Enhanced Cathode Performance: The Heterostructure Construction of LiCoO2@Co3O4@Li6.4La3Zr1.4Ta0.6O12.

ABSTRACT

In this study, the heterostructure cathode material LiCoO2@Co3O4@Li6.4La3Zr1.4Ta0.6O12 was prepared by coating Li6.4La3Zr1.4Ta0.6O12 on the surface of LiCoO2 through a one-step solid-phase synthesis. The morphology, structure, electrical state, and elemental contents of both pristine and modified materials were assessed through a range of characterization techniques. Theoretical calculations revealed that the LCO@LLZTO material possessed a reduced diffusion barrier compared to LiCoO2, thereby facilitating the movement of Li ions. Electrochemical tests indicated that the capacity retention rate of the modified cathode composites stood at 70.43% following 300 cycles at a 2C rate. This high rate occurred because the Li6.4La3Zr1.4Ta0.6O12 film on the surface enhanced the migration of Li+, and the spinel phase of Co3O4 had better interfacial stability to alleviate the generation of microcracks by inhibiting the phase change from the layered phase to the rock-salt phase, which considerably improved the electrochemical properties.