Dual-Porosity (Ta0.2Nb0.2Ti0.2Zr0.2Hf0.2)C High-Entropy Ceramics with High Compressive Strength and Low Thermal Conductivity Prepared by Pressureless Sintering.

ABSTRACT

Porous (Ta0.2Nb0.2Ti0.2Zr0.2Hf0.2)C high-entropy ceramics (HEC) with a dual-porosity structure were fabricated by pressureless sintering using a mixture powder of ceramic precursor and SiO2 microspheres. The carbothermal reduction in the ceramic precursor led to the formation of pores with sizes of 0.4-3 µm, while the addition of SiO2 microspheres caused the appearance of pores with sizes of 20-50 µm. The porous HECs exhibit competitive thermal insulation (4.12-1.11 W·m-1 k-1) and extraordinary compressive strength (133.1-41.9 MPa), which can be tailored by the porosity of the ceramics. The excellent properties are ascribed to the high-entropy effects and dual-porosity structures. The severe lattice distortions in the HECs lead to low intrinsic thermal conductivity and high compressive strength. The dual-porosity structure is efficient at phonon scattering and inhabiting crack propagations, which can further improve the thermal insulation and mechanical properties of the porous HECs.