Shear bond strength of a self-adhesive resin cement to dentin surface treated with Nd:YAG and femtosecond lasers.

This study aims to evaluate the effect of Nd:YAG and femtosecond lasers irradiation on the shear bond strength (SBS) of a self-adhesive resin cement to the human dentin surface. One hundred extracted third molar teeth were randomly divided into 10 experimental groups according to dentin surface treatments; with and without the bonding agent, Nd:YAG 302 J/cm2 and 440 J/cm2, femtosecond 4 J/cm2 and 7 J/cm2, and control groups were prepared. After surface treatments, a self-adhesive resin cement was luted by using a bonding jig (Ultradent Products Inc.). The specimens were then subjected to shear test at a crosshead speed of 0.5 mm/min, and failure loads were recorded as megapascal (MPa). Two-way analysis of variance and Tukey HSD tests were performed (p Ë‚ 0.05). Representative specimens from each experimental subgroup were examined by means of SEM. The highest SBS values were obtained in Group 302 J/cm2 Nd:YAG with bonding agent, and there is no statistical difference between Group 440 J/cm2 Nd:YAG with bonding and Group 7 J/cm2 femtosecond with bonding (p > 0.05). The lowest SBS values were observed in Group control without bonding agent. Nd:YAG and femtosecond laser treatments improved the adhesion between the dentin surface and the self-adhesive resin cement.