Histological evaluation of osseointegration between conventional and novel bone-level tapered implants in healed bone-A preclinical study.

AIMS: To histologically compare osseointegration and crestal bone healing between newly introduced tapered, self-cutting bone-level test implants and tapered bone-level control implants in sites with fully healed sites. METHODS: Sixty-six implants (33 test, 33 control) were placed 1 mm subcrestally in a minipig model and underwent qualitative histologic and quantitative histometric analyses after 3, 6 and 12 weeks of submerged healing. The primary and secondary outcomes were the bone-to-implant contact (BIC) and first bone-to-implant contact (fBIC). Outcomes between the test and control implants were statistically compared. RESULTS: The BIC values of the test implants were comparable and non-inferior over the time points studied, except for the 12 weeks time point which showed statistically significantly higher BIC values of the test (88.07 ± 5.35%) compared to the control implants (80.88 ± 7.51%) (p = .010). Similarly comparable and non-inferior were the fBIC values, except for the 6-week outcome, which showed statistically higher values for the test (-546.5 ± 450.80 µm) compared to the control implants (-75.7 ± 100.59 µm). fBIC results for the test implants were qualitatively more stable and consistent between test time points. CONCLUSION: Novel self-cutting bone-level test implants demonstrated superior osseointegration and similar bone levels compared to conventional bone-level implants after a healing period of 12 weeks in healed ridges.

Preclinical evaluation of a new synthetic carbonate apatite bone substitute on periodontal regeneration in intrabony defects.

OBJECTIVE: To evaluate the potential of a novel synthetic carbonate apatite bone substitute (CO3 Ap-BS) on periodontal regeneration. BACKGROUND: The use of various synthetic bone substitutes as a monotherapy for periodontal regeneration mainly results in a reparative healing pattern. Since xenografts or allografts are not always accepted by patients for various reasons, a synthetic alternative would be desirable. METHODS: Acute-type 3-wall intrabony defects were surgically created in 4 female beagle dogs. Defects were randomly allocated and filled with CO3 Ap-BS (test) and deproteinized bovine bone mineral (DBBM) or left empty (control). After 8 weeks, the retrieved specimens were scanned by micro-CT, and the percentages of new bone, bone substitute, and soft tissues were evaluated. Thereafter, the tissues were histologically and histometrically analyzed. RESULTS: Healing was uneventful in all animals, and defects were present without any signs of adverse events. Formation of periodontal ligament and cementum occurred to varying extent in all groups without statistically significant differences between the groups. Residues of both bone substitutes were still present and showed integration into new bone. Histometry and micro-CT revealed that the total mineralized area or volume was higher with the use of CO3 Ap-BS compared to control (66.06 ± 9.34%, 36.11 ± 6.40%; p = .014, or 69.74 ± 2.95%, 42.68 ± 8.68%; p = .014). The percentage of bone substitute surface covered by new bone was higher for CO3 Ap-BS (47.22 ± 3.96%) than for DBBM (16.69 ± 5.66, p = .114). CONCLUSIONS: CO3 Ap-BS and DBBM demonstrated similar effects on periodontal regeneration. However, away from the root surface, more new bone, total mineralized area/volume, and higher osteoconductivity were observed for the CO3 Ap-BS group compared to the DBBM group. These findings point to the potential of CO3 Ap-BS for periodontal and bone regeneration.

Vitality of autologous retromolar bone grafts for alveolar ridge augmentation after a 3-months healing period: A prospective histomorphometrical analysis.

OBJECTIVES: The incorporation of retromolar bone grafts used for alveolar ridge augmentation is not well understood. This prospective observational study aims to supply histomorphometrical data from bone graft biopsies taken at the time of retrieval and after a 3-month healing period using patient-matched biopsies. MATERIALS AND METHODS: In 17 patients, trephine biopsies of the graft were acquired at the time of graft retrieval and after a 3-month healing period. The biopsies were compared histomorphometrically regarding the number of osteocytes, appearance of osteocyte lacunae, quantity, surface area, and activity of the Haversian canals. RESULTS: All grafts appeared clinically stable after screw removal and 17 implants were placed. Histomorphometric analysis revealed no significant difference in the number of osteocytes (p = .413), osteocyte lacunae (p = .611), the ratio of filled/empty osteocyte lacunae (p = .467) and active Haversian canals (p = .495) between the biopsies retrieved after a 3-months healing period with those at the time of grafting. The only significant difference was noted in the mean surface area of the Haversian canals (p = .002). Specifically, the grafts post 3-month healing showed a significantly larger mean area (0.069 mm2) compared to the time of grafting (0.029 mm2). CONCLUSION: This study demonstrates, compared to other data, a high rate of vital structures in retromolar bone block grafts after 3 months of healing, exhibiting the same histological features in comparison to the biopsies from the native alveolar ridge. Standard histomorphometrical parameters, e.g., the amount of filled or empty osteocyte lacunae for the description of the vitality of the graft need to be reappraised.

Osteoinduction and osteoimmunology: Emerging concepts.

The recognition and importance of immune cells during bone regeneration, including around bone biomaterials, has led to the development of an entire field termed "osteoimmunology," which focuses on the connection and interplay between the skeletal system and immune cells. Most studies have focused on the "osteogenic" capacity of various types of bone biomaterials, and much less focus has been placed on immune cells despite being the first cell type in contact with implantable devices. Thus, the amount of literature generated to date on this topic makes it challenging to extract needed information. This review article serves as a guide highlighting advancements made in the field of osteoimmunology emphasizing the role of the osteoimmunomodulatory properties of biomaterials and their impact on osteoinduction. First, the various immune cell types involved in bone biomaterial integration are discussed, including the prominent role of osteal macrophages (OsteoMacs) during bone regeneration. Thereafter, key biomaterial properties, including topography, wettability, surface charge, and adsorption of cytokines, growth factors, ions, and other bioactive molecules, are discussed in terms of their impact on immune responses. These findings highlight and recognize the importance of the immune system and osteoimmunology, leading to a shift in the traditional models used to understand and evaluate biomaterials for bone regeneration.

Spontaneous regeneration of keratinized tissue at implants and teeth.

AIM: To investigate the spontaneous regeneration of the implanto-mucosal and dento-gingival unit after complete removal of keratinized tissue (KT). MATERIALS AND METHODS: One hemi-mandible per dog (n = 4) was allocated to receive three dental implants (test sites, premolar region), whereas three premolars on the contralateral side were controls. After osseointegration, the entire KT (buccal + lingual) was surgically excised on all test and control sites, leaving the bone exposed. Clinical measurements were performed before excision (T0 ) and after 12 weeks (T1 ). Following healing, the animals were euthanized, and the specimens were histologically processed. Descriptive statistical analyses were performed. RESULTS: Clinical measurements revealed that at T1 , on all teeth, a band of KT was spontaneously regenerated (mean width: 2.60 ± 0.66 mm), whereas on implants, KT was detected only occasionally at mesial or distal but not at buccal sites (mean total: 0.35 ± 0.53 mm; p < .0001). Histologically, spontaneous regeneration of the dento-gingival unit was evident, displaying masticatory mucosa. At the implant sites, on the other hand, the implanto-mucosal unit was characterized by a non-keratinized epithelium and elastic fibres, indicating the characteristics encountered in alveolar mucosa. CONCLUSION: After excision of KT at implant sites, the spontaneous regeneration of the soft tissue is characterized by a non-keratinized epithelium typical for alveolar mucosa, while at tooth sites the spontaneous regeneration was characterized by soft tissue resembling gingiva.

Sequential osseointegration of a novel implant system based on 3D printing in comparison with conventional titanium implants.

OBJECTIVES: To evaluate the sequential osseointegration of a novel titanium implant system based on a 3D printing technology in comparison with conventional titanium implants. MATERIAL AND METHODS: Two novel titanium implants based on 3D printing were tested in the mandible of eight Beagle dogs. As a control, two different commercially available titanium implants were used. The implants were staged to accommodate healing periods of 2 and 6 weeks. The primary outcome variable was bone-to-implant contact (BIC) in non-decalcified tissue sections and micro-CT analysis. RESULTS: Histomorphometrically, the proportions of tissues adjacent to the implant surfaces were similar for all implants, whereas the BIC percentage of new mineralized bone was greater for the control implants after both 2 and 6 weeks (p < .05). Micro-CT analysis revealed increasing osseous volume and BIC from 2 to 6 weeks. In contrast to the histomorphometry, the BIC evaluation with the micro-CT data revealed a significantly higher BIC for the two test implants compared with controls (p < .001). The analysis of the total implant surface area disclosed a value that was approximately double as high for the test compared to the control implants. CONCLUSIONS: The novel titanium implant system based on 3D printing yielded values for osseointegration that were adequate and satisfactory. The higher percentage of new mineralized bone in the control implants is explained by the fact of a completely different three-dimensional surface area.

Clinical and histologic evaluation of heterotopic mucosa transpositioning at teeth and dental implants.

AIM: To investigate the healing after heterotopic mucosa transpositioning at dental implants and teeth. MATERIALS AND METHODS: One hemimandible per dog (n = 4) was allocated to receive 3 implants (test), whereby 3 premolars on the contralateral side served as controls. After osseointegration, a Z-plasty was performed on the buccal aspect of the test and control sites to heterotopically move the zone of keratinized tissue (KT) into a region with non-keratinized tissue (nKT) and vice versa. Clinical measurements were performed before (T0) and at 12 weeks following heterotopic transposition (T1). Thereafter, specimens were processed for histological analysis. RESULTS: Clinical measurements revealed that at T1, a band of KT was reestablished at teeth (mean: 2.944 ± 1.866 mm), whereas at implants, the transpositioned nKT resulted in a mucosa without any signs of keratinization (mean: 0 mm; p < .0001). At implant sites, the probing attachment level loss was more pronounced compared to tooth sites (-1.667 ± 1.195 mm and -1.028 ± 0.878 mm, respectively; p = .0076). Histologically, the transpositioned nKT, was accompanied by the formation of KT at the tooth but not at implant sites. The supracrestal soft tissues were statistically significantly higher at tooth compared to implant sites (2.978 ± 0.483 mm and 2.497 ± 0.455 mm, p = .0083). The transpositioned KT remained mostly unaltered in its morphological characteristics. CONCLUSIONS: The findings of this study indicate that: (a) transpositioned KT may retain its morphological characteristics; and (b) transpositioned nKM was accompanied by the formation of KT at the tooth but not at implant sites.

Histological evaluation following treatment of recession-type defects with coronally advanced flap and a novel human recombinant amelogenin.

OBJECTIVES: To histologically evaluate the effects of a novel human recombinant amelogenin (rAmelX) on periodontal wound healing / regeneration in recession-type defects. MATERIALS AND METHODS: A total of 17 gingival recession-type defects were surgically created in the maxilla of three minipigs. The defects were randomly treated with a coronally advanced flap (CAF) and either rAmelX (test), or a CAF and placebo (control). At three months following reconstructive surgery, the animals were euthanized, and the healing outcomes histologically evaluated. RESULTS: The test group yielded statistically significantly (p = 0.047) greater formation of cementum with inserting collagen fibers compared with the control group (i.e., 4.38 mm ± 0.36 mm vs. 3.48 mm ± 1.13 mm). Bone formation measured 2.15 mm ± 0.8 mm in the test group and 2.24 mm ± 1.23 mm in the control group, respectively, without a statistically significant difference (p = 0.94). CONCLUSIONS: The present data have provided for the first-time evidence for the potential of rAmelX to promote regeneration of periodontal ligament and root cementum in recession-type defects, thus warranting further preclinical and clinical testing. CLINICAL RELEVANCE: The present results set the basis for the potential clinical application of rAmelX in reconstructive periodontal surgery.

The effect of connective tissue graft or a collagen matrix on epithelial differentiation around teeth and implants: a preclinical study in minipigs.

OBJECTIVES: This study aimed to histologically evaluate the healing at 8 weeks after coronally advanced flap (CAF) with either a superficial (SCTG) or deep palatal connective tissue graft (DCTG), or a collagen matrix (CM) to cover recession defects at teeth and implants. MATERIAL AND METHODS: One mandibular side of 6 miniature pigs received each 3 titanium implants 12 weeks after extraction. Eight weeks later, recession defects were created around implants and contralateral premolars and 4 weeks later randomly subjected to CAF + SCTG, CAF + DCTG, or CAF + CM. After 8 weeks, block biopsies were histologically analyzed. RESULTS: For the primary outcome, i.e., keratinization of the epithelium, all teeth and implants exhibited a keratinized epithelium with no histological differences among them also not in terms of statistically significant differences in length (SCTG 0.86 ± 0.92 mm, DCTG 1.13 ± 0.62 mm, and Cm, 1.44 ± 0.76 mm). Pocket formation was histologically seen at all teeth, around most implants with SCTG and DCTG, however not in the CM implant group. The connective tissue grafts showed hardly signs of degradation, whereas the CM was partly degraded and integrated in connective tissue. The mean gain in gingival height was similar in all experimental groups (SCTG 3.89 ± 0.80 mm, DCTG 4.01 ± 1.40 mm, CM 4.21 ± 0.64 mm). Statistically significant differences were found in the height of the junctional epithelium between the control teeth and the connective tissue groups (p = 0.009 and 0.044). CONCLUSIONS: In this animal model, the use of either a superficial or deep connective tissue graft or a collagen membrane did not seem to have any impact on the epithelial keratinization around both teeth and implants. All procedures (CAF + SCTG/DCTG/CM) resulted in a long JE that was even longer at implants. CLINICAL RELEVANCE: Deep/superficial palatal connective tissue graft yielded similar keratinization around teeth/implants. Given the absence of pocket formation and inflammatory processes at implants when using a CM, CAF + CM might bear potential clinical benefits.

Benchmark performance of anodized vs. sandblasted implant surfaces in an acute dehiscence type defect animal model.

OBJECTIVES: Crestal bone formation represents a crucial aspect of the esthetic and biological success of dental implants. This controlled preclinical study analyzed the effect of implant surface and implant geometry on de novo crestal bone formation and osseointegration. MATERIALS AND METHODS: Histological and histomorphometrical analysis was performed to compare three implant groups, that is, (1) a novel, commercially available, gradient anodized implant, (2) a custom-made geometric replica of implant "1," displaying a superhydrophilic micro-rough large-grit sandblasted and acid-etched surface, and (3) a commercially available implant, having the same surface as "2" but a different implant geometry. The study applied a standardized buccal acute-type dehiscence model in minipigs with observation periods of 2 and 8 weeks of healing. RESULTS: The amount of newly formed crestal bone (BATA) around control groups (2) and (3) was significantly increased when compared to the test group (1) at the 8 weeks of healing time point. Similar results were obtained for all parameters related to osseointegration and direct bone apposition, to the implant surface (dBIC, VBC, and fBIC), demonstrating superior osseointegration of the moderately rough, compared to the gradient anodized functionalization. After 2 weeks, the osseointegration (nBIC) was found to be influenced by implant geometry with group (3) outperforming groups (1) and (2) on this parameter. At 8 weeks, nBIC was significantly higher for groups (2) and (3) compared to (1). CONCLUSIONS: The extent (BATA) of de novo crestal bone formation in the acute-type dehiscence defects was primarily influenced by implant surface characteristics and their ability to promote osseointegration and direct bone apposition. Osseointegration (nBIC) of the apical part was found to be influenced by a combination of surface characteristics and implant geometry. For early healing, implant geometry may have a more pronounced effect on facilitating osseointegration, relative to the specific surface characteristics.

Evidence of re-osseointegration after electrolytic cleaning and regenerative therapy of peri-implantitis in humans: a case report with four implants.

OBJECTIVE: To evaluate re-osseointegration after electrolytic cleaning and regenerative therapy of dental implants with peri-implantitis in humans. MATERIAL AND METHODS: Four dental implants that developed peri-implantitis underwent electrolytic cleaning followed by regenerative therapy with guided bone regeneration. All four implants developed recurrent peri-implantitis and were therefore explanted 6 to 13 months later. Radiographic bone level, probing depth, and bleeding on probing were determined at the time of surgery, 6 months later, and before implant retrieval. The peri-implant tissues were histologically and histomorphometrically analyzed. RESULTS: All four implants demonstrated radiographic and histological bone gain, reduced probing depth, and bleeding on probing. Radiographic bone gain was 5.8 mm mesially and 4.8 mm distally for implant #1, 3.3 mm and 2.3 mm for implant #2, 3.1 mm and 0.5 mm for implant #3, and 3.5 mm and 2.8 mm for implant #4. The histometric mean and maximum vertical bone gain for implant #1 to #4 was 1.65 mm and 2.54 mm, 3.04 mm and 3.47 mm, 0.43 mm and 1.27 mm, and 4.16 mm and 5.22 mm, respectively. The percentage of re-osseointegration for implant #1 to #4 was 21.0%, 36.9%, 5.7%, and 39.0%, respectively. In one implant, the newly formed bone was deposited directly onto calculus on the implant surface. CONCLUSIONS: We found that (1) re-osseointegration is possible on a formerly contaminated implant surface and (2) the electrolytic cleaning process seems to be effective enough at sites with calculus residues. CLINICAL RELEVANCE: Since re-osseointegration can be achieved by electrolytic cleaning, this decontamination technique may be considered as a future treatment concept.

Cross-linked hyaluronic acid slows down collagen membrane resorption in diabetic rats through reducing the number of macrophages.

OBJECTIVES: We previously showed that accelerated degradation of collagen membranes (CMs) in diabetic rats is associated with increased infiltration of macrophages and blood vessels. Since pre-implantation immersion of CMs in cross-linked high molecular weight hyaluronic acid (CLHA) delays membrane degradation, we evaluated here its effect on the number of macrophages and endothelial cells (ECs) within the CM as a possible mechanism for inhibition of CM resorption. MATERIALS AND METHODS: Diabetes was induced with streptozotocin in 16 rats, while 16 healthy rats served as control. CM discs were labeled with biotin, soaked in CLHA or PBS, and implanted under the scalp. Fourteen days later, CMs were embedded in paraffin and the number of macrophages and ECs within the CMs was determined using antibodies against CD68 and transglutaminase II, respectively. RESULTS: Diabetes increased the number of macrophages and ECs within the CMs (∼2.5-fold and fourfold, respectively). Immersion of CMs in CLHA statistically significantly reduced the number of macrophages (p < 0.0001) in diabetic rats, but not that of ECs. In the healthy group, CLHA had no significant effect on the number of either cells. Higher residual collagen area and membrane thickness in CLHA-treated CMs in diabetic animals were significantly correlated with reduced number of macrophages but not ECs. CONCLUSIONS: Immersion of CM in CLHA inhibits macrophage infiltration and reduces CM degradation in diabetic animals. CLINICAL RELEVANCE: The combination of CLHA and CM may represent a valuable approach when guided tissue regeneration or guided bone regeneration procedures are performed in diabetic patients.

Pre-clinical evaluation of the effect of a volume-stable collagen matrix on periodontal regeneration in two-wall intrabony defects.

AIM: To histologically evaluate the effect of a new collagen matrix on periodontal regeneration. MATERIALS AND METHODS: Two-wall intrabony defects were surgically created bilaterally distally to the maxillary first and third pre-molars in beagle dogs. The defects were randomly allocated to open flap debridement either with (test) or without (control) a volume-stable collagen matrix (VCMX). After 12 weeks, the dogs were euthanized, and the specimens histologically processed. Descriptive, histomorphometrical (vertical gain of periodontal tissues) and statistical analyses were then performed. RESULTS: Healing was uneventful in most cases. Residual VCMX was still present and showed integration into new bone, new periodontal ligament, connective tissue and, in some specimens, into new cementum. Periodontal regeneration occurred to a varying extent in both groups. New continuous cementum and new bone formation were statistically significantly greater in the test group (4.12 mm and 3.28 mm, respectively) than in the control group (1.54 mm and 2.47 mm, respectively) (p = .009 and p = .037, respectively). The junctional epithelium was longer in the control group (2.21 mm) than in the test group (1.49 mm, p = .16). CONCLUSION: The present results have for the first time provided histologic evidence for the potential of this novel VCMX to facilitate periodontal regeneration thus warranting further pre-clinical and clinical testing.

Immunohistochemical Evaluation of Periodontal Regeneration Using a Porous Collagen Scaffold.

(1) Aim: To immunohistochemically evaluate the effect of a volume-stable collagen scaffold (VCMX) on periodontal regeneration. (2) Methods: In eight beagle dogs, acute two-wall intrabony defects were treated with open flap debridement either with VCMX (test) or without (control). After 12 weeks, eight defects out of four animals were processed for paraffin histology and immunohistochemistry. (3) Results: All defects (four test + four control) revealed periodontal regeneration with cementum and bone formation. VCMX remnants were integrated in bone, periodontal ligament (PDL), and cementum. No differences in immunohistochemical labeling patterns were observed between test and control sites. New bone and cementum were labeled for bone sialoprotein, while the regenerated PDL was labeled for periostin and collagen type 1. Cytokeratin-positive epithelial cell rests of Malassez were detected in 50% of the defects. The regenerated PDL demonstrated a larger blood vessel area at the test (14.48% ± 3.52%) than at control sites (8.04% ± 1.85%, p = 0.0007). The number of blood vessels was higher in the regenerated PDL (test + control) compared to the pristine one (p = 0.012). The cell proliferative index was not statistically significantly different in pristine and regenerated PDL. (4) Conclusions: The data suggest a positive effect of VCMX on angiogenesis and an equally high cell turnover in the regenerated and pristine PDL. This VCMX supported periodontal regeneration in intrabony defects.

Horizontal bone grafting using equine-derived cancellous bone blocks is associated with severe complications: A prospective clinical and histological pilot study.

AIMS: The aim of this prospective, clinical study was to evaluate the clinical performance and histological outcome of a new equine hydroxyapatite collagenated bone block (eHAC) for horizontal bone grafting prior to implant placement. MATERIALS AND METHODS: Five patients (two male/three female) with a mean age of 51.6 years (range 22-66 years) and a reduced horizontal bone width of the alveolar ridge (mean 3.5 mm) underwent horizontal bone grafting using eHAC at 10 grafting sites. Reentry was performed 6.9 months after the horizontal grafting procedure. Clinical follow-up (mean 28.9 month) considered width gain of the alveolar ridge, soft tissue healing, and complications. To evaluate graft incorporation, four additional patients underwent histological assessment of equine blocks adjacent to autologous blocks 3 and 6 months after grafting. RESULTS: The study was terminated after graft failure was observed in four of five patients. Mean horizontal bone width had increased by 3.6 ± 1.22 mm. Three out of nine implants placed had to be removed due to graft failure. Histological evaluation revealed large amounts of soft connective tissue within the grafts (mean 67.3 ± 9.5%). The proportion of new bone formation 3 months after the lateral grafting procedure revealed an average of 8.6%, compared to 11.4% after 6 to 7 months. CONCLUSION: Lateral ridge grafting using eHAC achieved measurable horizontal width gain but revealed high rates of severe complications. CLINICAL IMPLICATIONS: Within the limitations of this study, eHAC bone blocks cannot be recommended for horizontal bone grafting.

Crestal bone response to loaded zirconia and titanium implants: a radiographic and histometric analysis in canines.

OBJECTIVES: To evaluate the crestal bone response to a two-piece zirconia implant compared with a control titanium implant using periapical radiographs (PAs) and histometry. MATERIALS AND METHODS: Thirty zirconia and 30 titanium implants were placed in healed posterior mandibles of five canines. Full-ceramic single-tooth restorations were cemented after 6 weeks of healing. Three observers measured the distance between the implant shoulder and the crestal bone (DIB) at placement, loading, and harvesting after 4 or 16 weeks in function. The influence of implant material and loading time on DIB as well as the inter-observer agreement were analyzed. Additionally, histometric distance between implant shoulder and most coronal bone-to-implant contact (IS-cBIC) was compared with DIB. RESULTS: Mean DIB values increased between 4 and 16 weeks of loading for both zirconia (from 1.66 to 2.25 mm; P < 0.0001) and titanium (from 1.81 to 1.95 mm; P = 0.06). Zirconia yielded mean IS-cBIC values of 2.18 mm and 2.48 mm (P < 0.001) and titanium 2.23 mm and 2.34 mm (P = 0.27) after 4 and 16 weeks, respectively. The raters reached an excellent intraclass correlation coefficient. PAs underestimated the bone loss on average by 0.39 mm. CONCLUSIONS: Zirconia implants showed a greater increase of DIB during early healing and function than titanium. CLINICAL RELEVANCE: Crestal peri-implant tissue dimensions may show more pronounced changes around two-piece zirconia implants during early healing. PAs may underestimate peri-implant bone loss.

Hyaluronic acid slows down collagen membrane degradation in uncontrolled diabetic rats.

AIM: To examine the in vitro biokinetics of hyaluronic acid (HA) from a collagen membrane (CM) and to evaluate the in vivo effect of immersion of the CM in HA solution on its degradation in streptozotocin (STZ)-induced diabetes conditions in a rat calvaria subcutaneous model. BACKGROUND: CM degradation is accelerated in uncontrolled diabetic rats. Immersion of CM in HA has been suggested to decrease their resorption rate without interfering with their tissue integration and structural degradation. However, it is unknown to what extent CM degradation may be influenced by its immersion in HA solution under a condition mimicking a medically compromised situation with an increased inflammatory level such as diabetes. MATERIALS AND METHODS: CMs were soaked in cross-linked HA. Protein adsorption and the HA release were quantified by ELISA. Diabetes was induced in sixteen rats, while 16 healthy rats served as control. CM was prepared and labeled prior to implantation with Biotin. Seventeen CM were immersed in HA and 17 CM in PBS. In each animal, one test or one control disk was implanted. In order to compare the collagen content, two similar non-implanted CM were used as baseline. Fourteen days after surgery, thirty-two animals were sacrificed. The entire calvaria including the skin above, was chemically fixed, decalcified, and embedded in paraffin. Five-µm-thick sections were analyzed histologically and histomorphometrically using H&E and avidin-peroxidase staining. RESULTS: The in vitro results demonstrated that the CM adsorbed roughly 80% of the total HA content. After 10 days, 36.3% of the initial HA remained on the CM. The in vivo results demonstrated that diabetes significantly reduced the thickness of the CM, while HA had a significant effect on keeping the membrane thickness. HA increased the residual collagen content in the diabetic group (P < 0.0001) but no such effect was observed in the healthy group. CONCLUSION: Immersion of CM in HA prior to the implantation delays membrane degradation in uncontrolled diabetic compared with normoglycemic rats.

Self-regenerative capacity of intra-oral bone defects.

OBJECTIVE: To provide an overview on the self-regenerative capacity of various types of intra-oral bone defects. MATERIALS AND METHODS: This paper has narratively reviewed the most important aspects of bone biology and the healing outcomes related to the self-regenerative capacity (i.e. without the placement of any biomaterial) of bone defects that occur following tooth extraction, autogenous graft harvesting, periapical lesions, cystic lesions of the jaws, third molar extraction and experimentally created ridge defects. RESULTS: In animals (i.e. dogs and monkeys), the greatest changes in horizontal and vertical dimension occur during the first 6 months following tooth extraction. In humans, bone remodelling may take from several months to years and exhibits marked inter-individual variability. Following tooth extraction at compromised sites (e.g. presence of severe bone loss at the time-point of extraction), the healing may occur slower and a substantial volume reduction can be expected than following tooth extraction at non-compromised sites. In the mandibular symphysis and ramus, the bone defects resulting following bone block harvesting are gradually healing to a large extent, but complete healing appears not to occur due to poorer space provision and wound stability capacities. Defects after peri-apical surgery display a substantial self-regenerative capacity and heal at a great extent without the use of any adjunct measures. The vast majority of jawbone defects after cystectomy heal at a great extent and without apparent influence in the shape of the jaw, without the need of adjunct measures. After surgical removal of mandibular third molars, bone fill can be observed over a period of at least 12 months, with the most substantial change (e.g. the greatest bone fill) occurring during the first 3 months after surgery. However, complete fill of these residual bone defects does not always occur. CONCLUSIONS: Intra-oral bone defects possess a high self-regenerative capacity. Factors such as extent of bone loss, presence of bony walls, closed healing environment, space provision and mechanical wound stability substantially influence healing/regeneration.

Excessive occlusal load on chemically modified and moderately rough titanium implants restored with cantilever reconstructions. An experimental study in dogs.

OBJECTIVE: To evaluate the outcomes of excessively loaded implants. MATERIAL AND METHODS: In five dogs, all mandibular premolars were extracted. After 3 months, six implants (three SLA® and three SLActive®) were placed (S). After 4 weeks, implants were restored: one single crown with stable occlusal contacts (SC), one crown and a cantilever unit with excessive occlusal contacts (OL), and a non-loaded implant (NL). Bleeding-on-probing (BoP), attachment level (AL), mucosal margin (GM) were assessed. Resonance frequency analysis (RFA) was assessed weekly. Standardized X-rays were taken at S, 4 and 24 weeks. RESULTS: Similar findings were observed for SLA® and SLActive® implants regarding PlI, GI, GM, AL, and BL. No significant differences were detected between baseline and 24-weeks or between treatment modalities for all clinical parameters (p > .05). Six months after loading, RFA values were significantly greater than at implant placement. No significant differences between treatment modalities were found. Linear radiographic measurements yielded similar results between SLA® and SLActive® implants. SLA® OL implants yielded a statistically significant gain on peri-implant bone density over all other groups (p = .012). Radiographic results were confirmed by descriptive histology. Technically, loosened occlusal screws occurred in 13.3% (SC = 3.3%; OL = 10%), while abutment fractures totalized 23.3% (SC = 6.6%; OL = 16.6%). CONCLUSIONS: Excessive occlusal load applied to implants (SLA® or SLActive®) restored with cantilevers did not cause loss of osseointegration or significant changes in their clinical, radiographic, or histologic outcomes. Early excessive occlusal load on SLA® implants promoted a gain in peri-implant bone density. Excessively loaded implants showed more technical complications.

Soft tissue response to dental implant closure caps made of either polyetheretherketone (PEEK) or titanium.

OBJECTIVE: Polyetheretherketone (PEEK) is a popular synthetic thermoplastic polymer for medical applications, but its clinical use suffers from several limitations. Therefore, the aim was to compare the soft tissue response to dental implant closure caps made of PEEK or titanium as evaluated by the occurrence of multinucleated giant cells (MNGCs). MATERIAL AND METHODS: Forty-two implants were placed in the maxilla of seven miniature pigs. While commercially pure titanium (Ti) implants had a Ti closure cap, ceramic implants made of either zirconia (Zr) or alumina-toughened zirconia (Zr + Al) received a PEEK closure cap. Histomorphometry was performed to evaluate the number of small and large MNGCs being in contact with the PEEK or the Ti in different compartments of the implant systems. RESULTS: No histological signs of inflammation were noticed, and MNGCs were observed on both PEEK and Ti closure caps and on all three implant types. Significantly higher numbers of MNGCs were found on closure caps made of PEEK than on closure caps made of Ti on the external closure cap surface facing both soft (p = 0.0008 for PEEK on Zr and p = 0.0016 for PEEK on Zr + Al) and hard tissues (p = 0.016 for PEEK on Zr and p = 0.003 for PEEK on Zr + Al) as well as in the internal closure cap surface (p = 0.014 for PEEK on Zr and p = 0.0088 for PEEK on Zr + Al). No statistically significant differences in the number of MNGCs were observed on the three implant types. CONCLUSIONS: Significantly more MNGCs were in contact with PEEK than with Ti closure caps.