Effect of dopants on the soft magnetic properties and high frequency characteristics of FeCoBM (M = Ti, Nb, Hf, and Ta) thin films.

ABSTRACT

Effect of dopants on the soft magnetic properties and high frequency characteristics of FeCoBM thin films (M = Ti, Nb, Hf, and Ta) have been studied. For (Fe0.55Co0.45)(100-x)B(x) (x = 5-15) thin films, with the increase of B content, the resistivity was increased because B could decrease the crystallinity of the films. The (Fe0.55Co0.45)90B10 thin film showed the optimum properties, where 4piM(s) = 16.1 kG, H(ce) = 64.2 Oe, H(ch) = 13.5 Oe, H(k) = 310 Oe and p = 338 microomega-cm. To reduce the coercivity of the film, the elements M, including Ti, Nb, Hf, and Ta, were selected to substitute for B in the FeCoB films. It was found that (Fe0.55Co0.45)90B6Ti2Nb2 thin film after annealing at a temperature of 200 degrees C for 30 min showed the optimal properties, where 4piM(s) = 15.8 kG, H(ce) = 4.8 Oe, H(ch) = 3.6 Oe, H(k) = 224 Oe and p = 290 microomega-cm. The theoretically calculated ferromagnetic resonance frequency of the developed films can be higher than 5 GHz.