In-lab simulation of CAD/CAM grinding and intaglio surface treatments of 4YSZ monolithic restorations: Effect on its load-bearing capacity under fatigue.

ABSTRACT

OBJECTIVES: To evaluate the effect of in-lab simulation of CAD/CAM grinding and intaglio surface treatments on the surface characteristics (topography and roughness) and fatigue behavior of adhesively luted 4YSZ simplified restorations. METHODS: Ceramic discs (Ø = 10 mm, thickness = 1 mm) were randomly allocated into 6 groups considering "In-lab simulation of CAD/CAM grinding" (ground or polished) and "intaglio surface treatments" Ctrl (without surface treatment), AlOx (aluminum oxide air abrasion) or GLZ (glaze spray application). The surface roughness of all samples was measured, the treated discs received a ceramic primer, were luted with resin cement onto a dentin analogue material (woven glass-reinforced epoxy resin) and tested under a cyclic fatigue test (step-stress approach, n = 15; 1.4 Hz, 10,000 cycles/step, step-size of 100N starting at 200N until failure). A complementary analysis was performed to corroborate the findings in the fatigue test that the glaze fill defects increase the mechanical properties of the ceramic. To do so, bars (n= 10; 1.0 × 1.0 × 12 mm; considering the groups N-ID non-indented; ID indented; ID-GLZ indented plus glaze spray application) were indented in a vickers hardness tester to produce a crack pattern, treated with glaze or not, and then submitted to flexural strength tests (FS). Fractographic and topographic analysis were performed. RESULTS: In-lab simulation of CAD/CAM grinding decreased the fatigue failure load of the 4YSZ ceramic when comparing polished and ground groups, regardless of surface treatment. GLZ induced better fatigue performance compared to the air abrasion, regardless of the grinding condition (ground or polished surface). The results of the flexural strength test corroborated the findings in the fatigue test, as the ID-GLZ group presented superior FS than the ID group, however both had inferior FS than N-ID. There is an inverse association between roughness and fatigue failure load, as the higher the surface roughness, the lower the fatigue failure load. Failures in the fatigue and flexural strength tests started from the face subjected to tensile stresses. CONCLUSION: In-lab simulation of CAD/CAM grinding had a detrimental effect on the fatigue behavior of 4YSZ and glaze spray induced better 4YSZ performance compared to the air abrasion. The intaglio surface treatments differently influenced the 4YSZ fatigue performance, however, only glaze spray can reverse the damage caused by the grinding.