Effect of Ceramic and Nylon Fiber Content on Composite Silica Sol Slurry Properties and Bending Strength of Investment Casting Shell.

ABSTRACT

In order to improve the performance of the investment casting shell, ceramic and nylon fiber was added to the silica sol slurry to study the effect of ceramic and nylon fiber on the liquidity of the silica sol slurry and the bending strength of the investment casting shell. Meanwhile, the fracture surface of shell sample was observed by SEM. The experiment results indicate that the movement viscosity of slurry increases with ceramic and nylon fiber content, increasing from 0 to 0.75 wt.%. The movement viscosity of ceramic fiber composite slurry is higher than nylon fiber composite slurry. The wet and high strength of shell firstly increases then decreases, with an increase of ceramic and nylon fiber content. When the ceramic and nylon fibers' contents are 0.6 wt.%, the maximum wet strengths are 3.56 MPa and 3.84 Mpa respectively, increasing by approximately 38% and 43%. Moreover, the high strength of shell achieves its highest value, 5.08 Mpa, when the ceramic fiber content is 0.6 wt.%; however, when the nylon fiber content was more than 0.3%, the high strength of the nylon fiber reinforced shell was decreased sharply. Therefore, an addition of ceramic and nylon fiber to silica sol slurry distinctly influences the wet and high strength of investment casting shell.