Recycling Local Waste Glass Bottles into Cement Paste: Effect on Hydration, Microstructure, and CO2 Emission.

Large amounts of waste glass are generated along with the manufacturing of glass products, causing detrimental effects on the environment. Through crushing and ball-milling, waste glass powder (WGP) can be acquired from glass bottles and has been suggested in cementitious systems due to its potential pozzolanic activity. To better understand the impact of WGP on cementitious composites, experimental tests of rheology, heat of hydration, and strength development were conducted on cement pastes with and without WGP. Results show that the rheological performance of cement paste is improved when WGP with particles passing through 80 µm sieves is incorporated. The retarding effect and pozzolanic reaction were observed through X-ray diffraction patterns and thermo-gravimetric parameter analyses. A calcium hydroxide (CH) content calculation further confirms the secondary reactivity of WGP in cement pastes. Compared with the samples without WGP, the normalized CH content of binder per unit mass containing 35% WGP decreased by 21.01%, 24.94%, and 27.41% at the ages of 1, 28, and 90 days, respectively, which contributes to late-age strength development of pastes. At the same time, the hydration per unit of cement was increased by 21.53%, 15.48%, and 11.68%, which improved the cement efficiency. In addition, WGP particles provide nuclei for hydration products, facilitating the subsequent growth of C-S-H and strength development in late ages. Based on value engineering analysis, WGP was found to reduce the impact of Portland cement on the environment by 34.9% in terms of carbon dioxide emissions, indicating a bright prospect for WGP in the cement industry.