Production of a NiO/Al primary battery employing powder-based electrodes.

This paper describes the use of aluminum and zinc as anodic materials for a battery employing nickel (II) oxide (NiO) as cathode. Comparison of both materials resulted in the development of a compact, cost effective, and easy to use primary NiO/Al battery employing an alkaline electrolyte. The system features electrodes composed of powder forms of the active materials on modified paper substrates that are contained in a simple multilayer design utilizing thin laminated plastic materials to provide structure and flexibility to the battery as well as a paper separator. Various concentrations of potassium hydroxide (KOH) electrolyte were examined and maximum performance was observed at 6 M KOH. A maximum current density and power density of 1.94 mA/cm2 and 1 mW/cm2 , respectively was achieved. This user-friendly device was able to produce a maximum capacity of 2.33 mAh/g when 2 mA/g was applied. This work demonstrates the viability of a paper-based battery featuring powder electrodes as a possible power source for microelectronic devices.

Inorganic Solid-State Electrolytes for Lithium Batteries: Mechanisms and Properties Governing Ion Conduction.

This Review is focused on ion-transport mechanisms and fundamental properties of solid-state electrolytes to be used in electrochemical energy-storage systems. Properties of the migrating species significantly affecting diffusion, including the valency and ionic radius, are discussed. The natures of the ligand and metal composing the skeleton of the host framework are analyzed and shown to have large impacts on the performance of solid-state electrolytes. A comprehensive identification of the candidate migrating species and structures is carried out. Not only the bulk properties of the conductors are explored, but the concept of tuning the conductivity through interfacial effects-specifically controlling grain boundaries and strain at the interfaces-is introduced. High-frequency dielectric constants and frequencies of low-energy optical phonons are shown as examples of properties that correlate with activation energy across many classes of ionic conductors. Experimental studies and theoretical results are discussed in parallel to give a pathway for further improvement of solid-state electrolytes. Through this discussion, the present Review aims to provide insight into the physical parameters affecting the diffusion process, to allow for more efficient and target-oriented research on improving solid-state ion conductors.