PLA-PEG forming worm-like nanoparticles despite unfavorable packing parameter: Formation mechanism, thermal stability and potential for cell internalization.
Int J Pharm
; 643: 123263, 2023 Aug 25.
Article
em En
| MEDLINE
| ID: mdl-37482230
ABSTRACT
Most nanoparticles produced for drug delivery purposes are spherical. However, the literature suggests that elongated particles are advantageous, notably in terms of cellular uptake. Thus, we synthesized biocompatible polylactide-b-poly(ethylene glycol) (PLA-PEG) polymers bearing carboxylate moieties, and used them to formulate worm-like nanoparticles by a simple emulsion-evaporation process. Worm-like nanoparticles with variable aspect ratio were obtained by simply adjusting the molar mass of the PLA block the shorter the molar mass of the PLA block, the more elongated the particles. As PLA molar mass decreased from 80,000 g/mol to 13,000 g/mol, the proportion of worm-like nanoparticles increased from 0 to 46%, in contradiction with the usual behavior of block polymers based on their packing parameter. To explain this unusual phenomenon, we hypothesized the shape arises from a combination of steric and electrostatic repulsions between PEG chains bearing a carboxylate moiety present at the dichloromethane-water interface during the evaporation process. Worm-like particles turned out to be unstable when incubated at 37 °C, above polymer glass transition temperature. Indeed, above Tg, a Plateau-Rayleigh instability occurs, leading to the division of the worm-like particles into spheres. However, this instability was slow enough to assess worm-like particles uptake by murine macrophages. A slight but significant increase of internalization was observed for worm-like particles, compared to their spherical counterparts, confirming the interest of developing biocompatible anisotropic nanoparticles for pharmaceutical applications such as drug delivery.
Palavras-chave
Texto completo:
1
Base de dados:
MEDLINE
Assunto principal:
Polímeros
/
Nanopartículas
Limite:
Animals
Idioma:
En
Ano de publicação:
2023
Tipo de documento:
Article