we propose an active uptake mechanism, such as endocytosis, for the internalization of the ODN-nanoparticle formulations.

Effect of ultrasonication on the stability of oligonucleotides adsorbed on nanoparticles and liposomes.

In the present study, oligonucleotides were adsorbed onto the surface of cationic liposomes and nanoparticles at different ratios. As a result, the surface charges of the colloidal carriers were decreased with increasing oligonucleotide concentration. At a certain oligonucleotide concentration, complete charge neutralization led to the aggregation of the carrier systems. Further increasing oligonucleotide concentrations reversed the surface charge of liposomes and nanoparticles to a negative one. Ultrasonication was investigated as a possible means for the homogenization of the formed aggregates. However, the use of ultrasonication led to a time-dependent damage of oligonucleotides adsorbed onto AH-Chol liposomes and MMAEMC-nanoparticles, as well as of unbound oligonucleotides. Nearly 60% of the oligonucleotides adsorbed to MMAEMC-nanoparticles and 65% of ODNs adsorbed to the liposomes were degraded by the effect of cavitation produced by ultrasonication within 10 min. In contrast, the oligonucleotides were protected from degradation when DEAE-stabilized PHCA-nanoparticles were employed as ODN carriers. More than 80% of the oligonucleotides entangled in the surface matrix of these nanoparticles remained intact.