Enhanced thermoelectric performance of bar-coated SWCNT/P3HT thin films.

The influence of processing conditions, such as ink concentration and coating method, on the thermoelectric properties of SWCNT/P3HT nanocomposite films was investigated systematically. Using simple wire-bar-coating, SWCNT/P3HT nanocomposite films with high thermoelectric performance could be obtained without additional P3HT doping. The wire-bar-coated SWCNT/P3HT nanocomposite films exhibited power factors of up to 105 µW m(-1) K(-2) at room temperature. The SWCNT bundles with diameters in the range of 6-23 nm formed an interconnected network in the wire-bar-coated nanocomposite films. Network formation in these nanocomposite films was expected to be strongly related to the development of electrical pathways due to inter-SWCNT bundle connections. This study suggests that the thermoelectric performance of SWCNT/P3HT nanocomposite films could be optimized by controlling their processing conditions and morphology.