RESUMO
We present an in-depth analysis of the surface band alignment and local potential distribution of InP nanowires containing a p-n junction using scanning probe and photoelectron microscopy techniques. The depletion region is localized to a 15 nm thin surface region by scanning tunneling spectroscopy and an electronic shift of up to 0.5 eV between the n- and p-doped nanowire segments was observed and confirmed by Kelvin probe force microscopy. Scanning photoelectron microscopy then allowed us to measure the intrinsic chemical shift of the In 3d, In 4d, and P 2p core level spectra along the nanowire and the effect of operating the nanowire diode in forward and reverse bias on these shifts. Thanks to the high-resolution techniques utilized, we observe fluctuations in the potential and chemical energy of the surface along the nanowire in great detail, exposing the sensitive nature of nanodevices to small scale structural variations.
RESUMO
III-nitrides are considered the material of choice for light-emitting diodes (LEDs) and lasers in the visible to ultraviolet spectral range. The development is hampered by lattice and thermal mismatch between the nitride layers and the growth substrate leading to high dislocation densities. In order to overcome the issue, efforts have gone into selected area growth of nanowires (NWs), using their small footprint in the substrate to grow virtually dislocation-free material. Their geometry is defined by six tall side-facets and a pointed tip which limits the design of optoelectronic devices. Growth of dislocation-free and atomically smooth 3D hexagonal GaN micro-prisms with a flat, micrometer-sized top-surface is presented. These self-forming structures are suitable for optical devices such as low-loss optical cavities for high-efficiency LEDs. The structures are made by annealing GaN NWs with a thick radial shell, reforming them into hexagonal flat-top prisms with six equivalents either m- or s-facets depending on the initial heights of the top pyramid and m-facets of the NWs. This shape is kinetically controlled and the reformation can be explained with a phenomenological model based on Wulff construction that have been developed. It is expected that the results will inspire further research into micron-sized III-nitride-based devices.
RESUMO
In this work, we present a method to synthesize arrays of hexagonal InGaN submicrometer platelets with a top c-plane area having an extension of a few hundred nanometers by selective area metal-organic vapor-phase epitaxy. The InGaN platelets were made by in situ annealing of InGaN pyramids, whereby InGaN from the pyramid apex was thermally etched away, leaving a c-plane surface, while the inclined {101Ì 1} planes of the pyramids were intact. The as-formed c-planes, which are rough with islands of a few tens of nanometers, can be flattened with InGaN regrowth, showing single bilayer steps and high-quality optical properties (full width at half-maximum of photoluminescence at room temperature: 107 meV for In0.09Ga0.91N and 151 meV for In0.18Ga0.82N). Such platelets offer surfaces having relaxed lattice constants, thus enabling shifting the quantum well emission from blue (as when grown on GaN) to green and red. For single InGaN quantum wells grown on the c-plane of such InGaN platelets, a sharp interface between the quantum well and the barriers was observed. The emission energy from the quantum well, grown under the same conditions, was shifted from 2.17 eV on In0.09Ga0.91N platelets to 1.95 eV on In0.18Ga0.82N platelets as a result of a thicker quantum well and a reduced indium pulling effect on In0.18Ga0.82N platelets. On the basis of this method, prototype light-emitting diodes were demonstrated with green emission on In0.09Ga0.91N platelets and red emission on In0.18Ga0.82N platelets.
RESUMO
In this paper, we correlate the growth of InAs nanowires with the detailed interface trap density (Dit) profile of the vertical wrap-gated InAs/high-k nanowire semiconductor-dielectric gate stack. We also perform the first detailed characterization and optimization of the influence of the in situ doping supplied during the nanowire epitaxial growth on the sequential transistor gate stack quality. Results show that the intrinsic nanowire channels have a significant reduction in Dit as compared to planar references. It is also found that introducing tetraethyltin (TESn) doping during nanowire growth severely degrades the Dit profile. By adopting a high temperature, low V/III ratio tailored growth scheme, the influence of doping is minimized. Finally, characterization using a unique frequency behavior of the nanowire capacitance-voltage (C-V) characteristics reveals a change of the dopant incorporation mechanism as the growth condition is changed.
RESUMO
In this work, arrays of predominantly relaxed InGaN platelets with indium contents of up to 18%, free from dislocations and offering a smooth top c-plane, are presented. The InGaN platelets are grown by metal-organic vapor phase epitaxy on a dome-like InGaN surface formed by chemical mechanical polishing of InGaN pyramids defined by 6 equivalent {101Ì 1} planes. The dome-like surface is flattened during growth, through the formation of bunched steps, which are terminated when reaching the inclined {101Ì 1} planes. The continued growth takes place on the flattened top c-plane with single bilayer surface steps initiated at the six corners between the c-plane and the inclined {101Ì 1} planes, leading to the formation of high-quality InGaN layers. The top c-plane of the as-formed InGaN platelets can be used as a high-quality template for red micro light-emitting diodes.