Characterization of Oxygen Defect Clusters in UO2+ x Using Neutron Scattering and PDF Analysis.

ABSTRACT

In hyper-stoichiometric uranium oxide, both neutron diffraction work and, more recently, theoretical analyses report the existence of clusters such as the 222 cluster, comprising two anion vacancies and two types of anion interstitials. However, little is known about whether there exists a region of low deviation-from-stoichiometry in which defects remain isolated, or indeed whether at high deviation-from-stoichiometry defect clusters prevail that contain more excess oxygen atoms than the di-interstitial cluster. In this study, we report pair distribution function (PDF) analyses of UO2 and UO2+ x ( x ≈ 0.007 and x ≈ 0.16) samples obtained from high-temperature in situ neutron scattering experiments. PDF refinement for the lower deviation from stoichiometry sample suggests the system is too dilute to differentiate between isolated defects and di-interstitial clusters. For the UO2.16 sample, several defect structures are tested, and it is found that the data are best represented assuming the presence of center-occupied cuboctahedra.