RESUMO
OBJECTIVES: The aim of the present study was to compare the surface morphology alterations, mineral content, and surface roughness of eroded enamel surface versus eroded enamel surface which was preceded by Bioactive Glass 45S5 (BAG45S5) application in both primary and permanent human dentitions. MATERIALS AND METHODS: Fifty-two primary teeth and fifty-two permanent teeth were selected. Teeth were randomly divided into 4 groups of twenty-six teeth each. Groups A1 and B1 underwent erosion with 1% citric acid, while groups A2 and B2 were subjected to application of BAG45S5 powder followed by the same erosive conditions as A1 and B1. Measurements were performed by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and surface profilometry. They were used to examine the surface morphology alterations, mineral content, and surface roughness, respectively. RESULTS: SEM of enamel which received BAG45S5 showed smoother surface in primary teeth post erosion. EDX analysis showed that enamel exhibited crucial resistance to mineral loss in the group which received BAG45S5 prior to inducing erosion as compared to the induced erosion-only group. This was significant (p < 0.005) in both human dentitions. Erosion-only groups showed significantly less surface roughness in permanent teeth (p < 0.045). A marked decrease in surface roughness was observed in surfaces receiving BAG45S5, primary teeth (p < 0.001), and permanent teeth (p < 0.001). CONCLUSIONS: Bioactive Glass 45S5 proved successful against erosive conditions in both primary and permanent teeth with better performance in the permanent teeth so it can be regarded as a means of prevention. CLINICAL RELEVANCE: Bioactive Glass 45S5 powder could be used not only to remove stains but also as a prophylactic preventive measure against the multiple episodes of acidic food and beverage consumption in children.