Mean-stress sensitivity of an ultrahigh-strength steel under uniaxial and torsional high and very high cycle fatigue loading.

The influence of load ratio on the high and very high cycle fatigue (VHCF) strength of Ck45M steel processed by thermomechanical rolling integrated direct quenching was investigated. Ultrasonic fatigue tests were performed under uniaxial and torsional loading at load ratios of R = -1, 0.05, 0.3, and 0.5 with smooth specimens and specimens containing artificially introduced defects. Up to 2 × 105 cycles, failure originated from surface aluminate inclusions and pits under both loading conditions. The prevailing fracture mechanisms in the VHCF regime were interior crack initiation under uniaxial loading and surface shear crack initiation under torsional loading. The mean-stress sensitivity and the fatigue strength were evaluated using fracture mechanics approaches. Equal fatigue limits for uniaxial and torsional loading were determined considering the size of crack initiating defects and the appropriate threshold condition for Mode-I crack growth. Furthermore, the mean-stress sensitivity is independent of loading condition and can be expressed by σ w R = σ w R = - 1 · 1 - R 2 0.63 and τ w R = τ w R = - 1 · 1 - R 2 0.63 .

The Fabrication of Ultrahigh-Strength Steel with a Nanolath Structure via Quenching-Partitioning-Tempering.

A novel low-alloy ultrahigh-strength steel featuring excellent mechanical properties and comprising a nanolath structure was fabricated in this work using a quenching-partitioning-tempering (Q-P-T) process. The Q-P-T process comprised direct quenching and an isothermal bainitic transformation for partitioning after thermo-mechanical control processing (online Q&P) and offline tempering (reheating and tempering). The ultrafine nanolath martensite/bainite mixed structure, combined with residual austenite in the form of a thin film between the nanolaths, was formed, thereby conferring excellent mechanical properties to the steel structures. After the Q-P-T process, the yield and tensile strengths of the steels reached 1450 MPa and 1726 MPa, respectively. Furthermore, the Brinell hardness and elongation rate were 543 HB and 11.5%, respectively, with an average impact energy of 20 J at room temperature.

Research on the Welding Process and Weld Formation in Multiple Solid-Flux Cored Wires Arc Hybrid Welding Process for Q960E Ultrahigh-Strength Steel.

This paper proposes a novel welding process for ultrahigh-strength steel. The effects of welding parameters on the welding process and weld formation were studied to obtain the optimal parameter window. It was found that the metal transfer modes of solid wires were primarily determined by electrical parameters, while flux-cored wires consistently exhibited multiple droplets per pulse. The one droplet per pulse possessed better welding stability and weld formation, whereas the short-circuiting transfer or one droplet multiple pulses easily caused abnormal arc ignition that decreased welding stability, which could easily lead to a "sawtooth-shaped" weld formation or weld offset towards one side with more spatters. Thus, the electrical parameters corresponding to one droplet per pulse were identified as the optimal parameter window. Furthermore, the weld zone (WZ) was predominantly composed of AF, and the heat-affected zone (HAZ) primarily consisted of TM and LM. Consequently, the welded joint still exhibited excellent mechanical properties, particularly toughness, despite higher welding heat input. The average tensile strength reached 928 MPa, and the impact absorbed energy at -40 °C for the WZ and HAZ were 54 J and 126 J, respectively. In addition, the application of triple-wire welding for ultrahigh-strength steel (UHSS) demonstrated a significant enhancement in post-weld deposition rate, with increases of 106% and 38% compared to single-wire and twin-wire welding techniques, respectively. This process not only utilized flux-cored wire to enhance the mechanical properties of joints but also achieved high deposition rate welding.