Monolayer Doping of Germanium with Arsenic: A New Chemical Route to Achieve Optimal Dopant Activation.

Reported here is a new chemical route for the wet chemical functionalization of germanium (Ge), whereby arsanilic acid is covalently bound to a chlorine (Cl)-terminated surface. This new route is used to deliver high concentrations of arsenic (As) dopants to Ge, via monolayer doping (MLD). Doping, or the introduction of Group III or Group V impurity atoms into the crystal lattice of Group IV semiconductors, is essential to allow control over the electronic properties of the material to enable transistor devices to be switched on and off. MLD is a diffusion-based method for the introduction of these impurity atoms via surface-bound molecules, which offers a nondestructive alternative to ion implantation, the current industry doping standard, making it suitable for sub-10 nm structures. Ge, given its higher carrier mobilities, is a leading candidate to replace Si as the channel material in future devices. Combining the new chemical route with the existing MLD process yields active carrier concentrations of dopants (>1 × 1019 atoms/cm3) that rival those of ion implantation. It is shown that the dose of dopant delivered to Ge is also controllable by changing the size of the precursor molecule. X-ray photoelectron spectroscopy (XPS) data and density functional theory (DFT) calculations support the formation of a covalent bond between the arsanilic acid and the Cl-terminated Ge surface. Atomic force microscopy (AFM) indicates that the integrity of the surface is maintained throughout the chemical procedure, and electrochemical capacitance voltage (ECV) data shows a carrier concentration of 1.9 × 1019 atoms/cm3 corroborated by sheet resistance measurements.

Phosphorus monolayer doping (MLD) of silicon on insulator (SOI) substrates.

This paper details the application of phosphorus monolayer doping of silicon on insulator substrates. There have been no previous publications dedicated to the topic of MLD on SOI, which allows for the impact of reduced substrate dimensions to be probed. The doping was done through functionalization of the substrates with chemically bound allyldiphenylphosphine dopant molecules. Following functionalization, the samples were capped and annealed to enable the diffusion of dopant atoms into the substrate and their activation. Electrical and material characterisation was carried out to determine the impact of MLD on surface quality and activation results produced by the process. MLD has proven to be highly applicable to SOI substrates producing doping levels in excess of 1 × 1019 cm-3 with minimal impact on surface quality. Hall effect data proved that reducing SOI dimensions from 66 to 13 nm lead to an increase in carrier concentration values due to the reduced volume available to the dopant for diffusion. Dopant trapping was found at both Si-SiO2 interfaces and will be problematic when attempting to reach doping levels achieved by rival techniques.