Role of Nitrogen and Yttrium Contents in Manufacturing (Cr, Y)Nx Film Nanostructures.

The high-power impulse magnetron sputtering (HiPIMS) technique was applied to deposit multilayer-like (Cr, Y)Nx coatings on AISI 304L stainless steel, using pendular substrate oscillation and a Cr-Y target and varying the nitrogen flow rate from 10 to 50 sccm. The microstructure, mechanical and tribological properties were investigated by scanning and transmission electron microscopy, X-ray photoelectron spectroscopy, X-ray diffraction, instrumented nano-hardness, and wear tests. The columnar grain structure became highly segmented and nanosized due to pendular substrate oscillation and the addition of yttrium. The deposition rate increased continuously with the growing nitrogen flow rate. The increase in nitrogen flow from 10 to 50 sccm increased the hardness of the coatings (Cr, Y)Nx, with a maximum hardness value of 32.7 GPa for the coating (Cr, Y)Nx with a nitrogen flow of 50 sccm, which greatly surpasses the hardness of CrN films with multilayer-like (Cr, Y)Nx coatings architecture. The best mechanical and tribological performance was achieved for a nitrogen flow rate of 50 sccm. This was enabled by more elevated compressive stresses and impact energies of the impinging ions during film growth, owing to an increase of HiPIMS peak voltage with a rising N2/Ar ratio.

Development of Scheelite Tailings-Based Ceramic Formulations with the Potential to Manufacture Porcelain Tiles, Semi-Stoneware and Stoneware.

New ceramic formulations based on scheelite tailing were developed, and their potential in the ceramic industry was evaluated. Green bodies with different contents of scheelite tailing (0-8 wt%) were sintered (1150 °C, 1200 °C, and 1250 °C) and characterized in terms of the main mineralogical phases, microstructure, and physico-mechanical properties. The mullite was the main phase identified in all sintered temperatures. This result was also ratified with the aid of scanning electron microscope (SEM) images, in which small needles of the mullite were detected. The presence of mullite is required because it contributes to increasing the mechanical resistance of the material. The physico-mechanical properties measured (water absorption, linear shrinkage, apparent porosity, and flexural strength) were compared to the ISO 13006, and the samples sintered at 1150 °C presented potential to be used as semi-stoneware, while those sintered at 1200 °C and 1250 °C can be employed stoneware and porcelain tiles, respectively.