Calcium release and physical properties of modified carbonate apatite cement as pulp capping agent in dental application.

ABSTRACT

BACKGROUND: Carbonate apatite (CO3Ap) and silica-calcium phosphate composite (SCPC) are bone substitutes with good prospect for dental application. SCPC creates a hydroxyapatite surface layer and stimulate bone cell function while, CO3Ap induce apatite crystal formation with good adaptation providing good seal between cement and the bone. Together, these materials will add favorable properties as a pulp capping material to stimulate mineral barrier and maintain pulp vitality. The aim of this study is to investigate modification of CO3Ap cement combined with SCPC, later term as CO3Ap-SCPC cement (CAS) in means of its chemical (Calcium release) and physical properties (setting time, DTS and pH value). METHODS: The study consist of three groups; group 1 (100% calcium hydroxide, group 2 CO3Ap (60% DCPA 40% vaterite, and group 3 CAS (60% DCPA 20% vaterite 20% SCPC. Distilled water was employed as a solution for group 1, and 0.2 mol/L Na3PO4 used for group 2 and group 3.Samples were evaluated with respect to important properties for pulp capping application such as pH, setting time, mechanical strength and calcium release evaluation. RESULTS: The fastest setting time was in CO3Ap cement group without SCPC, while the addition of 20% SCPC slightly increase the pH value but did not improved the cement mechanical strength, however, the mechanical strength of both CO3Ap groups were significantly higher than calcium hydroxide. All three groups released calcium ions and had alkaline pH. Highest pH level, as well as calcium released level, was in the control group. CONCLUSION: The CAS cement had good mechanical and acceptable chemical properties for pulp capping application compared to calcium hydroxide as a gold standard. However, improvements and in vivo studies are to be carried out with the further development of this material.