RESUMO
OBJECTIVE: This study evaluated the influence of Nd:YAG laser on the evaporation degree (ED) of the solvent components in total-etch and self-etch adhesives. MATERIALS AND METHODS: The ED of Gluma Comfort Bond (Heraeus-Kulzer) one-step self-etch adhesive, and Adper Single Bond 2 (3M ESPE), and XP Bond (Dentsply) total-etch adhesives was determined by weight alterations using two techniques: Control--spontaneous evaporation of the solvent for 5 min; Experimental--Nd:YAG laser irradiation for 1 min, followed by spontaneous evaporation for 4 min. The weight loss due to evaporation of the volatile components was measured at baseline and after 10 s, 20 s, 30 s, 40 s, 50 s, 60 s, 70 s, 80 s, 90 s, 100 s, 110 s, 2 min, 3 min, 4 min, and 5 min. RESULTS: Evaporation of solvent components significantly increased with Nd:YAG laser irradiation for all adhesives investigated. Gluma Comfort Bond showed significantly higher evaporation of solvent components than Adper Single Bond 2 and XP Bond. All the adhesives lost weight quickly during the first min of Nd:YAG laser irradiation. CONCLUSION: The application of Nd:YAG laser on adhesives before light curing had a significant effect on the evaporation of the solvent components, and the ED of Gluma Comfort Bond one-step self-etch adhesive was significantly higher than with Adper Single Bond 2 and XP Bond total-etch adhesives. CLINICAL RELEVANCE: The use of the Nd:YAG laser on the uncured adhesive technique can promote a greater ED of solvents, optimizing the longevity of the adhesive restorations.
Assuntos
Adesivos Dentinários/química , Lasers de Estado Sólido , Solventes/química , Cimentos Dentários/química , Cimentos Dentários/efeitos da radiação , Adesivos Dentinários/efeitos da radiação , Humanos , Umidade , Cura Luminosa de Adesivos Dentários/métodos , Teste de Materiais , Transição de Fase , Solventes/efeitos da radiação , Temperatura , Fatores de Tempo , VolatilizaçãoRESUMO
Teeth are constituted mainly of hydroxyapatite molecules (Ca(10)(PO(4))(6)(OH)(2)), grouped in different microstructural arrangements, depending on the dental layer considered (enamel or dentine). In the present work, these dental microstructural arrangements were characterized by atomic force microscopy. Enamel and dentine samples were cut from freshly extracted bovine incisor teeth. After metallographic polishing, the dental surfaces were etched with lactic acid (113.8 mmol/L, pH 3.3). Three etching times were tested: 1, 3 and 5 min. Atomic force micrographs showed that 1 min of etching time was effective to remove the smear layer, polishing debris and scratches, and display the characteristics of interest for both enamel and dentine. Although the bovine dental enamel rod cross-section presented keyhole-like shape, its measured dimensions (8.8 microm of major axis and 3.7 microm of minor axis) exhibited an insignificant discrepancy from human prisms diameters. Bovine dentinal tubules displayed larger mean diameters (4.0 microm) and a lower density (approximately 17,100 tubules/mm(2)) than human dentine, suggesting that the use of bovine dentine as a substitute for human dentine in resin adhesion investigations should be reconsidered. Apatite nanoparticles presented a mean radius (22-23 nm) considerably smaller than that of human teeth.
Assuntos
Esmalte Dentário/ultraestrutura , Dentina/ultraestrutura , Animais , Bovinos , Microscopia de Força AtômicaRESUMO
O propósito da presente pesquisa foi avaliar a rugosidade do esmalte dentário após microabrasäo, seguido de diferentes métodos de polimento. Foram selecionados 60 dentes humanos íntegros, que sofreram três avaliaçöes em rugosímetro Perthometer S8P (Pherten-Mahr, Germany). A primeira foi feita no esmalte íntegro. A segunda, após a microabrasäo, e a terceira avaliaçäo foi feita após os procedimentos de polimento. Os dados obtidos com as avaliaçöes foram analisados estatisticamente. De acordo com os resultados, verificou-se que: o ácido clorídrico a 18 por cento promove mais irregularidades na superfície dental; as técnicas de polimento promoveram alisamento semelhante para as duas concentraçöes ácidas, näo havendo diferença estatisticamente significante entre os métodos; os métodos de polimento empregados proporcionaram maior lisura da superfície do esmalte que em sua condiçäo original
Assuntos
Esmalte Dentário , Técnicas In Vitro , Microabrasão do Esmalte/métodos , Polimento Dentário/métodos , Ácido ClorídricoRESUMO
Foi realizado um estudo experimental no qual se avaliou a rugosidade superficial de três cimentos de ionômero de vidro após acabamento e polimento com dois sistemas diferentes de polimento, utilizando-se dois tipos de agentes lubrificantes. Os cimentos utilizados foram: Dyract (Dentsply), Vitremer (3M) e Vidrion R (S. S. White). Confeccionaram-se 20 corpos-de-prova (c.p.) de 9 mm de diâmetro e 3 mm de espessura com cada material a partir de tubetes anestésicos. Após uma semana de armazenamento em água a 37ºC, todas as amostras tiveram o mesmo acabamento, realizado com broca de 12 lâminas. O polimento foi realizado da seguinte forma: dos 20 c.p. de cada material, 10 foram polidos com discos Sof-Lex de granulaçäo fina e extrafina (3M), sendo cinco c.p., lubrificados com manteiga de cacau e cinco com ácido poliacrílico em gel; os demais c.p. foram polidos com pontas siliconadas verde e cinza (K. G. Sorensen), sendo cinco lubrificados com manteiga de cacau e cinco com ácido poliacrílico em gel. Mediu-se o parâmetro de rugosidade superficial Ra para todos os c.p., em rugosímetro Perthometer S8P, e, para cada um deles, efetuaram-se cinco mediçöes antes e cinco após o polimento, para efeito de amostragem estatística (600 mediçöes ao total). Aplicou-se aos dados obtidos o método estatístico da análise de variância (ANOVA) e o teste de Tukey, concluindo-se que, quanto ao material restaurador, o Dyract apresentou menor rugosidade se comparado ao Vidrion R e Vitremer; em relaçäo ao polimento, os discos Sof-Lex apresentaram resultados superiores às pontas de silicone e os agentes lubrificantes näo apresentaram diferença significante estatisticamente