Effect of biofilm exposure on marginal integrity of composite restorations.

PURPOSE: To evaluate the effect of bacterial exposure on the marginal integrity of dentin-resin interfaces for composites with and without bioactive glass (BAG). METHODS: Cavity preparations of 5 mm width and 1.5 mm depth were machined into dentin disks by means of a computer controlled milling system. After applying the bonding agent, cavity preparations (n=3-5) were restored by incremental technique with experimental resin composites (50:50 BisGMA/TEGDMA: 72wt% filler) with different filler compositions: control - 67 wt% silanated strontium glass and 5wt% aerosol-silica filler and BAG - 57 wt% silanated strontium glass and 15 wt% BAG-65 wt% silica. Samples were then stored in sterile Todd-Hewitt media or co-incubated with Streptococcus mutans (UA 159), at 37°C, 5% CO2 for 1-2 weeks. For samples co-incubated with a living biofilm, a luciferase assay was performed in order to assess its viability. Surfaces were impressed before and after each storage condition and replicas examined in a scanning electron microscope. Using image analysis software (Image J), the discontinuous margins percentage (%DM) was quantitatively assessed. Data were analyzed using two-way ANOVA followed by Tukey's test (α= 0.05). RESULTS: Gap size ranged between 7-23 µm. The bacterial exposure significantly increased the %DM in both groups predominantly due to the formation of new gap regions. There was no difference between control and BAG composites regarding %DM and the biofilm viability. Bacterial exposure promoted degradation of composite restoration marginal integrity, with no difference between composites with and without BAG. CLINICAL SIGNIFICANCE: The samples incubated with living biofilm had a higher gap percentage in the margins, confirming the negative effect of cariogenic bacteria on margin degradation. The parameters defined for such synergy can help to understand the multi-factorial aspect of marginal discontinuity and therefore, predict the behavior of composite restorations subjected to the challenging oral environment.

Antimicrobial potential of resin matrices loaded with coffee compounds.

This study evaluated the biological behavior of the coffee compounds Trigonelline (T), chlorogenic acid (C), and nicotinic acid (N), correlating with their release from a resin matrix. Minimum inhibitory concentration (MIC) was evaluated against Streptococcus mutans UA159, and cytotoxicity was assessed by methyl tetrazolium salt on OD-21 cells. Resin matrices (bisphenol A-glycidyl-dimethacrylate/triethylene glycol-dimethacrylate 70/30 wt%, camphorquinone/ethyl 4-dimethyl aminobenzoate 0.5/1 wt%) were doped with coffee compounds in different concentrations (10/20/30/40/50 wt%), performing 15 groups (T10-T50, C10-C50, N10-N50), and a control group with no coffee compound. Degree of conversion (DC%) was analyzed by Fourier transform infrared spectroscopy. Antimicrobial properties were evaluated by bioluminescence (Luciferase assay). The release from loaded matrices was analyzed over time (24 hr, 6, 14, 21 and 28 days), using high-performance liquid chromatography (HPLC). Data were submitted to ANOVA/Tukey's test (α = 0.05). MIC for T and C was 6 mg/ml, and 4 mg/ml for N. None of them were cytotoxic. Only T50 and C50 showed lower DC% than control (α < 0.05). Some groups (T30/T40/T50/C40/C50/N50) were strongly antimicrobial, reducing bacterial activity approximately five times compared to control (α < 0.05). For T30, T40, T50, C40, and C50, the HPLC showed a release above or closer to MIC values mainly in 24 hr, but for N50, up to 28 days. In conclusion, the coffee compounds presented antimicrobial activity, depending on their concentration when added in resin matrices, being found a correlation with their release.