Synthesis, characterization, and osteocompatibility evaluation of novel alanine-based polyphosphazenes.

This study deals with the synthesis and in vitro osteocompatibility evaluation of two novel alanine-containing biodegradable ester polyphosphazenes as candidates to form self-setting composites with hydroxyapatite (HAp) precursors. The two novel biodegradable polyphosphazenes synthesized were poly[(ethyl alanato)1.0(ethyl oxybenzoate)1.0 phosphazene] (PN-EA/EOB) and poly[(ethyl alanato)1.0(propyl oxybenzoate)1.0 phosphazene] (PN-EA/POB). The polymers were characterized by multinuclear magnetic resonance (NMR), differential scanning calorimetry (DSC), and gel permeation chromatography (GPC). Biodegradability and percentage water absorption of the polymers were evaluated by following the mass change in phosphate buffer (pH 7.4) at 37 degrees C. PN-EA/POB underwent faster degradation and showed higher water absorption compared to PN-EA/EOB. Both polymers became insoluble in common organic solvents following hydrolysis presumably due to crosslinking reactions accompanying the degradation process. Osteoblast cell adhesion and proliferation on PN-EA/EOB and PN-EA/POB was followed by scanning electron microscopy (SEM) and by using a biochemical assay. Both PN-EA/EOB and PN-EA/POB supported the adhesion and proliferation of primary rat osteoblast cells in vitro. Furthermore, the enzymatic activity of the osteoblast cells cultured on the polymers was confirmed by the alkaline phosphatase activity. Thus, these biodegradable amino-acid-based polyphosphazenes are promising new materials for forming self-setting bone cements.

Patterning poly(organophosphazenes) for selective cell adhesion applications.

Five polyphosphazenes with different hydrophilicites were synthesized and screened in vitro. The purpose was to identify unique types of polymeric substrates that distinctly favored or markedly prevented cellular adhesion. The SK-N-BE(2c) human neuroblastoma cell line, utilized for its electrogenic responses, was used to test this differential adhesion. In particular, the objective was to specifically culture this cell line in a highly selective pattern. Each candidate polymer was cast into films and plated with neuroblastoma cells for 3 days. The polyphosphazene materials which showed negative cellular adhesive properties (-CAPs) were poly[bis(trifluoroethoxy)phosphazene] (TFE) and poly[bis(methoxyethoxyethoxy)phosphazene] (MEEP). The polyphosphazenes which showed positive cellular adhesive properties (+CAPs) were poly[(methoxyethoxyethoxy)(1.0)(carboxylatophenoxy)(1.0)phosphazene] (PMCPP), poly[(methoxyethoxyethoxy)(1.0)(cinnamyloxy)(1.0)phosphazene] (PMCP), and poly[(methoxyethoxyethoxy)(1.0)(p-methylphenoxy)(1.0)phosphazene] (PMMP). To test cellular selectivity, films of -CAP and +CAP were copatterned onto glass substrates. The micropatterned films were plated with SK-N-BE(2c) neuroblastoma cells for one week. The results showed that neuroblastoma cells adhere selectively (over 60%) to the +CAP microfeatures. We also showed that multiple properties can be achieved with a single material and that we can use TFE as both a -CAP and an insulation layer and PMCP as a conductive +CAP layer.