RESUMO
This study evaluated the effect on adhesive layer thickness, bond strength, and adhesive failure pattern of the application of universal adhesive (Scotchbond Universal) using either manual or rotary brush in dentin previously impregnated with bioceramic sealer (Sealer Plus BC) using a manual brush, at 24 h and 1 year. Eighty-eight bovine crowns were divided into four groups (n = 22) according to the intervention: (i) use of bioceramic sealer and adhesive application using manual brush, (ii) use of bioceramic sealer and adhesive application using rotary brush, (iii) use of resin sealer and adhesive application using manual brush, and (iv) use of resin sealer and adhesive application using rotary brush. Subsequently, specimens were restored with a composite resin (Filtek Z-250). Adhesive layer thickness was evaluated using confocal microscopy. Bond strength was assessed using the microtensile bond strength test, and adhesive failure pattern was evaluated under a stereomicroscope. Data were analyzed using two-way ANOVA/Tukey tests. Specimens where a rotary brush had been used exhibited lower adhesive layer thickness. Specimens treated with resin sealer and using a manual brush showed lower bond strength values and a higher occurrence of adhesive failures at 24 h and 1 year than specimens treated with bioceramic sealer and using rotary brush for adhesive application.
Assuntos
Resinas Compostas , Colagem Dentária , Cimentos de Resina , Resistência à Tração , Animais , Colagem Dentária/métodos , Bovinos , Cimentos de Resina/química , Resinas Compostas/química , Teste de Materiais , Adesivos Dentinários/química , Análise do Estresse Dentário , Dentina , Propriedades de Superfície , Microscopia Confocal , Fatores de TempoRESUMO
In this study, we evaluated the effect of four different strategies for bonding a CAD/CAM resin nanoceramic restoration (Lava Ultimate, 3M) to the dentin surface using a universal adhesive (Scotch Bond Universal, 3M) and adhesive resin cement (RelyX Ultimate, 3M) on the shear bond strength (SBS) and failure mode. The strategies comprised: (i) immediate sealing, immediate bonding; (ii) immediate sealing, bonding after 2 weeks with provisional restoration; (iii) immediate sealing with flowable resin composite reinforcement and bonding after 2 weeks with provisional restoration; and (iv) no immediate sealing, and bonding after 2 weeks with provisional restoration. After bonding, all the specimens were thermocycled, shear tests were performed using a universal testing machine, and failure modes were determined using stereomicroscope and scanning electron microscopy. The highest mean SBS was recorded with immediate sealing, immediate bonding strategy. Most adhesive failures with exposed dentinal tubules were noted in specimens exposed to bonding after 2 weeks with no immediate sealing, which was associated with the lowest SBS. Mixed failures predominated in all immediate dentin sealing groups. Immediate sealing with universal adhesives improves SBS, particularly in the single-visit approach, which has shown significantly better performance, whereas the provisional phase has a negative effect.
Assuntos
Resinas Compostas , Colagem Dentária , Análise do Estresse Dentário , Adesivos Dentinários , Cimentos de Resina , Resistência ao Cisalhamento , Resinas Compostas/química , Colagem Dentária/métodos , Humanos , Cimentos de Resina/química , Adesivos Dentinários/química , Dentina , Microscopia Eletrônica de Varredura , Teste de Materiais , Restauração Dentária Permanente/métodos , Cerâmica/química , Desenho Assistido por Computador , Propriedades de Superfície , Falha de Restauração DentáriaRESUMO
The objective of this study was to determine the effects on the colour of adding increasing concentrations of graphene to orthodontic fixed retainer adhesives and to evaluate changes in optical transmission during light curing and the resultant degree of conversion. Two different types of adhesives commonly used for fixed retainers were investigated: A packable composite (Transbond) and a flowable composite (Transbond Supreme). Graphene was added to the adhesives in three different concentrations (0.01, 0.05, and 0.1 wt%). Adhesives without graphene addition were set as control groups. A Minolta colourimeter was used to measure the colour and translucency parameters. Irradiance transmitted during curing was quantified using MARC Light Collector. Fourier-transform infrared spectroscopy was used to record degree of conversion. Data were statistically analysed with the Student's t-test and one-way ANOVA with Tukey's tests (α = 0.05). The findings showed that incorporating graphene darkened the adhesive colour significantly and reduced translucency. As the graphene concentration reached 0.1 wt%, samples became opaque; yet, no adverse effect on degree of conversion was observed. The addition of graphene reduces optical transmission of lingual retainer adhesives; the effect increases with graphene concentration.
Assuntos
Bis-Fenol A-Glicidil Metacrilato , Colagem Dentária , Grafite , Cimentos Dentários , Cimentos de Resina/química , Teste de Materiais , Resinas Compostas/química , Adesivos/químicaRESUMO
This study aimed at examining the bond strength between zirconia and ceramic veneer, following the ISO 9693 guidelines. A total of fifty specimens of zirconia/ceramic-veneer system were produced using two commercial zirconias (VITA YZ-HTWhite and Zolid HT+ White, referred to as Group A and Group B, respectively) and a ceramic-veneering material (Zirkonia 750). The microstructure (via x-ray diffraction analysis, XRD and Secondary Electron mode, SEM) and the mechanical properties (via 3-point bending tests) of the two groups were assessed. Then, experiments were conducted according to the ISO 9693 and conventional protocols applied for producing zirconia/ceramic-veneer restorations. Bond strength values, measured by 3-point bending tests, were 34.42 ± 7.60 MPa for Group A and 31.92 ± 6.95 MPa for Group B. SEM observations of the cohesively fractured surfaces (on the porcelain side) and the examination for normality using the Shapiro-Wilk test suggested the use of Weibull statistical analysis. Median strength (σ50%) for Group A and Group B was 34.76 and 32.22 MPa, while the characteristic strength (σ63.2%) was 35.78 and 33.14 MPa, respectively. The Weibull modulus disparity between groups (12.69 and 13.07) was not significant. Bond strength exceeded the ISO 9693 minimum of 20 MPa, suggesting satisfactory strength for clinical use.
Assuntos
Colagem Dentária , Porcelana Dentária , Análise do Estresse Dentário , Facetas Dentárias , Teste de Materiais , Microscopia Eletrônica de Varredura , Difração de Raios X , Zircônio , Zircônio/química , Porcelana Dentária/química , Propriedades de Superfície , Cerâmica/química , Materiais Dentários/química , HumanosRESUMO
This study evaluated bond strength of glass fiber posts to root dentin using push-out (PO) and diametral compression (DC), testing glycolic acid as a conditioner and varying dentin moisture. An additional aim was to test whether DC can be an alternative test to PO for bond strength assessment. Eighty bovine teeth were divided into eight groups (n = 10) defined by the use of either 37% glycolic acid or 37% phosphoric acid (PA) on moist or wet dentin before bonding with either Adapter SingleBond/RelyX ARC or One Step Plus/Duo-Link Bisco. Each tooth provided discs with an internal diameter of 2 mm, external diameter of 5 mm, and height of 2 mm, which underwent PO and DC. Finite element analysis (FEA) was carried out on 3D models. When analyzing PO results through linear regression, the highest values of bond strength were observed using glycolic acid on wet dentin in the cervical and middle thirds of the teeth. Analyzing DC results, the only statistical influence on values was the dental thirds. The scatterplot of the DC results and the PO bond strength values indicated no relationship between the results of the two tests (r = 0.03; p = 0.64). PO test detected more sensitive changes in bond strength values than DC.
Assuntos
Colagem Dentária , Dentina , Análise de Elementos Finitos , Vidro , Ácidos Fosfóricos , Técnica para Retentor Intrarradicular , Animais , Bovinos , Dentina/efeitos dos fármacos , Vidro/química , Ácidos Fosfóricos/química , Adesivos Dentinários/química , Cimentos de Resina/química , Análise do Estresse Dentário , Teste de Materiais , Raiz Dentária , Glicolatos/química , Condicionamento Ácido do DenteRESUMO
This study evaluated the effect of different concentrations of alpha-tocopherol in gel form on fracture strength, hybrid layer formation, and microtensile bond strength of endodontically treated teeth bleached with 40% hydrogen peroxide (H2 O2 ). Sixty bovine incisors were randomized into one of six groups (n = 10 incisors per group) defined by the interventions carried out after endodontic treatment. In the control group, no additional intervention was carried out, while all teeth in the five intervention groups were bleached with 40% H2 O2 and subsequently treated with alpha-tocopherol at concentrations of 15% (15AT), 20% (20AT), or 25% (25AT), with 10% sodium ascorbate (10SA), or with nothing (40HP). Fracture strength was evaluated in a mechanical testing machine, hybrid layer formation was assessed using scanning electron microscopy, and bond strength was determined using microtensile bond-strength testing. Data were analyzed using Kruskal-Wallis and Dunn's tests. No statistically significant difference regarding fracture strength was observed among groups. Hybrid layer formation was greater in the 15AT group than in groups 40HP and 10SA. Teeth in groups 15AT, 20AT, and 25AT demonstrated higher bond strength than teeth in groups 40HP and 10SA. Alpha-tocopherol, preferably at 15%, effectively reverses the deleterious effects, of bleaching, on hybrid layer formation and bond strength to dentin.
Assuntos
Colagem Dentária , Clareamento Dental , Dente não Vital , Bovinos , Animais , Antioxidantes/química , Antioxidantes/farmacologia , alfa-Tocoferol/farmacologia , Resistência à Flexão , Resinas Compostas/química , Ácido HipoclorosoRESUMO
This study aimed to evaluate the effect of n-propyl gallate as pre-treatment for resin-dentin bond strength. The dentin pre-treatments evaluated included propyl gallate of concentrations 0.1% (w/v), 1.0% (w/v), and 10.0% (w/v), as well as glutaraldehyde 5.0% (v/v), and distilled water as a control treatment. Dentin specimens were prepared for Fourier Transformed Infrared Spectroscopy (FT-IR) (n = 3/pre-treatment). Pre-treatments were actively applied to dentin blocks before performing the adhesive procedure to composite resin. Microtensile bond strength to dentin (µTBS) (n = 8/pre-treatment) was determined after 24 h and 6 months of storage. Data were submitted to a two-way ANOVA, followed by Tukey's post hoc test. As for FT-IR, propyl gallate 1%-treated specimens presented higher water, carbonate, collagen, and amide absorbance rates compared to other tested groups, while specimens pre-treated with glutaraldehyde and distilled water presented similar absorbance curves. Regarding µTBS, all concentrations of propyl gallate resulted in statistically significant higher bond strength values than distilled water at 24 h. After 6 months of storage, propyl gallate 0.1% was the only group that maintained µTBS over time. Propyl gallate 0.1% might be a suitable dentinal pre-treatment due to being able to present chemical bonds with demineralized dentin and providing resin-dentin bond stability after 6 months of storage.
Assuntos
Colagem Dentária , Galato de Propila , Galato de Propila/análise , Galato de Propila/farmacologia , Adesivos Dentinários/química , Glutaral , Espectroscopia de Infravermelho com Transformada de Fourier , Cimentos de Resina/química , Dentina , Resistência à Tração , Teste de Materiais , Cimentos Dentários/farmacologia , Resinas Compostas/química , Água/químicaRESUMO
BACKGROUND Modification of the glass fiber post (GFP) with titanium dioxide or silver particles can improve the durability and reliability of dental treatments for ensuring long-term success. This research assessed the tensile bond strength (TBS) of an adhesive system used for cementing GFPs into root dentin following the incorporation of nanoparticles of titanium dioxide (NTiO2) and silver (NAg). MATERIAL AND METHODS Sixty human maxillary canines were prepared to create a 10-mm intra-radicular space for post placement from the cementoenamel junction. The specimens were randomly allocated into 2 groups (a non-thermocycling group and a thermocycling group). Each group was divided into 3 subgroups (10 samples each) according to the adhesive system used (adhesive system devoid of any addition, adhesive system including 1% NAg, and adhesive system infused with 1% NTiO2). TBS tests were conducted and recorded in MPa using a Universal Testing Machine, with an axial load applied at a rate of 0.5 mm/min until failure. The TBS for both groups (non-thermocycling and thermocycling) was measured in megapascals (MPa), and the failure type was recorded. The data were statistically analyzed using one-way analysis of variance (ANOVA) and Tukey's test with P.
Assuntos
Adesivos , Colagem Dentária , Vidro , Titânio , Humanos , Cimentos de Resina/química , Resistência à Tração , Reprodutibilidade dos Testes , Prata , Dentina , Teste de MateriaisRESUMO
BACKGROUND This study investigates the effect of artificial aging of direct resin nanohybrid composites on mean bond strength values for veneer ceramic samples. MATERIAL AND METHODS Ninety direct nanohybrid composite resin (Tetric N-Ceram) cylindrical discs were divided into 5 groups (n=18 each) based on aging cycles (thermocycling), as follows: TC=no aging (control), T1=850, T3=2500, T6=5000, and T12=10000 cycles, representing 1, 3, 6, and 12 months of clinical usage, respectively. Lithium disilicate glass ceramic (IPS e.max Press) cylindrical discs were cemented to resin discs using resin cement (Variolink N) after surface treatments (ceramic etching, silaning, composite abrasion). Differences in means between subgroups were calculated using one-way ANOVA, followed by the Tukey honestly significant differences post hoc test. Differences were considered statistically significant with a P value ≤0.05. RESULTS The highest SBS between ceramic and aged composite was observed at 1 month (m=20.35) but did not differ significantly from the control group (m=20.97). For all other subgroups (3, 6, 12 months) SBS was significantly less than that of the control (P≤0.05). At 1 and 3 months, cohesive failures were more common, whereas adhesive failures were more common in 6- and 12-month-old composites. CONCLUSIONS SBS of aged composites was less than that of non-aged composites, with SBS decreasing proportionally as the resin aged. When cementing a ceramic restoration over existing composite restorations, those older than 1 month should be removed and replaced with new ones.
Assuntos
Cerâmica , Resinas Compostas , Colagem Dentária , Facetas Dentárias , Teste de Materiais , Cerâmica/química , Resinas Compostas/química , Teste de Materiais/métodos , Colagem Dentária/métodos , Cimentos de Resina/química , Porcelana Dentária/química , Humanos , Análise do Estresse Dentário , Propriedades de SuperfícieRESUMO
BACKGROUND Dentin contamination with hemostatic agents before bonding indirect restorations negatively affects the bond strength. However, the consensus on which materials could be used to clean contamination of hemostatic agents has not been explored. The aim of this study was to assess the effect of Katana Cleaner applied on the surface of dentin contaminated with hemostatic agents on the shear bond strength (SBS) of self-adhesive resin cement by comparing it with three other surface cleaners. MATERIAL AND METHODS Ninety dentin specimens were divided into a no contamination group (control) (n=10), 4 groups contaminated with 25% aluminum chloride (Viscostat Clear) (n=40), and 4 groups contaminated with 20% ferric sulfate (Viscostat) (n=40). Subsequently, 4 different cleaners were used for each contamination group (water rinse, phosphoric acid, chlorhexidine, and Katana Cleaner). Then, self-adhesive resin cement was directly bonded to the treated surfaces. All specimens were subjected to 5000 thermal cycles of artificial aging. The shear bond strength was measured using a universal testing machine. RESULTS Two-way analysis of variance showed that the contaminant type as the main factor was statistically non-significant (p=0.655), cleaner type as the main factor was highly significant (p<0.001), and interaction between the contaminant and cleaner was non-significant (p=0.51). The cleaner type was the main factor influencing the bond strength. Phosphoric acid and chlorhexidine showed better performance than Katana Cleaner. CONCLUSIONS Cleaning dentin surface contamination with phosphoric acid and chlorhexidine had better performance than with Katana Cleaner.
Assuntos
Colagem Dentária , Dentina , Hemostáticos , Cimentos de Resina , Resistência ao Cisalhamento , Humanos , Dentina/efeitos dos fármacos , Hemostáticos/farmacologia , Colagem Dentária/métodos , Clorexidina/análogos & derivados , Clorexidina/farmacologia , Teste de Materiais/métodos , Propriedades de Superfície/efeitos dos fármacos , Adesivos Dentinários , Compostos Férricos/químicaRESUMO
Red-fluorescing dentine indicates bacterial contamination [Caries Res 2002; 36: 315-319]. We investigated effect of removal of red fluorescent dentine caries on shear bond strength and fracture mode of 4 adhesive approaches. Sixty-five carious teeth and 50 noncarious controls were distributed into 4 groups: Clearfil™ self-etch (CSE), OptiBond™ FL total etch (OTE), Scotchbond™ Universal total etch (STE) and self-etch (SSE). Samples were excited at 405 nm and viewed through 530 nm filter. Carious samples were ground flat exposing strongly red-fluorescing (StrongRF) dentine, on which a composite cylinder was placed, using one of 4 adhesives. After 22 h in water, shear bond strength and fracture mode were analysed. StrongRF was removed; composite cylinders were placed on weakly red-fluorescing (WeakRF) dentine and tested as described above. Finally, red-fluorescing dentine was removed, and composite cylinders were placed on non-fluorescing (NonRF) dentine and tested. Composites were placed at 3 corresponding heights in controls. After 22 h in water, shear bond strength testing and fracture mode analysis were performed. Differences were tested using Mann-Whitney or Wilcoxon tests (p ≤0.05). Median (Q1, Q3) shear bond strength on StrongRF was SSE 14.4 (9.2, 18.2) MPa >CSE 10.2 (6.4, 17.3) MPa >STE 9.1 (6.9, 11.2) MPa >OTE 6.8 (4.0, 10.8) MPa. Shear bond strength increased statistically significantly for all adhesives on WeakRF: SSE 19.8 (13.6, 24.3) MPa >STE 19.5 (12.7, 23.1) MPa >CSE 17.5 (12.0, 22.5) MPa >OTE 15.8 (11.9, 20.9) MPa. Only STE 25.6 (22.4, 29.1) MPa and CSE 22.1 (17.6, 24.6) MPa were significantly different on NonRF compared to WeakRF. For controls tested at corresponding depths, superficial shear bond strength was OTE 18.7 (16.0, 22.1) MPa >STE 18.4 (12.0, 25.9) MPa >CSE 18.1 (12.7, 20.7) MPa >SSE 13.0 (9.6, 17.8) MPa. This was significantly higher compared to StrongRF except for SSE. Central shear bond strength was not significantly different to WeakRF, deep shear bond strength was significantly lower for SSE and CSE but higher for OTE compared to carious. Conclusion: StrongRF dentine should be removed for higher shear bond strength, but WeakRF dentine can often be preserved without compromising adhesive bond strength.
Assuntos
Resinas Compostas , Colagem Dentária , Humanos , Resinas Compostas/química , Cimentos Dentários , Adesivos Dentinários/química , Cimentos de Resina/química , Condicionamento Ácido do Dente , Dentina , Água , Teste de MateriaisRESUMO
INTRODUCTION: In orthodontics, white spot lesions are a persistent and widespread problem caused by the demineralization of buccal tooth surfaces around bonded brackets. The remaining adhesive around the brackets leads to surface roughness, which might contribute to demineralization. The present in vitro study aimed to compare a conventional and a modern adhesive system (APC Flash-Free technology) for orthodontic brackets with regard to the adhesion of Streptococcus sobrinus, a leading caries pathogen. METHODS: This in vitro study included 20 premolar teeth and compared 10 APC Flash-Free adhesive-coated ceramic brackets (FF)with 10 conventionally bonded (CB) ceramic clarity brackets. Specimens were incubated in an S. sobrinus suspension for 3 h. To evaluate the bacterial formation, samples were analysed with a scanning electron microscope (SEM). Imaging software was used to quantify and statistically compare percentage values of colonization (PVC) in both groups' adhesion and transition areas. RESULTS: We found a significant difference in biofilm formation between the groups for the adhesive and transition areas. PVC in the adhesive area was approximately 10.3-fold greater for the CB group compared with the FF group (median: 3.2 vs 0.31; P < 0.0001). For the transition area, median PVC was approximately 2.4-fold greater for the CB group compared with the FF group (median: 53.17 vs 22.11; P < 0.01). CONCLUSIONS: There was a significantly lower level of S. sobrinus formation around the FF bracket system than there was surrounding the conventionally bonded group. This study suggests that the FF adhesive bracket system can help reduce the occurrence of bacterial growth around orthodontic brackets.
Assuntos
Colagem Dentária , Braquetes Ortodônticos , Desmineralização do Dente , Humanos , Dente Pré-Molar , Cerâmica , Biofilmes , Colagem Dentária/métodos , Teste de MateriaisRESUMO
OBJECTIVE: To evaluate stability outcomes and failure rates associated with four types of lingual retainers: (1) dead-soft wire, (2) multistrand stainless steel (SS) wire, (3) CAD/CAM nitinol, and (4) connected bonding pads (CBPs) after 3 years of retention. METHODS: This study enrolled 96 patients (66 females, 30 males) with a median age of 19 years with four types of lingual retainers: (1) 0.016 × 0.022-inch dead-soft wire, (2) 0.0215-inch five-strand SS wire, (3) 0.014 × 0.014-inch CAD/CAM nitinol wire, and (4) CBPs. The irregularity index, intercanine distances, and arch lengths were obtained and used to evaluate mandibular stability. Failure rates were also assessed during this study. Data were statistically analysed. RESULTS: Irregularity increased, whereas intercanine width and arch length decreased after 3 years of retention. The greatest irregularity was associated with the CBPs and the least with the CAD/CAM retainers. Changes in stability measurements were significantly higher in the dead-soft wire and CBPs than those in the CAD/CAM nitinol and multistrand SS wires. Parallel to these changes, the frequency of failure yielded similar results with the same significance between the groups. The failure rate of CBPs, in contrast to the CAD/CAM nitinol and multistrand SS wires, was significantly higher in the right quadrant (P < .05). CONCLUSION: After taking the 3-year results into consideration, CAD/CAM nitinol and multistrand SS wires were found to be more successful than the others in maintaining mandibular stability. The most failures were observed with CBPs after 3 years of retention.
Assuntos
Colagem Dentária , Contenções Ortodônticas , Adolescente , Feminino , Humanos , Masculino , Adulto Jovem , Ligas , Colagem Dentária/métodos , Seguimentos , Mandíbula , Desenho de Aparelho Ortodôntico , Aço Inoxidável , Ensaios Clínicos Controlados Aleatórios como AssuntoRESUMO
OBJECTIVE: To compare the clinical effectiveness of V-bend bonded retainers (BR) versus vacuum-formed retainers (VFR) regarding their capacity to maintain treatment stability and survival rates after 12 months. MATERIALS AND METHODS: Patients finishing orthodontic treatment were randomly allocated into two groups. The BR group received maxillary and mandibular BRs in the lingual surfaces of the anterior teeth. The VFR group received VFRs right after fixed appliances removal. The patients were evaluated at four time-points: at fixed appliances removal (T0), after 3 (T1), 6 (T2) and 12 months (T3). In each time-point digital models were obtained and analysed with the OrthoAnalyzer™ software. Treatment stability based on occlusal outcomes and retainers' survival rates were evaluated. Intergroup comparisons were performed using Mann-Whitney U-tests. The Kaplan-Meier survival plot and the log-rank test were employed to assess the retainers' survival. RESULTS: Both BR and VFR groups included 25 patients. The groups were comparable regarding their baseline characteristics. Up to 6 months, both retainers were equally effective; however, after 12 months, BRs were more effective in maintaining the incisors' alignment in the maxilla and the mandible compared to the VFRs. No differences were noticed in the intercanine and intermolar widths, overjet and overbite. There were no differences regarding the retainers' survivability in both arches. CONCLUSIONS: BRs were more effective in maintaining the alignment of the incisors in the maxilla and mandible compared to VFRs after 12 months. Both retainers presented the same survival rates after the same period.
Assuntos
Desenho de Aparelho Ortodôntico , Contenções Ortodônticas , Humanos , Feminino , Masculino , Vácuo , Adolescente , Colagem Dentária/métodos , Resultado do Tratamento , Má Oclusão/terapia , Adulto Jovem , IncisivoRESUMO
OBJECTIVE: We aimed to develop a tool for virtual orthodontic bracket removal based on deep learning algorithms for feature extraction from bonded teeth and to demonstrate its application in a bracket position assessment scenario. MATERIALS AND METHODS: Our segmentation network for virtual bracket removal was trained using dataset A, containing 978 bonded teeth, 20 original teeth, and 20 brackets generated by scanners. The accuracy and segmentation time of the network were tested by dataset B, which included an additional 118 bonded teeth without knowing the original tooth morphology. This tool was then applied for bracket position assessment. The clinical crown center, bracket center, and orientations of separated teeth and brackets were extracted for analyzing the linear distribution and angular deviation of bonded brackets. RESULTS: This tool performed virtual bracket removal in 2.9 ms per tooth with accuracies of 98.93% and 97.42% (P < 0.01) in datasets A and B, respectively. The tooth surface and bracket characteristics were extracted and used to evaluate the results of manually bonded brackets by 49 orthodontists. Personal preferences for bracket angulation and bracket distribution were displayed graphically and tabularly. CONCLUSIONS: The tool's efficiency and precision are satisfactory, and it can be operated without original tooth data. It can be used to display the bonding deviation in the bracket position assessment scenario. CLINICAL SIGNIFICANCE: With the aid of this tool, unnecessary bracket removal can be avoided when evaluating bracket positions and modifying treatment plans. It has the potential to produce retainers and orthodontic devices prior to tooth debonding.
Assuntos
Aprendizado Profundo , Colagem Dentária , Braquetes Ortodônticos , Colagem Dentária/métodos , Descolagem Dentária/métodos , Microscopia Eletrônica de VarreduraRESUMO
OBJECTIVES: This study aimed to evaluate the dentin bond performance of various resin luting cement (RLC) systems combined with universal adhesives in different luting strategies. MATERIALS AND METHODS: Three self-adhesive resin luting cements (SRLCs) were used with universal adhesives as primers. Twelve specimens per group were prepared to measure shear bond strength (SBS) under distinct luting strategies in etch-&-rinse and self-etch modes. Regarding luting strategies, the bonded specimens were categorized into four groups based on tooth primer application and the curing mode of the SRLC paste: (i) with light irradiation of the tooth primer (wL) + dual-cure mode (DC) of the SRLC paste, (ii) wL + self-cure mode (SC) of the SRLC paste, (iii) without light irradiation of the tooth primer (woL) + DC mode of the SRLC paste, and (iv) woL + SC mode of the SRLC paste. Specimens were also subjected to different storage conditions: 24 h in water (baseline condition) and 10,000 cycles of thermal cycling. RESULTS: Luting strategy, storage condition, and SRLC system type significantly influenced dentin SBS values in both etching modes. Notably, certain SRLCs exhibited significantly higher dentin SBS when the primer was light-irradiated compared with no primer irradiation. CONCLUSION: Most SRLCs demonstrated higher dentin bond strength with light-irradiated primers, suggesting potential enhancement of dentin bond performance via primer light irradiation.
Assuntos
Colagem Dentária , Análise do Estresse Dentário , Teste de Materiais , Cimentos de Resina , Resistência ao Cisalhamento , Cimentos de Resina/química , Colagem Dentária/métodos , Adesivos Dentinários/química , Propriedades de Superfície , Técnicas In Vitro , Cimentos Dentários/química , Dentina , HumanosRESUMO
OBJECTIVE: The study aims to evaluate the shear bond and flexural strength fatigue behavior of yttrium-stabilized zirconia (4YSZ) repaired using different resin composites. MATERIALS AND METHODS: Cylindric specimens of 4YSZ were obtained for the bond strength (Ø = 6 mm, 1.5 mm of thickness) and biaxial flexural strength (Ø = 15 mm, 1 mm of thickness) fatigue tests and divided into 3 groups according to the repair resin composite: EVO (nanohybrid), BULK (bulk-fill), and FLOW (flowable). The zirconia surface was air-abraded with alumina particles, a 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) primer was applied, and the resin composite was build-up over the zirconia. Fatigue shear bond strength and flexural fatigue strength tests were performed (n = 15). One-way ANOVA and Tukey post hoc tests were carried out for both outcomes, besides scanning electron microscopy and finite element analysis. RESULTS: The repair material affected the fatigue shear bond strength of zirconia ceramic. The BULK group (18.9 MPa) depicted higher bond strength values than FLOW (14.8 MPa) (p = 0.04), while EVO (18.0 MPa) showed similar results to both groups. No effect was observed for the mechanical behavior (p = 0.53). The stress distribution was similar for all groups. CONCLUSION: The repair of yttrium-stabilized zirconia (4YSZ) ceramics with bulk-fill resin composites was the best option for high fatigue bond strength. However, the fatigue mechanical performance was similar regardless of the applied repair material. CLINICAL RELEVANCE: The repair of yttrium-stabilized zirconia (4YSZ) monolithic restorations may be performed with nanohybrid and bulk-fill resin composites in order to promote longevity in the treatment.
Assuntos
Colagem Dentária , Metacrilatos , Colagem Dentária/métodos , Propriedades de Superfície , Teste de Materiais , Resinas Compostas/química , Zircônio/química , Cerâmica/química , Resistência ao Cisalhamento , Ítrio/química , Cimentos de Resina/química , Análise do Estresse DentárioRESUMO
OBJECTIVES: This study aimed at comparing the microtensile bond strength (MTBS) and interfacial adaptation of a modern self-curing and a light-curing restorative bulk-fill composite to a conventional composite applied with the layering technique. METHODS: Forty-eight occlusal cavities were divided in three main groups (16/group) based on tested materials: (i) STELA, bulk-fill self-curing restorative (STELA, SDI Ltd.); (ii) 3 M-BULK, bulk-fill composite (Filtek One Bulk-Fill, 3 M Oral Care); and (iii) 3 M-CTR, a conventional composite (Filtek Supreme XTE, 3 M Oral Care). These were used in combination with their adhesives in self-etch (SE) or etch-and-rinse (ER) mode. Specimens stored in artificial saliva (24 h or 12 months) were evaluated for MTBS and fractography. The interfacial analysis was performed through confocal microscopy. ANOVA and Fisher's LSD post hoc tests were performed with a level of significance of 5%. RESULTS: All the tested materials applied in ER mode presented (24 h) greater bond strength than in SE mode. Although all materials showed a significant drop in the bond strength after prolonged storage, STELA showed the highest bonding performance and interfaces with few gaps. 3 M-BULK had the lowest bond strength and an interface with several voids and gaps. CONCLUSIONS: All materials were affected by interface degradation and bonding reduction over prolonged aging. However, their use in combination with adhesives applied in ER mode may offer greater immediate bonding performance. CLINICAL RELEVANCE: The use of restorative light-curing bulk-fill composites may generate gaps at the bonding interface and voids. STELA may represent a suitable alternative to avoid such issues.
Assuntos
Colagem Dentária , Cimentos de Resina , Saliva Artificial , Cimentos de Resina/química , Resinas Compostas/química , Teste de MateriaisRESUMO
PURPOSE: To investigate the effects of different surface treatments and thicknesses on the color, transparency, and surface roughness of ultra-transparent zirconia. METHODS: A total of 120 Katana ultra-translucent multi-layered zirconia specimens were divided into 12 groups according to the thickness (0.3, 0.5, and 0.7 mm) and surface treatment (control, airborne particle abrasion [APA], lithium disilicate coating, and glaze on). Color difference (ΔE00) and relative translucency parameter (RTP00) were calculated using a digital spectrophotometer. The surface roughness (Ra, Rq, Sa, and Sq) was measured using a non-contact profile scanner. The surface morphologies and microstructures of the samples were observed using a tungsten filament scanning electron microscope. Statistical analyses were performed by one-way and two-way analysis of variance (ANOVA) followed by post hoc multiple comparisons and Pearson's correlation (α = 0.05). RESULTS: The results showed that the surface treatment, ceramic thickness, and their interactions had significant effects on ΔE00 and RTP00 (p < 0.001). The surface treatment significantly altered the micromorphology and increased the surface roughness of the ceramic samples. APA exhibited the lowest transparency, largest color difference, and highest surface roughness. Zirconia with 0.3 mm and 0.7 mm thicknesses showed strong negative correlations between Sa and RTP00. CONCLUSIONS: The three internal surface treatments significantly altered the surface roughness, color difference, and transparency of ultra-transparent zirconia. As the thickness increased, the influence of the inner surface treatment on the color difference and transparency of zirconia decreased. CLINICAL IMPLICATIONS: For new zirconia internal surface treatment technologies, in addition to considering the enhancement effect on the bonding properties, the potential effects on the color and translucency of high-transparency zirconia should also be considered. Appropriately increasing the thickness of zirconia restorations helps minimize the effect of surface treatment on the optical properties.
Assuntos
Cor , Teste de Materiais , Microscopia Eletrônica de Varredura , Espectrofotometria , Propriedades de Superfície , Zircônio , Zircônio/química , Porcelana Dentária/química , Materiais Dentários/química , Colagem Dentária/métodosRESUMO
OBJECTIVES: The purpose of this study is to evaluate the bond strength of different computer-aided design / computer-aided manufacturing (CAD/CAM) hybrid ceramic materials following different pretreatments. METHODS: A total of 306 CAD/CAM hybrid material specimens were manufactured, n = 102 for each material (VarseoSmile Crownplus [VSCP] by 3D-printing; Vita Enamic [VE] and Grandio Blocs [GB] by milling). Each material was randomly divided into six groups regarding different pretreatment strategies: control, silane, sandblasting (50 µm aluminum oxide particles), sandblasting + silane, etching (9% hydrofluorics acid), etching + silane. Subsequently, surface roughness (Ra) values, surface free energy (SFE) were measured. Each specimen was bonded with a dual-cured adhesive composite. Half of the specimens were subjected to thermocycling (5000 cycles, 5-55 °C). The shear bond strength (SBS) test was performed. Data were analyzed by using a two-way analysis of variance, independent t-test, and Mann-Whitney-U-test (α = 0.05). RESULTS: Material type (p = 0.001), pretreatment strategy (p < 0.001), and the interaction (p < 0.001) all had significant effects on Ra value. However, only etching on VSCP and VE surface increased SFE value significantly. Regarding SBS value, no significant difference was found among the three materials (p = 0.937), while the pretreatment strategy significantly influenced SBS (p < 0.05). Etching on VSCP specimens showed the lowest mean value among all groups, while sandblasting and silane result in higher SBS for all test materials. CONCLUSIONS: The bond strength of CAD/CAM hybrid ceramic materials for milling and 3D-printing was comparable. Sandblasting and silane coupling were suitable for both millable and printable materials, while hydrofluoric etching should not be recommended for CAD/CAM hybrid ceramic materials. CLINICAL RELEVANCE: Since comparable evidence between 3D-printable and millable CAD/CAM dental hybrid materials is scarce, the present study gives clear guidance for pretreatment planning on different materials.