Statistical Analysis of Morphological Characteristics of Inconel 718 Formed by High Deposition Rate and High Laser Power Laser Cladding.

ABSTRACT

Laser cladding is one of the emerging additive manufacturing technologies and has been adopted in various industrial fields. In this study, the morphological characteristics of a single clad of Inconel 718 manufactured by coaxial laser cladding with high laser power from 4200 W to 5400 W, powder feeding rate from 25 g/min to 50 g/min, and cladding speed from 20 mm/s to 50 mm/s are studied. The cross-section of the melt pool is analyzed and classified by type into three types shallow dilution, flat dilution, and fluctuating dilution. Nine parameters are designed to describe the morphological characteristics of the clad, and the corresponding linear regression models are developed to establish a quantitative relationship between the combined process parameters and morphological characteristics. The results indicate that the total area of the cross-section A, the clad area above the substrate Ac, the area of the molten substrate Am, the total height of the cross-section H, the height of the clad above the substrate hc, the penetration depth hm, the clad width W, the dilution ratio D, and the wetting angle θ are determined by complex coupling of energy input and mass accumulation, and they are proportional to PF0.4/V, P0.5F/V, P/F0.2/V0.4, P2F0.6/V, PF0.7/V, P2/F/V0.3, P/V0.8, P/FV0.2, and PF7/V0.8, respectively. The large linear regression coefficients and the analysis residuals indicate the high reliability of the statistical linear regression models. This work aims to provide a comprehensive understanding of the influence of the main processing parameters on the morphological characteristics of the clad, which is of great value in providing a reference and laying a basis for the practical application of laser cladding technology at a high deposition rate.