Hierarchical synthesis of silver nanoparticles and wires by copolymer templates and visible light.
J Colloid Interface Sci
; 352(1): 81-6, 2010 Dec 01.
Article
em En
| MEDLINE
| ID: mdl-20817167
ABSTRACT
Self-assembled silver wires in micro-meter scale were obtained from aqueous silver nitrate solution in the presence of a comb-like copolymer as the sole organic component. The requisite copolymer was easily prepared by the grafting poly(oxyethylene)-monoamine (POE-amine) onto poly(styrene-co-maleic anhydride) (SMA). Upon storage at ambient temperature with exposure to daylight, the aqueous AgNO(3)/SMA-POE solution gradually underwent a color changed from transparent pale-yellow to dark-violet over a period of hours, and after several months a solid precipitate was deposited. The formation process was monitored by ultraviolet-visible spectrometer, particle size analysis, scanning electron microscope, and transmission electron microscope. Silver wires were hierarchically formed by progressive transformation from the initial appearance of silver nanoparticles (ca. 10nm in diameter), followed by the intermediate rectangles (0.6-1.0µm in width and 0.4µm in length) in solution and ultimately the precipitates in micro-scale of silver wires at 1.6-6.4µm in diameter and 100-370µm in length. The progressive formation of the precipitated silver wires was accelerated by the exposure of visible light as a photo-reducing energy source. The micron-scale wires have a silver content over 97.4wt.% and a sheet resistance of 5.5×10(1)Ω/square.
Texto completo:
1
Base de dados:
MEDLINE
Assunto principal:
Compostos Organometálicos
/
Polietilenoglicóis
/
Poliestirenos
/
Prata
/
Nanopartículas Metálicas
/
Nanofios
/
Maleatos
Idioma:
En
Ano de publicação:
2010
Tipo de documento:
Article