RESUMO
The scaffold pore size influences many critical physical aspects of tissue engineering, including tissue infiltration, biodegradation rate, and mechanical properties. Manual measurements of pore sizes from scanning electron micrographs using ImageJ/FIJI are commonly used to characterize scaffolds, but these methods are both time-consuming and subject to user bias. Current semi-automated analysis tools are limited by a lack of accessibility or limited sample size in their verification process. The work here describes the development of a new MATLAB algorithm, PoreScript, to address these limitations. The algorithm was verified using three common scaffold fabrication methods (e.g., salt leaching, gas foaming, emulsion templating) with varying pore sizes and shapes to demonstrate the versatility of this new tool. Our results demonstrate that the pore size characterization using PoreScript is comparable to manual pore size measurements. The PoreScript algorithm was further evaluated to determine the effect of user-input and image parameters (relative image magnification, pixel intensity threshold, and pore structure). Overall, this work validates the accuracy of the PoreScript algorithm across several fabrication methods and provides user-guidance for semi-automated image analysis and increased throughput of scaffold characterization.
RESUMO
Polymerization of high internal phase emulsions (polyHIPEs) is a well-established method for the production of high porosity foams. Researchers are often regulated to using a time-intensive trial and error approach to achieve target pore architectures. In this work, we performed a systematic study to identify the relative effects of common emulsion parameters on pore architecture (mixing speed, surfactant concentration, organic phase viscosity, molecular hydrophobicity). Across different macromer chemistries, the largest magnitude of change in pore size was observed across surfactant concentration (~6 fold, 5-20 wt%), whereas changing mixing speeds (~4 fold, 500-2000 RPM) displayed a reduced effect. Furthermore, it was observed that organic phase viscosity had a marked effect on pore size (~4 fold, 6-170 cP) with no clear trend observed with molecular hydrophobicity in this range (logP = 1.9-4.4). The efficacy of 1,4-butanedithiol as a reactive diluent was demonstrated and provides a means to reduce organic phase viscosity and increase pore size without affecting polymer fraction of the resulting foam. Overall, this systematic study of the microarchitectural effects of these macromers and processing variables provides a framework for the rational design of polyHIPE architectures that can be used to accelerate design and meet application needs across many sectors.