Preparation and Characterization of Durian Husk-Based Biocomposite Films Reinforced With Nanocellulose From Corn Husk and Pineapple Leaf.
Biopolymers
; : e23619, 2024 Aug 08.
Article
em En
| MEDLINE
| ID: mdl-39115118
ABSTRACT
This research explores the integration of corn husk nanocellulose (CHNc) and pineapple leaf nanocellulose (PLNc) as reinforcing agents in a carboxymethyl cellulose-based film derived from durian husk (CMCDH). Through a solvent-casting method, composite films were fabricated with varying nanocellulose contents (15, 30, and 45 wt%). Analysis using Fourier transform infrared spectroscopy and x-ray diffraction confirmed the effectiveness of alkaline and bleaching treatments in eliminating noncellulosic components. Transmission electron microscopy image revealed the rod-like morphology of CHNc and PLNc, with dimensions approximately 206.5 × 7.2 nm and 150.7 × 6.5 nm, respectively. The inclusion of nanocellulose decreased the transparency of CMCDH films while enhancing their tensile strength, thermal stability, and water vapor transmission rate. Notably, CMCDH/PLNc(30%) exhibited the highest tensile strength at 5.06 ± 0.83 MPa, representing a remarkable 220% increase compared to CMCDH biofilm. Thermogravimetric analysis and differential scanning calorimeter results indicated that nanocellulose incorporation delayed the film's decomposition temperature by approximately 10°C. Moreover, CMCDH/PLNc(30%) demonstrated the lowest water vapor transmission rate, marking a 20% improvement. However, the film's properties were compromised at the highest nanocellulose content (45 wt%) due to observed fiber aggregation, as revealed by scanning electron microscopy analysis.
Texto completo:
1
Base de dados:
MEDLINE
Idioma:
En
Ano de publicação:
2024
Tipo de documento:
Article