Plasma-Sprayed (Bi2O3)0.705 (Er2O3)0.245 (WO3)0.05 Electrolyte for Intermediate-Temperature Solid Oxide Fuel Cells (IT-SOFCs).
J Therm Spray Technol
; 31(1-2): 297-306, 2022.
Article
em En
| MEDLINE
| ID: mdl-37520912
ABSTRACT
Stabilized bismuth oxide material with fluorite structure (δ-Bi2O3) has been studied as a promising electrolyte material for intermediate temperature solid oxide fuel cells (IT-SOFCs) due to its high oxygen ion conductivity in mediate temperature. Especially, the ternary system Bi2O3-Er2O3-WO3 is widely concerned for its high ionic conductivity and thermal stability. In this study, regarding its low melting point, the possibility to deposit dense Bi2O3-Er2O3-WO3 ((Bi2O3)0.705 (Er2O3)0.245 (WO3)0.05, EWSB) electrolyte by plasma spraying was examined. It was confirmed that the sintered EWSB bulk presents a high ion conductivity of 0.34 S cm-1 at 750 °C and excellent stability that indicates no structure transformation and conductivity degradation after annealing at 600 °C for 1000 h. The phase structure and cross-sectional microstructure of plasma-sprayed EWSB were characterized by XRD and SEM. Results showed that the as-plasma-sprayed EWSB presents a dense microstructure with well bonded lamellae. The XRD showed the formation of EWSB with δ-phase and a trace of ß-phase, while the ß-phase disappeared after annealing at 750 °C for 10 h. The deposited EWSB electrolyte presented the excellent ionic conductivity of 0.26 S cm-1 at 750 °C which can be directly applied to SOFC at intermediate temperature.
Texto completo:
1
Base de dados:
MEDLINE
Idioma:
En
Ano de publicação:
2022
Tipo de documento:
Article