Conversion of char from pyrolysis of plastic wastes into alternative activated carbons for heavy metal removal.

The valorization of post-consumer mixed plastics in pyrolysis processes represents an abundant reservoir of carbon that can be effectively converted into useful chars. This process not only holds appeal in terms of improving plastic waste concerns but also contributes to the reduction of greenhouse gas emissions, thus aligning with the principles of a circular economy paradigm. In this study, the char produced from the pyrolysis of post-consumer mixed plastic waste has been activated with Na2CO3, KOH, NaOH, and K2CO3 to improve the textural, structural, and composition characteristics, leading to improved adsorption capability. These characteristics were studied by N2 adsorption-desorption isotherms, scanning electron microscopy, elemental and immediate analysis, and X-ray photoelectron spectroscopy. The developed surface area (SBET) was 573, 939, 704 and 592 m2 g-1 for Na2CO3, KOH, NaOH and K2CO3 activated carbons, respectively. These activated chars (ACs) were tested for the adsorption of heavy metals in both synthetic waters containing Pb, Cd, and Cu and industrial wastewater collected at an agrochemical production plant. Na2CO3-AC was the best performing material. The metal uptake in synthetic waters using a batch set-up was 40, 13 and 12 mg g-1 for Pb, Cd and Cu. Experiments in a column set-up using Na2CO3-AC resulted in a saturation time of 290, 16, and 80 min for Pb, Cd, and Cu synthetic waters, respectively, and metal uptakes of 26.8, 4.1, and 7.9 mg g-1, respectively. The agrochemical effluents, containing mainly Cr, Cu, Mn, and Zn were tested in a plug-flow column. The metal uptake notably decreased compared to synthetic water due to a competition effect for active sites.

Life-Cycle Assessment of the thermal and catalytic pyrolysis over sepiolite of face masks.

Since the start of the global COVID-19 pandemic, extensive quantities of face masks have been used and discarded. Most of these masks end up in landfills, causing a high environmental impact and no benefits. However, there are alternative ways to deal with this waste in a more sustainable way. For example, valorisation of face masks through pyrolysis has received special attention because it offers efficient application to produce a liquid oil that can be used as a diesel substitute and a solid char that can be used as an activated carbon substitute after activation. In this context, this study applies the Life-Cycle Assessment methodology to quantify and analyse the environmental impacts of different treatment scenarios based on the pyrolysis of surgical masks and FFP2 masks. It also compares their environmental performance with the conventional practice of landfilling. The scenarios studied include both thermal and catalytic pyrolysis by using sepiolite, a low-cost material abundant in Spain. Data on the pyrolysis process were obtained from laboratory experiments. It was found that the use of the produced oil as a diesel substitute very significantly reduces the environmental impact in all pyrolysis scenarios. Consequently, the pyrolysis of face masks can reduce the environmental impact caused by the treatment of this waste material. Furthermore, the thermal pyrolysis performs environmentally better than the catalytic pyrolysis. In all scenarios, freshwater ecotoxicity and marine ecotoxicity are the environmental impact categories that cause the highest environmental impact overall.

Effects of distance to the sea and geomorphological characteristics on the quantity and distribution of microplastics in beach sediments of Granada (Spain).

Microplastics became an unprecedented challenge and mapping their contamination all over the world is needed in order to establish baseline levels and identify the polymers in order to enhance adequate legislation and policy. The main objective of this study is to demonstrate the existence of microplastic pollution on three beaches on the coast of Granada (Spain), namely La Herradura, Motril Beach and La Rábita, characterizing the particles and the relationships in their distribution. This may contribute supporting the studies carried out at a national level in accordance with the Directive on Marine Strategy (2008/56/EC). The results showed a greater median concentration of particles/kg of dry sediment in La Herradura (45.0 ±â€¯24.7) than in Motril (31.5 ±â€¯21.5) and La Rábita (22.0 ±â€¯23.2). These data revealed a higher contamination by microplastics in an enclosed bay-type beach (La Herradura) in comparison with open delta-type beaches. The predominant morphologies were microspheres and fragments, with maximum median concentrations of 38.0 ±â€¯23.7 and 6.0 ±â€¯0.7 particles/kg, respectively. The distribution and size of the particles is affected by the geomorphological and sedimentary characteristics of these beaches, which are different from any other in Spain and in the Mediterranean in general. The beaches of Granada showed more microplastic contamination than Greek or Slovenian beaches, but less than other Spanish beaches. In this area of the Mediterranean, the presence of microplastics can be affected by the wind, sea currents or methodological aspects such as the pore size of the filters used. All of these factors were analysed when comparing the beaches of Granada with other Mediterranean beaches. This study shows that there is contamination by microplastics on the beaches of Granada, which have been little explored until now due to the difficult geological and granulometric characteristics, and gives support to other national studies.

Effect of torrefaction conditions on greenhouse crop residue: Optimization of conditions to upgrade solid characteristics.

This work investigated the possibility of using a greenhouse crop waste as a fuel, since it is an abundant residue in the Mediterranean area of Spain. The residue is mainly composed by biomass with a little quantity of plastic. The physical and chemical characteristics of the biomass were determined by elemental analysis, proximate analysis, FT-IR, FE-SEM and thermogravimetry. Additionally, a torrefaction process was carried out as a pre-treatment to improve the energy properties of the biomass material. The optimal conditions (time and temperature) of torrefaction were found to be 263°C and 15min using the gain and loss method. Further studies were carried out with the sample prepared with the nearest conditions to the optimal in order to determine the effect of the plastic fraction in the characteristics and torrefaction process of the waste studied.

Kinetics of thermal decomposition of some biomasses in an inert environment. An investigation of the effect of lead loaded by biosorption.

The thermal behavior of some types of raw and lead-polluted biomasses typical in south Spain was studied by non-isothermal thermogravimetry. Experiments were carried out in nitrogen atmosphere at three heating rates (5, 10 and 20°C/min). The results of thermogravimetric tests carried out proved that the presence of lead did not change the main degradation pathways of selected biomass (almond shell (AS) and olive pomace (OP)). However, from a point of view of mass loss, lead-polluted samples showed higher decomposition temperatures and decomposition at higher rate. The determination of activation energies was performed by isoconversional methods of Flynn-Wall-Ozawa (FWO), Kissinger-Akahira-Sunose (KAS) and Friedman (FR). In general, lead-polluted samples showed lower activation energies than raw ones. Then, Coast-Redfern method was applied to determine kinetic function. The kinetic function that seems to determine the mechanism of thermal degradation of main components of all samples was nth order reaction. Finally, a model based on three parallel reactions (for three pseudocomponents) that fit to nth order reactions was evaluated. This model was appropriate to predict the pyrolysis behavior of the raw and lead-polluted samples in all pyrolysis conditions studied.