Recycling of silicon from silicon cutting waste by Al-Si alloying in cryolite media and its mechanism analysis.

More than 40% of the crystalline silicon has been wasted as silicon cutting waste (SCW) during the wafer production process. This waste not only leads to resource wastage but also causes environmental burden. In this paper, SCW produced by the diamond-wire sawing process was recycled by Al-Si alloying process. Cryolite was introduced to the reaction system to dissolve the SiO2 layer existed on the surface of the Si particles in SCW. Alloys with 12.02 wt% of Si were prepared and the mechanism of the alloying process was investigated in detail. The Si-Al-cryolite system and SiO2-Al-cryolite system were studied individually to analyze the reaction process and transferring behavior of Si and SiO2 in SCW. The SiO2 shell was firstly transformed into Si-O-F ions. Then the Si-O-F ions diffused to the reaction interface by the effect of the concentration gradient and were reduced to Si by the aluminothermic reduction reaction: 4Al (l) + 3SiO2 (dissolved in the melt) = 3Si (Al)+ 2Al2O3 (dissolved in the melt). Then the internal Si particles were released into cryolite after the dissolution of SiO2 and transferred to the reaction interface by the effect of gravity. The influences of the mass ratio of Al/SCW and agitation modes on the Si content of the alloys and the Si recovery ratio in SCW were investigated. With the increase of the mass ratio of Al/SCW from 2.2 to 6.5, the Si recovery ratio in SCW increased from 44.08% to 69.05%, but the silicon content of the alloys decreased from 16.06 wt% to 8.83 wt%. Agitation can effectively improve the smelting effect during smelting by which the silicon content of the alloys and the Si recovery ratio in SCW increased from 12.02 wt% and 64.25% to 13.17 wt% and 69.46%, respectively.

Influencing factors and kinetics analysis on the leaching of iron from boron carbide waste-scrap with ultrasound-assisted method.

In this paper, the ultrasound-assisted leaching of iron from boron carbide waste-scrap was investigated and the optimization of different influencing factors had also been performed. The factors investigated were acid concentration, liquid-solid ratio, leaching temperature, ultrasonic power and frequency. The leaching of iron with conventional method at various temperatures was also performed. The results show the maximum iron leaching ratios are 87.4%, 94.5% for 80min-leaching with conventional method and 50min-leaching with ultrasound assistance, respectively. The leaching of waste-scrap with conventional method fits the chemical reaction-controlled model. The leaching with ultrasound assistance fits chemical reaction-controlled model, diffusion-controlled model for the first stage and second stage, respectively. The assistance of ultrasound can greatly improve the iron leaching ratio, accelerate the leaching rate, shorten leaching time and lower the residual iron, comparing with conventional method. The advantages of ultrasound-assisted leaching were also confirmed by the SEM-EDS analysis and elemental analysis of the raw material and leached solid samples.