Effective Magnetic Field Dependence of the Flux Pinning Energy in FeSe0.5Te0.5 Superconductor.

The role of a layered structure in superconducting pinning properties is still at a debate. The effects of the vortex shape, which can assume for example a staircase form, could influence the interplay with extrinsic pinning coming from the specific defects of the material, thus inducing an effective magnetic field dependence. To enlighten this role, we analysed the angular dependence of flux pinning energy U(H,θ) as a function of magnetic field in FeSe0.5Te0.5 thin film by considering the field components along the ab-plane of the crystal structure and the c-axis direction. U(H,θ) has been evaluated from magneto-resistivity measurements acquired at different orientations between the applied field up to 16 T and FeSe0.5Te0.5 thin films grown on a CaF2 substrate. We observed that the U(H,θ) shows an anisotropic trend as a function of both the intensity and the direction of the applied field. Such a behaviour can be correlated to the presence of extended defects elongated in the ab-planes, thus mimicking a layered superconductor, as we observed in the microstructure of the compound. The comparison of FeSe0.5Te0.5 with other superconducting materials provides a more general understanding on the flux pinning energy in layered superconductors.

Critical Current and Pinning Features of a CaKFe4As4 Polycrystalline Sample.

We analyze the magnetic behavior of a CaKFe4As4 polycrystalline sample fabricated by a mechanochemically assisted synthesis route. By means of DC magnetization (M) measurements as a function of the temperature (T) and DC magnetic field (H) we study its critical parameters and pinning features. The critical temperature Tc has been evaluated by M(T) curves performed in Zero Field Cooling-Field Cooling conditions. These curves show the presence of a little magnetic background for temperatures above Tc, as also confirmed by the hysteresis loops M(H). Starting from the M(H) curves, the critical current density Jc of the sample has been calculated as a function of the field at different temperatures in the framework of the Bean critical state model. The Jc(H) values are in line with the ones reported in the literature for this typology of samples. By analyzing the temperature dependence of the critical current density Jc(T) at different magnetic fields, it has been found that the sample is characterized by a strong type pinning regime. This sample peculiarity can open perspectives for future improvement in the fabrication of this material.