Effect of multiple firings on optical and mechanical properties of Virgilite-containing lithium disilicate glass-ceramic of varying thickness.

OBJECTIVES: To investigate the effect of multiple firings on color, translucency, and biaxial flexure strength of Virgilite-containing (Li0.5Al0.5Si2.5O6) lithium disilicate glass ceramics of varying thickness. MATERIALS AND METHODS: Sixty discs were prepared from Virgilite-containing lithium disilicate blocks. Discs were divided according to thickness (n = 30) into T0.5 (0.5 mm) and T1.0 (1.0 mm). Each thickness was divided according to the number of firing cycles (n = 10); F1 (Control group): 1 firing cycle; F3: 3 firing cycles, and F5: 5 firing cycles. The discs were tested for color change (ΔE00) and translucency (TP00) using a spectrophotometer. Then, all samples were subjected to biaxial flexure strength testing using a universal testing machine. Data were collected and statistically analyzed (α = 0.5). For chemical analysis, six additional T0.5 discs (2 for each firing cycle) were prepared; for each firing cycle one disc was subjected to X-ray diffraction analysis (XRD) and another disc was subjected to Energy dispersive X-ray spectroscopy (EDX) and Scanning electron microscope (SEM). RESULTS: Repeated firing significantly reduced the translucency of F3 and F5 compared to F1 in T0.5 (p < 0.001), while for T1.0 only F5 showed a significant decrease in TP00 (p < 0.001). For ΔE00, a significant increase was recorded with repeated firings (p < 0.05) while a significant decrease resulted in the biaxial flexure strength regardless of thickness. CONCLUSIONS: Repeated firings had a negative effect on both the optical and mechanical properties of the Virgilite-containing lithium disilicate glass ceramics. CLINICAL RELEVANCE: Repeated firings should be avoided with Virgilite-containing lithium disilicate ceramics to decrease fracture liability and preserve restoration esthetics.

Effect of aging and fiber-reinforcement on color stability, translucency, and microhardness of single-shade resin composites versus multi-shade resin composite.

OBJECTIVE: The purpose of this study was to evaluate the effect of aging and fiber-reinforcement on the color stability, translucency, and microhardness of single-shade resin composites versus multi-shade resin composite. MATERIALS AND METHODS: Four resin composites (Filtek Z250, Omnichroma, Vittra APS Unique, Zenchroma) were tested. Three subgroups of specimens were prepared for each of the composites: control, polyethylene fiber-reinforcement, and glass fiber-reinforcement- groups (n = 10/per group). The samples were subjected to aging for 10,000 thermal cycles. Color differences (ΔE00 ) were calculated after aging. Relative translucency parameter (RTP00 ) and microhardness values were calculated before and after aging. A two-way analysis of variance and the generalized linear model was used (p < 0.05). RESULTS: The lowest and highest ΔE00 values were found for Filtek Z250 (0.6 ± 0.2) and Omnichroma resin composites (1.6 ± 0.4), respectively. The ΔE00 value of the polyethylene fiber-reinforcement group (1.2 ± 0.6) was significantly higher than the ΔE00 value of the glass fiber-reinforcement group (1.0 ± 0.4, p < 0.001). The RTP00 value of the glass fiber-reinforcement group (1.92 ± 0.78) was significantly higher than the RTP00 value of the polyethylene fiber-reinforcement group (1.72 ± 0.77, p < 0.001). The highest microhardness values were found in glass fiber-reinforcement group (76.48 ± 17.07, p < 0.001). CONCLUSION: Single-shade resin composites were more translucent, had higher color change, and lower hardness than multi-shade resin composite. For relative translucency and microhardness, statistical significance was found in the material and fiber type interaction. The glass fiber-reinforcement provided higher translucency, lower color change and higher microhardness values than polyethylene fiber-reinforcement group after aging. Thermocycling had a significant impact on the color stability, translucency parameter, and microhardness of the tested resin composite materials. CLINICAL SIGNIFICANCE: Single-shade resin composite materials have greater color-changing potential. The glass fiber-reinforcement optimize resin material mechanical properties and color stability more than polyethylene fiber-reinforcement.

Color stability of bleached tooth enamel brushed with different stain-removing toothpastes.

OBJECTIVE: The effects of four toothpastes on the color stability of in-office bleached tooth specimens were determined. MATERIALS AND METHODS: We evaluated an experimental toothpaste (EXP) and three commercially available toothpastes: Colgate Optic White (OPW), Aquafresh White & Protect (AWP), and Crest 3D White (CDW). OPW, AWP, and CDW contained inorganic abrasives, whereas EXP and AWP contained sodium polyphosphate. Forty-eight randomly selected human-extracted maxillary central incisors were bleached and brushed twice daily over 30 days. We analyzed the final color difference (ΔE*ab, ΔE00 , ΔWID ), arithmetic average surface roughness (Ra) of the enamel measured on days 0 and 30, and scanning electron microscopy images of enamel surfaces and toothpastes. ΔE*ab, ΔE00 , ΔWID , and Ra were analyzed using one-way analysis of variance and Tukey's test (α = 0.05). RESULTS: ΔE*ab and ΔE00 values were significantly lower after toothbrushing with EXP, OPW, and CDW than with AWP. OPW induced the greatest positive ΔWID . Ra was significantly increased by OPW and CDW, but slightly increased by AWP, with cube-like particles, and EXP, with no particle-like structures. CONCLUSIONS: Only EXP stabilized the color of bleached teeth without increasing the enamel surface roughness. Sodium polyphosphate with approximately 10 phosphate groups was effective at removing stains. CLINICAL SIGNIFICANCE: The effect of toothpaste on the color stability of bleached teeth depends on the constituting abrasives and chemical components. Polyphosphoric acid has different stain-removal effects depending on its degree of polymerization. Additionally, although certain types of abrasives may be effective for color stability, they also increase the surface roughness of the enamel.

The Impact of Modeling Liquids on Surface Roughness and Color Properties of Bulkfill Resin Composites After Simulated Tooth Brushing: An in Vitro Study. Part I.

OBJECTIVE: To evaluate the effect of different modeling agents on color changes, surface roughness, and translucency parameters over time in Bulkfill resin composites. MATERIAL AND METHODS: Sixty specimens were prepared using three Bulkfill resin composites (Tetric N-Ceram Bulkfill, Filtek One Bulkfill and Opus Bulkfill) and three modeling agents (Wetting Resin, Optibond FL and Ambar APS). All specimens were subjected to a simulated tooth-brushing (Baseline, 50.000 cycles, 100.000 cycles), and surface roughness was measured at each interval. Surface topography was evaluated. The translucency parameter and color changes were assessed after 24-h, 7-, 14- and 30-day immersion in water, wine, and coffee. Data was analyzed using ANOVA and Bonferroni test. RESULTS: All specimens increased roughness after simulated tooth-brushing (p < 0.05). Wetting Resin decreased roughness on Tetric N-Ceram Bulkfill (p < 0.05). The translucency parameter remained unaltered for all groups. All groups changed color after 30-days of immersion in wine and coffee (p < 0.05). Ambar APS and Wetting Resin on Tetric N-Ceram Bulkfill showed higher color changes when immersed in coffee (p < 0.05). CONCLUSION: The use of modeling agents does not jeopardize translucency properties but may affect surface roughness and color properties of Bulkfill resin composites depending on their composition. CLINICAL SIGNIFICANCE: The findings of this study suggest that surface roughness and color properties are affected by the differences in the composition between modeling agents and Bulkfill resins composites.

Studying the Stability of Anthocyanin Pigments Isolated from Juices of Colored-Fleshed Potatoes.

The aim of this study was to obtain extracts of anthocyanin pigments from red and purple-fleshed potato juices characterized by stable color. For this purpose, potato juices were pasteurized at different temperatures or fruit and vegetable concentrates were added to them. Color stability tests of the obtained pigments were carried out in model pH and temperature conditions and after adding to natural yogurt. Both the pasteurization process and the addition of fruit and vegetable concentrates to the potato juices positively affected their color and its stability in time. However, the pasteurization of the potato juices had a negative effect on the content of biologically active compounds, in contrast to the juices stabilized with the addition of fruit and vegetable concentrates. Anthocyanin pigments from red-fleshed potato juices were more stable than those isolated from the purple-fleshed potato juices. The results of model tests of the anthocyanin pigment concentrates from the colored-flesh potatoes and natural yoghurts with their addition confirmed the high stability of the tested concentrates.

Chitosan/Polyvinyl Alcohol-Based Biofilms Using Ternary Deep Eutectic Solvents towards Innovative Color-Stabilizing Systems for Anthocyanins.

Anthocyanins are amazing plant-derived colorants with highly valuable properties; however, their chemical and color instability issues limit their wide application in different food industry-related products such as active and intelligent packaging. In a previous study, it was demonstrated that anthocyanins could be stabilized into green plasticizers namely deep eutectic solvents (DESs). In this work, the fabrication of edible films by integrating anthocyanins along with DESs into biocompatible chitosan (CHT)-based formulations enriched with polyvinyl alcohol (PVA) and PVA nanoparticles was investigated. CHT/PVA-DES films' physical properties were characterized by scanning electron microscopy, water vapor permeability, swelling index, moisture sorption isotherm, and thermogravimetry analysis. Innovative red-to-blue formulation films were achieved for CHT/PVA nanoparticles (for 5 min of sonication) at a molar ratio 1:1, and with 10% of ternary DES (TDES)-containing malvidin-3-glucoside (0.1%) where the physical properties of films were enhanced. After immersion in solutions at different pH values, films submitted to pHs 5-8 were revealed to be more color stable and resistant with time than at acidic pH values.

Influence of in-office whitening on the color matching and surface characteristics of single-shade resin composites.

OBJECTIVE: The color matching of single-shade resin composites after in-office whitening was investigated. MATERIALS AND METHODS: Four single-shade resin composites were used. A total of 35% hydrogen peroxide was used as the whitening agent. The resin composite was placed in a cavity of an artificially discolored bovine tooth. The color differences between the restoration and surrounding enamel before and after whitening were determined based on ΔE*ab, ΔE00, and ΔWID. The color stability, surface roughness (Sa), and surface gloss (GU) of the resin composite alone were also evaluated. Statistical analyses were performed using repeated-measures analysis of variance with the Tukey-Kramer test. RESULTS: Based on the 50:50% of perceptibility and acceptability thresholds of ΔE*ab and ΔE00, none of the resin composite restorations were clinically acceptable before or after whitening. Regarding ΔWID, although all resin composites showed "acceptable match" in the baseline, they showed "mismatch" after the third session of whitening. Most of the resin composites alone were stable in color against whitening. CONCLUSIONS: Although the single-shade resin composites failed to achieve the expected color matching on discolored teeth either before or after the whitening, the impact of the whitening on the color of the resin composite alone may be negligible.

The influence of the addition of titanium oxide nanotubes on the properties of 3D printed denture base materials.

INTRODUCTION: In this study, the effects of adding titanium dioxide nanotubes (TiO2) to 3D-printed denture base resin on the mechanical and physical properties of denture bases were examined for the first time. METHODS: The specimens were digitally created using 3D builder software from Microsoft Corporation through computer-aided design. In accordance with the test specifications for transverse strength, impact strength, hardness, surface roughness, and color stability, specimens were designed and printed with certain dimensions following relevant standards. TiO2 nanotubes (diameter: 15-30 nm and length: 2-3 µm) were added to the 3D-printed denture base resin (DentaBase, Asiga, Australia) at 1.0% and 1.5% by weight. Flexural strength, impact strength (Charpy impact), hardness, surface roughness, and color stability were evaluated, and the collected data were analyzed with ANOVA followed by Tukey's post hoc test (α = 0.05). Field emission scanning electron microscopy (FESEM) and energy dispersive x-ray spectroscopy (EDX) mapping were used to evaluate the dispersion of the nanotubes. RESULTS: Compared with those of the control group (0.0 wt.% TiO2 nanotubes), the average flexural, impact, and hardness values of the 1.0 and 1.5 wt.% TiO2 nanotube reinforcement groups increased significantly. Both nanocomposite groups showed significant color changes compared to that of the pure resin, and there was a considerable reduction in the surface roughness of the nanocomposites compared to that of the control group. CONCLUSION: Adding TiO2 nanotubes to 3D-printed denture base materials at 1.0 and 1.5 wt.% could enhance the mechanical and physical properties of the material, leading to better clinical performance. CLINICAL SIGNIFICANCE: In terms of clinical applications, 3D-printed denture base material has been shown to be a viable substitute for traditional heat-cured materials. By combining this with nanotechnology, existing dentures could be significantly enhanced, promoting extended service life and patient satisfaction while addressing the shortcomings of the current standard materials.

Semisynthesis of Betaxanthins from Purified Betacyanin of Opuntia dillenii sp.: Color Stability and Antiradical Capacity.

The availability of pure individual betalains in sufficient quantities which permit deeper understanding is still a challenge. This study investigates the high-yielding semisynthesis of betaxanthins using betalamic acid from a natural source (Opuntia dillenii), followed by condensation with ʟ-amino acids and further purification. Moreover, the color stability of the four synthesized individual betaxanthins, namely proline (ʟ-ProBX), alanine (ʟ-AlaBX), leucine (ʟ-LeuBX), and phenylalanine (ʟ-PheBX) betaxanthins, was investigated at different pHs. Their relative contribution to free radical scavenging was also scrutinized by TEAC and DPPH. ʟ-AlaBX and ʟ-LeuBx showed a significantly (p < 0.05) higher antioxidant activity, whereas ʟ-ProBX was the most resistant to the hydrolysis of betaxanthin and hence the least susceptible to color change. The color stability was strongly influenced by pH, with the color of ʟ-ProBX, ʟ-LeuBX, and ʟ-AlaBX at pH 6 being more stable, probably due to the easier hydrolysis under acid conditions. The semisynthesis and purification allowed us to have available remarkable quantities of pure individual betaxanthins of Opuntia dillenii for the first time, and to establish their color properties and antioxidant capacity. This study could be a step forward in the development of the best natural food colorant formulation, based on the betalain structure, which is of special interest in food technology.

A review on improving the sensitivity and color stability of naturally sourced pH-sensitive indicator films.

Naturally sourced pH-sensitive indicator films are of interest for real-time monitoring of food freshness through color changes because of their safety. Therefore, natural pigments for indicator films are required. However, pigment stability is affected by environmental factors, which can in turn affect the sensitivity and color stability of the pH-sensitive indicator film. First, natural pigments (anthocyanin, betalain, curcumin, alizarin, and shikonin) commonly used in pH-sensitive indicator films are presented. Subsequently, the mechanisms behind the change in pigment color under different pH environments and their applications in monitoring food freshness are also described. Third, influence factors, such as the sources, types, and pH sensitivity of pigments, as well as environmental parameters (light, temperature, humidity, and oxygen) of sensitivity and color stability, are analyzed. Finally, methods for improving the pH-sensitive indicator film are explored, encapsulation of natural pigments, incorporation of a hydrophobic film-forming matrix or function material, and protective layer have been shown to enhance the color stability of indicator films, the addition of copigments or mental ions, blending of different natural pigments, and the utilization of electrospinning have been proved to increase the color sensitivity of indicator films. This review could provide theoretical support for the development of naturally sourced pH-sensitive indicator films with high stability and sensitivity and facilitate the development in the field of monitoring food freshness.

Effect of conventional cigarette smoking and recent heated tobacco products on CAD/CAM restorative materials.

OBJECTIVE: To determine the effects of conventional cigarette smoking (CS) and recent heated tobacco products (HTPs) on the surface roughness and color stability of different indirect restorative materials. MATERIALS AND METHODS: One hundred disc-shaped samples were constructed of three different restorative CAD/CAM materials: lithium disilicate glass-ceramic (IPS e.max CAD; Ivoclar Vivadent, Liechtenstein), zirconia (BruxZir® Zirconia, Glidewell, USA) and polyetheretherketone (BioHPP® bredent GmbH, Germany). Of the IPS e.max CAD and the Bruxzir samples, 20 samples were glazed, and 20 samples were polished, while the BioHPP samples were all polished according to the manufacturer's instructions. Fifty samples were subjected to conventional cigarette smoking (LM, Philip Morris International Inc., Egypt) (Groups: IPS e.max CAD_Glazed exposed to CS (LD_G_Cig), IPS e.max CAD_Polished exposed to CS (LD_P_Cig), Bruxzir_Glazed exposed to CS (Zr_G_Cig), Bruxzir _Polished exposed to CS (Zr_P_Cig) and BioHPP exposed to CS (PEEK_Cig) and fifty samples were exposed to heated tobacco product smoking (Heets, Russet selection, Philip Morris International Inc., Italy) (Groups: IPS e.max CAD_Glazed exposed to HTP (LD_G_HTP), IPS e.max CAD_Polished exposed to HTP (LD_P_HTP), Bruxzir_Glazed exposed to HTP (Zr_G_HTP), Bruxzir CAD_Polished exposed to HTP (Zr_P_HTP) and BioHPP exposed to HTP (PEEK_HTP).. Six hundred cigarettes/heets representing 30 days of medium smoking behavior (20 cigarettes/day) were used. Before and after exposure to smoke, the surface roughness of all the samples was measured using JITAI8101 surface roughness tester (Beijing Jitai Tech Detection Device Co., Ltd, China, and the color parameters were assessed using VITA Easyshade Advance 4.01 (VITA shade, VITA made, VITA). The data were analyzed using One-way ANOVA, paired sample t-test and independent sample t-test. The significance level was set at α < 0.05. The surface topography was evaluated by scanning electron microscopy (SEM) and analyzed using energy-dispersive X-ray (EDX) spectroscopy to determine changes in the surface chemical composition. RESULTS: Both types of smoking caused significant increases in the surface roughness of all the samples. There was a significant difference in color change between CS and HTP for all materials with different surface finish (P < 0.01) and zirconia had the greatest effect on color change (P < 0.001). In contrast, polyetheretherketone (PEEK) "BioHPP" had the least effect (P < 0.001). CONCLUSION: Exposure to different types of smoking induce changes in the surface topography and color of different esthetic restorative materials. Compared with HTP, conventional cigarette smoke has a greater effect on the surface roughness and color stability of esthetic restorative materials. The glazed surfaces showed less change in surface topography than did the polished surfaces. Zirconia showed better color stability when compared to polyetheretherketone (PEEK).

The color stability of artificial white spot lesions treated with resin infiltration after exposure to staining beverages.

BACKGROUND: To evaluate the effect of staining beverages on the color-changing of resin-infiltrated artificial white spot lesions (WSLs). METHODS: Thirty-five artificial WSLs were created by pH cycling on flat bovine teeth specimens. The WSLs were treated with resin infiltration and were divided into five groups based on staining beverages: artificial saliva, coffee, wine, green tea, and Coca-Cola. These specimens were subjected to a 28-day exposure to the respective beverages. Color stability was assessed using a spectrophotometer at different time points: baseline, after 7, 14, 21, and 28 days of exposure, and repolishing. The color difference (∆E) between each time point and the baseline was calculated. Statistical analysis was performed using two-way measures ANOVA with a significance level of p = 0.05. RESULTS: All resin-infiltrated specimens exposed to staining beverages for 7 days exhibited more significant color changes than those exposed to artificial saliva. The color change patterns varied based on the type of beverage. The color alterations intensified with extended immersion in the wine and Coca-Cola groups, while there were no significant differences in the color of specimens after 28 days of immersion in the coffee and green tea groups. However, after cleaning with pumice powder, all specimens showed significantly reduced color changes compared to those observed after 28 days of immersion, except those immersed in coffee. CONCLUSIONS: Exposure of resin-infiltrated bovine tooth specimens to staining beverages resulted in a significant color alteration as the immersion time increased. However, the staining effect could be minimized by cleaning with pumice powder, except for the coffee group. CLINICAL RELEVANCE: After resin infiltration treatment, patients should be advised to minimize the consumption of colored beverages to prevent staining that could impact esthetic appearance.

The effect of whitening toothpastes on the color stability and surface roughness of stained resin composite.

BACKGROUND: This study aimed to investigate the effect of whitening toothpastes on the color stability and surface roughness of resin composites stained with coffee and cigarette smoke. METHODS: Seventy-two disk-shaped specimens (6 × 2 mm) of suprananohybrid resin composite were randomly divided into two groups and exposed to coffee and cigarette smoke (n = 36). After staining, the samples randomly divided into four groups according to whitening toothpastes and were brushed for 4 min: Opalescence Whitening (OW); Colgate Optic White (COW); Curaprox Black is White (CPX) and, distilled water (control) (n = 9). Color was measured with spectrophotometer at the initial, after staining, and after brushing, and surface roughness was measured with profilometer at the initial and after brushing. A surface morphology analysis was examined using scanning electron microscopy and atomic force microscopy. The obtained data were statistically analyzed. (p < 0.05). RESULTS: Cigarette smoke caused a significantly higher color change than coffee in the resin composite (p < 0.05). Brushing with hydrogen peroxide and silica-containing whitening toothpaste showed significant differences in color change (p < 0.05). The lowest whitening effect was found in activated charcoal-containing toothpaste. While all toothpastes increased the degree of surface roughness of resin composites, the highest roughness was caused by whitening toothpastes containing activated charcoal. (p < 0.05). CONCLUSIONS: The color stability and surface properties of resin composites can be affected by brushing them with whitening toothpaste. The utilization of whitening toothpaste containing hydrogen peroxide can be considered a safe method for increasing the whiteness of discolored resin composites.

Effect of hydrogen peroxide versus charcoal-based whitening mouthwashes on color, surface roughness, and color stability of enamel.

BACKGROUND: Patients tend to favor the whitening mouthwashes as they are easily applied and affordable. This study aimed to evaluate the effect of hydrogen peroxide versus charcoal-based whitening mouthwashes on color, surface roughness, and color stability of enamel. In the current study, the whitening mouthwashes used have the ability to stop future stains due to their white seal technology. METHODS: A total of 21 permanent central incisor teeth extracted for periodontal reasons were used in the present study. Teeth roots were sectioned and crowns were mounted in self-cured acrylic resin blocks. The specimens were randomly divided into three groups (n = 7) according to the tested whitening mouthwash: Control group ? DW" (Distilled water), ?OW" group: Peroxide-based mouthwash (Colgate Optic White) and ?CP" group: Charcoal-based mouthwash (Colgate® Plax Charcoal). Regarding ?OW" and ?CP" groups, the specimens were immersed in 20 ml of the tested mouthwash in each corresponding group for 1 min twice daily (morning and evening) for a total of 12 uninterrupted weeks. Color change was assessed using VITA Easyshade spectrophotometer and surface roughness (Ra) was measured using a white light interferometer. The specimens were stained using black tea solution and color was measured after 24 h of immersion for assessment of color stability. RESULTS: Color change results revealed that both whitening mouthwashes were able to restore color comparable to the control group with no significant difference between them. Regarding surface roughness, the control group showed the highest mean Ra value, followed by ?OW" group while ?CP" group showed the lowest mean Ra value. While color stability after staining, the control group showed a significantly higher value than the ?CP" and ?OW" groups. CONCLUSION: Hydrogen peroxide and charcoal-based whitening mouthwashes improve the color of enamel with no adverse effect on the surface roughness. Both whitening mouthwashes were beneficial to maintain the color after staining and prevent future enamel stains.

The effect of various inhaled asthma medications on the color stability of paediatric dental restorative materials.

BACKGROUND: The purpose of the study is to analyse the effects of different inhaled asthma medications (IAMs) on the color change of dental restorative materials (DRMs). METHODS: In total, 192 samples were taken from six different DRMs: [Filtek Z550 (nanohybrid composite), Fusio Liquid Dentin (Self-adhering flowable composite), Filtek Ultimate (nanofilled flowable composite), Dyract XP (compomer), Fuji II LC (resin-modified glass ionomer), Fuji IX Fast (self-cured-packable glass ionomer), (n = 32)]. After the initial color values (CIELab) of DRMs were measured by using a spectrophotometer, each sample was exposed to the same IAMs via nebulizer according to the four different inhaled therapies and measurements were repeated on the 7th & 21st days. RESULTS: In all IAM groups, DRM with the least amount of ΔE was nanohybrid composite, while the highest ΔE was found in Fuji II LC. Among all experimental groups, only Fuji II LC which was administered the combined medication, exceeded the clinically unacceptable threshold (ΔE = 3.3) on 7th & 21st days. CONCLUSIONS: Consequently, important factors affecting the susceptibility to color stability are the type of IAMs, the administration time-dosage, and the type of DRMs.

Effect of aging on dimensional accuracy and color stability of CAD-CAM milled and 3D-printed denture base resins: a comparative in-vitro study.

BACKGROUND: There is a lack of studies comparing the dimensional accuracy and color stability of denture base resins made using computer-aided design and computer-aided manufacturing (CAD-CAM) milling, 3-dimensional (3D) printing, and conventional denture processing techniques. This makes it challenging to determine the best method to fabricate complete dentures. The objective of this in vitro investigation was to assess and contrast the color stability and dimensional accuracy of denture base resins that were 3D printed and CAD-CAM milled, both before and after aging by thermocycling using digital surface matching technology and a benchtop laser scanner without using a spray, to optimize adaptation of the denture base and cast to minimize any imperfections and to evaluate the impact of the denture cleansing solution on the stability of color. METHODS: Evaluation of the dimensional accuracy (n = 27) was completed on a sectional maxillary stone cast using a digital 3D-surface matching software before and after 5000 thermocycles. A spectrophotometer was used to measure the color change (△E00) of all disc specimens (N = 54) before and after 500 thermocycles and immersion in denture cleansing solution for 30 cycles (3 min each) daily for 6 days. The Kruskal Wallis test, Dunn's post hoc test, Tukey's test with Bonferroni adjustment, one sample t test and independent t test were used to statistically analyze the data (α < 0.05). RESULTS: Thermocycling decreased the dimensional accuracy of the heat polymerized group at all 5 locations and the 3D-printed group at locations 1, 3 and 5 (P > .05), while it had no significant difference on the CAD-CAM milled group at all locations (P < .05). The color change (△E00) was lowest in the CAD-CAM milled group, moderate in the heat-polymerized group and highest in the 3D-printed group. After immersion in denture cleanser, the color change (△E00) was significantly higher in the 3 groups compared with after thermocycling (P > .001). CONCLUSIONS: CAD-CAM milled resins had the highest dimensional accuracy and the best color stability, conventional heat polymerized acrylic resins showed moderate change in dimensional accuracy and color stability, while the 3D- printed resin had the lowest dimensional accuracy and color stability after aging by thermocycling.

Comparison of light transmittance and color changes between polyurethane and copolyester retainer materials after staining and destaining.

BACKGROUND: Retainers are the only effective approach to prevent orthodontic relapse. The aim of this study was to compare the changes in color and light-transmittance of rough and smooth thermoformed polyurethane and copolymer retainer samples after staining in different solutions and destaining with different approaches. METHODS: Four hundred copolyester (Essix® ACE) and 400 polyurethane (Zendura®) samples with different surface textures, smooth and rough, were stained in 4 different solutions (n = 100 per solution) over 28 days. Each of the four groups of 100 stained samples of each material was subdivided into 5 groups of 20 samples and subjected to different destaining solutions. Light transmittance and color changes were evaluated using a spectrometer and a spectrophotometer. Mean differences were compared using a two-way analysis of variance (ANOVA) and posthoc multiple comparison tests at P = 0.05. RESULTS: No significant differences in light transmittance were found between both untreated materials. Both materials were stained in a similar fashion and showed no significant differences between two materials after staining. Coffee and tea stained both materials more significantly than wine, but there was a significant difference of changes of color and light transmittance between rough and smooth surfaces during the destaining in coffee- and tea-stained samples of copolyester material. All destaining solutions were effective at removing all stains on the samples. The surface roughness of the material plays a significant role in the ability of the materials to be destained, demonstrating a more significant greater effect on cleaning rough samples for improvements in light-transmittance and greater changes in color. CONCLUSIONS: This study concluded that the surface of materials plays a significant role in the material destaining and staining. In addition, the different polymers used for retainer fabrication exhibited different responses during the destaining process depending on types of stains.

Can wheel polishers improve surface properties and color stability of monochromatic resin composites?

BACKGROUND: To overcome the color layering procedure, monochromatic resin composites have been introduced. However, little is known about their polishability, gloss and color stability. This study aimed to investigate the surface roughness, gloss, and color change of monochromatic resin composites polished with wheel systems after being immersed in coffee. MATERIALS AND METHODS: Omnichroma, Zenchroma, Essentia Universal, Charisma Diamond One and NeoSpectra ST were used to obtain 120-disc samples of 8 × 2 mm. Only one side of the sample was polished with Twist Dia (TWD) or Nova Twist (NOV). The samples were examined for surface roughness, gloss, and color (ΔE and ΔE00) before and after 7 days of immersion in coffee and subsequent repolishing. The discs were examined via SEM. Surface roughness and gloss values were analyzed using ANOVA, Tukey and Pearson correlation tests. ΔE and ΔE00 values were evaluated using T tests, multivariate ANOVA, and Dunnett's post-hoc tests. RESULTS: For TWD groups, the smoothest material was Omnichroma (p < 0.05), while for NOV groups, it was Omnichroma and Zenchroma. Omnichroma was the glossiest, while Charisma Diamond One was the least glossy. In TWD groups, Charisma Diamond One and Essentia Universal were the most discolored, while Zenchroma and Omnichroma were the least. For NOV groups, Essentia Universal and Charisma Diamond One were the most discolored, while NeoSpectra ST, Omnichroma and Zenchroma were the least. After repolishing, Charisma Diamond One did not reach the level of ΔE < 2, while the other groups showed values below. Color evaluation with the CIELab and CIEDE2000 systems revealed similar results for the TWD groups after post-staining. CONCLUSIONS: Smooth and glossy surfaces could be achieved with the wheel system regardless of the composite resin. Repolishing after discoloration ensures that the color recovery is below the acceptable limit. Color evaluations with CIELab and CIEDE2000 yielded similar results.

Color stability of dual-cured and light-cured resin cements: A systematic review and meta-analysis of in vitro studies.

PURPOSE: This systematic review and meta-analysis aimed to evaluate the difference in the color stability of light-cured and dual-cured resin cements. MATERIALS AND METHODS: Two separate reviewers used the PubMed, Scopus, Web of Science, Embase, and Scielo databases to execute the systematic review. For the analysis, studies that evaluated the color stability of dual-cured and light-cured resin cements over time were used. The random effects model was used in the meta-analysis. Analyses of subgroups were carried out based on the aging technique. The methodological quality of each in vitro study was evaluated in accordance with the parameters of a prior systematic review. RESULTS: From all databases, a total of 2223 articles were retrieved. Following the screening of titles and abstracts, 44 studies were selected for full text review, and a total of 27 articles were used for the qualitative analysis. Finally, 23 articles remained for the qualitative analysis. The majority of studies were labeled as having a medium risk of bias. The global analysis showed that the dual-cure resin cements had considerably greater differences in the color change (p = 0.006). A high heterogeneity index (86%) was found in the analysis. CONCLUSIONS: The best available in vitro evidence suggests that dual-polymerizing cement has higher color variation than light-polymerized materials. To reduce the likelihood of color change after the luting of thin ceramic restorations, clinicians should employ light-polymerizable resin cements.

Color stability of precolored and extrinsically colored monolithic multilayered polychromatic zirconia: Effects of surface finishing and aging.

PURPOSE: To explore the impact of zirconia types, coloring methods, and surface finishing on the color stability of monolithic multilayered polychromatic zirconia after artificial aging, including thermocycling and simulated toothbrushing. MATERIALS AND METHODS: Eighty square-shaped zirconia samples were divided into 2 types (M3Y-TZP and M6Y-PSZ), further categorized based on coloring methods (precolored and extrinsically colored) and surface finishing techniques (mechanical polishing or glazing). The color stability was assessed using the CIEDE2000 formula. Artificial aging was simulated via thermocycling and toothbrushing. All samples were analyzed with a spectrophotometer to determine the post-aging color changes (ΔE00). The ΔE00 were interpreted and classified using the 50:50% perceptibility threshold (PT) and the 50:50% acceptability threshold (AT). Comparisons between groups for ΔE00 differences were performed using three-way ANOVA, with pairwise comparisons facilitated by Fisher's protected least significant difference test, α = 0.05. RESULTS: The study results indicated significant impacts of zirconia type, coloring method, and surface finishing on color stability. The M6Y groups experienced significantly greater color changes (6.61 ± 1.63) compared to the M3Y groups (3.40 ± 2.24), p < 0.0001. For both types of zirconia, extrinsically colored samples exhibited significantly higher ΔE00 when mechanically polished (p = 0.004). However, surface finishing had no significant effect on ΔE00 in precolored samples of either zirconia material (p = 1.000). The evaluation and categorization of ΔE00 variations indicated that nearly all color changes in the M6Y groups, regardless of being precolored, extrinsically colored, polished, or glazed, were deemed extremely unacceptable (Grade 1). In contrast, the M3Y groups showed more acceptable results, with the majority of color changes classified as moderately unacceptable (Grade 3). CONCLUSIONS: The color stability of multilayered polychromatic zirconia is influenced by the type of material, extrinsic coloring, and the chosen surface treatment post-artificial aging. The translucent 6Y-PSZ exhibited lower color stability, especially with only mechanical polishing. For the fabrication of M3Y-TZP and 6Y-PSZ monolithic multilayered polychromatic zirconia restorations, extrinsic coloring should be paired with glazing to maintain color stability. Conversely, in the absence of extrinsic coloring, both glazing and mechanical polishing are effective in preserving color stability.