Fire propagation performance of intumescent fire protective coatings using eggshells as a novel biofiller.

This paper aims to synthesize and characterize an effective intumescent fire protective coating that incorporates eggshell powder as a novel biofiller. The performances of thermal stability, char formation, fire propagation, water resistance, and adhesion strength of coatings have been evaluated. A few intumescent flame-retardant coatings based on these three ecofriendly fire retardant additives ammonium polyphosphate phase II, pentaerythritol and melamine mixed together with flame-retardant fillers, and acrylic binder have been prepared and designed for steel. The fire performance of the coatings has conducted employing BS 476: Part 6-Fire propagation test. The foam structures of the intumescent coatings have been observed using field emission scanning electron microscopy. On exposure, the coated specimens' B, C, and D had been certified to be Class 0 due to the fact that their fire propagation indexes were less than 12. Incorporation of ecofriendly eggshell, biofiller into formulation D led to excellent performance in fire stopping (index value, (I) = 4.3) and antioxidation of intumescent coating. The coating is also found to be quite effective in water repellency, uniform foam structure, and adhesion strength.

Optimization of ultrasonication period for better dispersion and stability of TiO2-water nanofluid.

Nanofluids are promising in many fields, including engineering and medicine. Stability deterioration may be a critical constraint for potential applications of nanofluids. Proper ultrasonication can improve the stability, and possibility of the safe use of nanofluids in different applications. In this study, stability properties of TiO2-H2O nanofluid for varying ultrasonication durations were tested. The nanofluids were prepared through two-step method; and electron microscopies, with particle size distribution and zeta potential analyses were conducted for the evaluation of their stability. Results showed the positive impact of ultrasonication on nanofluid dispersion properties up to some extent. Ultrasonication longer than 150min resulted in re-agglomeration of nanoparticles. Therefore, ultrasonication for 150min was the optimum period yielding highest stability. A regression analysis was also done in order to relate the average cluster size and ultrasonication time to zeta potential. It can be concluded that performing analytical imaging and colloidal property evaluation during and after the sample preparation leads to reliable insights.

Effective ultrasonication process for better colloidal dispersion of nanofluid.

Improving dispersion stability of nanofluids through ultrasonication has been shown to be effective. Determining specific conditions of ultrasonication for a certain nanofluid is necessary. For this purpose, nanofluids of varying nanoparticle concentrations were prepared and studied to find out a suitable and rather mono-dispersed concentration (i.e., 0.5 vol.%, determined through transmission electron microscopy (TEM) analyses). This study aims to report applicable ultrasonication conditions for the dispersion of Al2O3 nanoparticles within H2O through the two-step production method. The prepared samples were ultrasonicated via an ultrasonic horn for 1-5h at two different amplitudes (25% and 50%). The microstructure, particle size distribution (PSD), and zeta potentials were analyzed to investigate the dispersion characteristics. Better particle dispersion, smaller aggregate sizes, and higher zeta potentials were observed at 3 and 5h of ultrasonication duration for the 50% and 25% of sonicator power amplitudes, respectively.