RESUMO
OBJECTIVE: This scoping review aims to assess the influence of air abrasion with aluminum oxide and bioactive glass on dentin bond strength. MATERIALS AND METHODS: An electronic search was conducted in three databases (PubMed, Cochrane Library, and Embase), on March 3rd, 2023, with previously identified MeSH Terms. A total of 1023 records were screened. Exclusion criteria include primary teeth, air abrasion of a substrate other than sound dentin, use of particles apart from aluminum oxide or bioactive glass, and studies in which bond strength was not assessed. RESULTS: Out of the 1023 records, title and abstract screening resulted in the exclusion of 895 and 67 studies, respectively, while full-text analysis excluded another 25 articles. In addition, 5 records were not included, as full texts could not be obtained after requesting the authors. Two cross-references were added. Thus, 33 studies were included in this review. It is important to emphasize the absence of standardization of air abrasion parameters. According to 63.6% of the studies, air abrasion does not influence dentin bond strength. Moreover, 30.3% suggest improving bonding performance, and 6.1% advocate a decrease. CONCLUSIONS: Air abrasion with aluminum oxide does not enhance or impair dentin bond strength. The available data on bioactive glass are limited, which hinders conclusive insights. CLINICAL SIGNIFICANCE: Dentin air abrasion is a widely applied technique nowadays, with numerous clinical applications. Despite the widespread adoption of this procedure, its potential impact on bonding performance requires a thorough analysis of the existing literature.
Assuntos
Colagem Dentária , Dentina , Propriedades de Superfície , Dentina/efeitos dos fármacos , Colagem Dentária/métodos , Humanos , Abrasão Dental por Ar/métodos , Óxido de Alumínio/químicaRESUMO
OBJECTIVE: This article aims to showcase the implementation of a digital workflow in addressing a case of multifactorial excessive gingival display in a patient with high esthetic demands, incorporating both surgical and restorative interventions in a single session. CLINICAL CONSIDERATIONS: A 28-year-old female patient presented with excessive gingival display, attributed to a combination of short teeth due to altered passive eruption, lip hyperactivity, and a sub-nasal depression that lodged the upper lip during spontaneous smiling. The multidisciplinary treatment strategy encompassed surgical crown lengthening, the placement of a biovolume in the maxillary concavity, and the rehabilitation of the six anterior teeth with direct composite resin, all done in a single session. Smilecloud Biometrics was used to digitally plan the smile, and the final wax-up/mock-up was approved by the patient prior to any irreversible procedure. A digital planning center (GuiderLab) enabled the materialization of the virtual planning and the printing of the periodontal surgical guide, the biovolume, and the resin layering guides for the restorative technique. CONCLUSIONS: Adopting a digital workflow in multidisciplinary cases with excessive gingival display leads to predictable and more expedited outcomes, ensuring a favorable result between soft and hard tissues. CLINICAL SIGNIFICANCE: Excessive gingival display is a condition with multifactorial etiologies, including dentoalveolar, periodontal, skeletal, or muscular origins, or a combination of these factors. The diagnoses of altered passive eruption and a hypermobile upper lip are common in daily clinical practice and can be successfully managed through surgical crown lengthening and filling of the maxillary concavity, respectively. To achieve the desired outcome, restorative procedures often complement these surgical interventions.
RESUMO
OBJECTIVE: This review aims to assess structural, chemical, and mechanical properties of coronal dentin after endodontic irrigation. MATERIALS AND METHODS: Reporting followed the PRISMA extension for scoping reviews. An electronic search was carried out in PubMed, Embase, and Cochrane Library. Records filtered by language and published up to November 4, 2022 were independently screened by two researchers. Studies evaluating structural, chemical, or mechanical properties of human permanent coronal dentin after irrigation within the scope of nonsurgical root canal treatment were included. Data were extracted regarding study type, sample description and size, experimental groups, outcome, evaluation method, and main findings. RESULTS: From the initial 1916 studies, and by adding 2 cross-references, 11 in vitro studies were included. Seven studies provide ultrastructural and/or chemical characterization, and six assessed microhardness and/or flexural strength. One percent to 8% sodium hypochlorite (NaOCl) and 1%-17% ethylenediaminetetraacetic acid (EDTA) were the most commonly tested solutions, with contact times of 2-240 min (NaOCl) and 1-1440 min (EDTA) being evaluated. CONCLUSIONS: Overall, the literature is consensual regarding the inevitable impact of NaOCl and chelating agents on coronal dentin, with both deproteinizing and decalcifying effects being concentration- and time-dependent. The alteration of mechanical parameters further confirmed the surface and subsurface ultrastructural and chemical changes. CLINICAL SIGNIFICANCE: Endodontic treatment success highly depends on restorative sealing. Understanding the result of exposing coronal dentin, the main substrate for bonding, to irrigants' action is crucial. The deproteinizing and decalcifying effects of NaOCl and chelating agents are both concentration- and time-dependent, causing surface and subsurface ultrastructural, chemical, and mechanical alterations.
Assuntos
Cavidade Pulpar , Dentina , Humanos , Ácido Edético/análise , Ácido Edético/farmacologia , Dentina/química , Irrigantes do Canal Radicular/análise , Irrigantes do Canal Radicular/farmacologia , Quelantes/análise , Quelantes/farmacologiaRESUMO
OBJECTIVES: This study aimed to improve the performance and mode of administration of a glass-reinforced hydroxyapatite synthetic bone substitute, Bonelike by Biosckin® (BL®), by association with a dextrin-based hydrogel, DEXGEL, to achieve an injectable and moldable device named DEXGEL Bone. METHODS: Twelve participants requiring pre-molar tooth extraction and implant placement were enrolled in this study. BL® granules (250-500 µm) were administered to 6 randomized participants whereas the other 6 received DEXGEL Bone. After 6 months, a bone biopsy of the grafted area was collected for histological and histomorphometric evaluation, prior to implant placement. The performance of DEXGEL Bone and BL® treatments on alveolar preservation were further analyzed by computed tomography and Hounsfield density analysis. Primary implant stability was analyzed by implant stability coefficient technique. RESULTS: The healing of defects was free of any local or systemic complications. Both treatments showed good osseointegration with no signs of adverse reaction. DEXGEL Bone exhibited increased granule resorption (p = 0.029) accompanied by a tendency for more new bone ingrowth (although not statistically significant) compared to the BL® group. The addition of DEXGEL to BL® granules did not compromise bone volume or density, being even beneficial for implant primary stability (p = 0.017). CONCLUSIONS: The hydrogel-reinforced biomaterial exhibited an easier handling, a better defect filling, and benefits in implant stability. CLINICAL RELEVANCE: This study validates DEXGEL Bone safety and performance as an injectable carrier of granular bone substitutes for alveolar ridge preservation. TRIAL REGISTRATION: European Databank on Medical Devices (EUDAMED) No. CIV-PT-18-01-02,705; Registo Nacional de Estudos Clínicos, RNEC, No. 30122.
Assuntos
Perda do Osso Alveolar , Aumento do Rebordo Alveolar , Substitutos Ósseos , Humanos , Dextrinas , Alvéolo Dental/cirurgia , Hidrogéis , Osseointegração , Extração Dentária/efeitos adversos , Aumento do Rebordo Alveolar/métodos , Perda do Osso Alveolar/etiologiaRESUMO
OBJECTIVE: To evaluate the effect of rubber dam isolation on shear bond strength of two different adhesive systems to enamel. MATERIALS AND METHODS: The mesial, distal, lingual, and vestibular enamel surfaces of thirty human third molars were prepared (total n = 120). A custom splint was made to fit a volunteer's maxilla, holding the specimens in place in the oral cavity. Four composite resin cylinders were bonded to each tooth with one of two bonding agents (OptiBond FL and Prime&Bond active) with or without rubber dam isolation. Shear bond strength was tested in a universal testing machine and failure modes were assessed. Significance level for statistical analyses was set at 5%. RESULTS: All pairwise comparisons revealed statistical differences (p < 0.05). The highest mean shear bond strength values were obtained in rubber dam experimental groups, regardless of the adhesive system. Group OptiBond FL with rubber dam presented the highest mean bond strength values. Fracture modes for specimens bonded without rubber dam isolation were adhesive and cohesive within enamel, while rubber dam experimental groups revealed only cohesive fractures. CONCLUSIONS: Absolute isolation with rubber dam increases bond strength to enamel, independent of the adhesive system. The three-step total-etch system OptiBond FL provided significantly higher bond strength values than Prime&Bond active under both experimental conditions. CLINICAL SIGNIFICANCE: Rubber dam isolation has a significant effect on bond strengths to enamel, independent of the adhesive system. Its application is, therefore, advised whenever adhesive procedures are performed. A filled three-step etch-and-rinse adhesive performed superiorly, with or without rubber dam isolation, when bonding to enamel compared to an isopropanol-based universal adhesive.
Assuntos
Colagem Dentária , Humanos , Diques de Borracha , Cimentos de Resina/química , Resinas Compostas/química , Esmalte Dentário , Teste de Materiais , Adesivos Dentinários/químicaRESUMO
OBJECTIVE: This study aims to evaluate and compare the film thickness obtained with a resin cement and two composite resins, preheated and/or ultrasonically vibrated, as luting agents. MATERIALS AND METHODS: One hundred and twenty-six (126) pairs of resin discs were randomly assigned to six experimental groups (n = 21) according to luting agent (Variolink Esthetic LC, IPS Empress Direct or Estelite Omega) and cementation technique (preheating at 68°C and/or ultrasonic vibration). Specimens were luted by applying a controlled force. Following sectioning and film thickness measurement through field emission gun scanning electron microscopy, statistical analysis was carried out considering a 5% significance level. RESULTS: Statistically significant lower film thickness was observed in Variolink Esthetic LC group when compared to all composite resin groups (p < 0.001), except IPS Empress Direct preheated and ultrasonically vibrated group (p = 0.073). IPS Empress Direct with ultrasonic vibration yielded statistically lower film thickness values than Estelite Omega groups, regardless of luting technique (p < 0.05). Ultrasonically vibrated Estelite Omega groups showed statistically lower film thickness values than solely preheated groups (p < 0.05). CONCLUSIONS: Both Variolink Esthetic LC and IPS Empress Direct preheated and ultrasonically vibrated provided the lowest film thickness. The addition of ultrasonic vibration during cementation proved to be effective in reducing film thickness of both tested composite resins. CLINICAL SIGNIFICANCE: The cementation technique will have variable results depending on the luting material. Adhesive cementation protocols with composite resins should mainly consider ultrasonic vibration, but also preheating, as strategies for reducing film thickness. The tested resin cement, alongside with IPS Empress Direct composite resin preheated and ultrasonically vibrated, provided the lowest film thickness among the tested materials and techniques.
Assuntos
Colagem Dentária , Cimentos de Resina , Cimentação , Resinas Compostas , Colagem Dentária/métodos , Cimentos Dentários , Porcelana Dentária , Teste de Materiais , Propriedades de SuperfícieRESUMO
OBJECTIVES: The aim of this study was to evaluate the shear bond strength inherent to immediate and delayed definitive composite resin restorations, over three different biomaterials. METHODS: Fifty-four aluminum blocks were randomly assigned to six experimental groups (n = 9) according to the biomaterial (Biodentine, TotalFill BC Putty, or PCM) and restoration timing (immediate or 7 days delayed). Regarding the restorative procedures, a two-step self-etch bonding system (Clearfil SE Bond) was applied and subsequently restored using a flowable composite resin (SDR). After shear bond strength testing, fracture pattern analysis was performed. The significance level was set at α = 0.05. RESULTS: Within the immediate groups, Biodentine showed the highest mean shear bond strength value, with no statistically significant differences (P > 0.05) being detected when compared with both TotalFill (P = 0.072) and PCM (P = 0.232) groups. Regarding the delayed restoration groups, Biodentine and TotalFill presented the highest mean shear bond strength value, with statistical differences when compared with PCM (P = 0.002 and P = 0.043, respectively). No statistically significant differences (P > 0.05) were verified between both immediate and delayed groups for each tested biomaterial. Also, a statistically significant association was found between the fracture type and the biomaterial (P < 0.001). CONCLUSIONS AND CLINICAL RELEVANCE: Our findings suggest that all tested biomaterials present suitable alternatives which allow to perform restorative procedures immediately after pulp capping biomaterial placement (3 or 12 min, depending on the bioactive cement), therefore requiring one single appointment to complete the procedure. Biodentine and TotalFill BC Putty have shown superior shear bond strength results when compared with PCM, within a delayed timeframe (7 days).
Assuntos
Colagem Dentária , Cimentos Dentários , Compostos de Cálcio , Resinas Compostas , Análise do Estresse Dentário , Teste de Materiais , Cimentos de Resina , Resistência ao Cisalhamento , SilicatosRESUMO
Collagenated porcine-derived bone graft materials exhibit osteoconductive properties and the development of different formulations intends to enhance bone regeneration. This study aims to evaluate bone healing in a rabbit cancellous bone defect in response to grafting with different physicochemical forms of heterologous porcine bone. Twenty-six adult male New Zealand White rabbits received two critical size femoral bone defects per animal (n = 52), each randomly assigned to one of the five tested materials (Apatos, Gen-Os, mp3, Putty, and Gel 40). Animals were sacrificed at 15- and 30-days post-surgery. Qualitative and quantitative (new bone, particle and connective tissue percentages) histological analyses were performed. Histomorphometry showed statistically significant differences in all evaluated parameters between mp3 and both Putty and Gel 40 groups, regardless of the timepoint (p < 0.05). Moreover, statistical differences were observed between Apatos and both Putty (p = 0.014) and Gel 40 (p = 0.007) groups, at 30 days, in regard to particle percentage. Within each group, regarding new bone formation, mp3 showed significant differences (p = 0.028) between 15 (40.93 ± 3.49%) and 30 (52.49 ± 11.04%) days. Additionally, intragroup analysis concerning the percentage of particles revealed a significant reduction in particle occupied area from 15 to 30 days in mp3 and Gen-Os groups (p = 0.009). All mp3, Gen-Os and Apatos exhibited promising results in terms of new bone formation, thus presenting suitable alternatives to be used in bone regeneration.
Assuntos
Materiais Biocompatíveis/química , Substitutos Ósseos/química , Transplante Ósseo , Osso Esponjoso/cirurgia , Xenoenxertos/transplante , Osteogênese , Tíbia/cirurgia , Animais , Osso Esponjoso/citologia , Masculino , Coelhos , SuínosRESUMO
(1) Background: access cavity preparation is the first stage of non-surgical endodontic treatment. The inaccuracy of this step may lead to numerous intraoperative complications, which impair the root canal treatment's prognosis and therefore the tooth's survival. Guided endodontics, meaning computer-aided static (SN) and dynamic navigation (DN) techniques, has recently emerged as a new approach for root canal location in complex cases. This review aims to compare SN and DN guided endodontics' techniques in non-surgical endodontic treatment. (2) Methods: an electronic search was performed on PubMed, Scopus, and Cochrane Library databases until October 2021. Studies were restricted by language (English, Spanish and Portuguese) and year of publication (from 2011 to 2021). (3) Results: a total of 449, 168 and 32 articles were identified in PubMed, Scopus, and Cochrane Library databases, respectively, after the initial search. Of the 649 articles, 134 duplicates were discarded. In this case, 67 articles were selected after title and abstract screening, of which 60 were assessed for eligibility through full-text analysis, with one article being excluded. Four cross-references were added. Thus, 63 studies were included. (4) Conclusions: guided endodontics procedures present minimally invasive and accurate techniques which allow for highly predictable root canal location, greater tooth structure preservation and lower risk of iatrogenic damage, mainly when performed by less experienced operators. Both SN and DN approaches exhibit different advantages and disadvantages that make them useful in distinct clinical scenarios.
RESUMO
The aim of this study is to compare root-end preparation performed with two different ultrasonic tips-CVDentus and NSK-and respective time requirements. After root-end resection, 32 teeth were randomly divided in two groups, according to the ultrasonic tip used for root-end preparation. Preparation time was recorded. Photomicrographs were taken to assess the following parameters: root surface microcracking, marginal integrity and presence of debris. One ultrasonic tip from each group was analyzed through scanning electron microscopy before and after root-end preparation. The significance level was set at α = 0.05. Incidence of microcracks in both groups was 12.5%. Solely intracanal microcracking was found, consistently positioned within the widest side of the remaining dentine. No statistically significant differences were verified between both experimental groups regarding marginal integrity (p = 0.102) and preparation time (p = 0.780), whereas statistical differences (p = 0.003) were found concerning the presence of debris (the minimum registered score was mostly verified in CVDentus group). NSK tips showed major morphological changes, with extensive surface wear and noticeable loss of particles, which was not verified on CVDentus tips. Our findings suggest significant differences regarding root-end preparation walls quality, with CVDentus tips showing better results. Concerning microcracking, as well as preparation time and marginal integrity, both ultrasonic tips showed similar results. Qualitative analysis exposed NSK tips major morphological changes and wear after use, which was not verified on CVDentus tips.
RESUMO
AIM: The purpose of the present study is to assess the color stability of two calcium silicate-based cements (CSCs) used in regenerative endodontic procedures (REPs). METHODS: A total of 40 acrylic single-rooted transparent teeth, with immature apex, were used. Root canals were filled up to 3 mm below the level of the cementoenamel junction, with either saline solution (Mineral Trioxide Aggregate (MTA)/saline and Biodentine/saline) or blood (MTA/blood and Biodentine/blood). Subsequently, ProRoot MTA® or BiodentineTM was placed in the root canal to create a cervical barrier. Color measurement was carried out at four different evaluation periods (3 h, 72 h, 7 days, and 6 months). Shade analysis within the L* a* b* color space was performed and color variation (∆E) calculated. The significance level for statistical analysis was set at p < 0.05. RESULTS: The four groups showed a significant decrease in L* values over time. The ΔE value increased over time for all groups but was not statistically significant for the Biodentine/blood group. Two-way ANOVA showed no interaction between the CSC and treatment (contact with saline solution or blood). CSC used was the factor responsible for ΔE over time, inducing statistically significant color variations from T3H to T7D (p = 0.04) and T3H to T6M (p < 0.01). After 6 months, MTA/saline had 5.08 (p = 0.001) higher ΔE than Biodentine/Saline and the MTA/blood had 3.65 (p = 0.009) higher than Biodentine/blood. CONCLUSIONS: After 6 months, regardless of blood exposure, Biodentine exhibits superior color stability compared to MTA. Biodentine might be a suitable alternative to MTA as a cervical barrier material in REPs.
RESUMO
The purpose of the present study was to assess the proper time to perform a restoration (immediately or delayed) after placement of two calcium silicate-based cements (CSCs) and to test the performance of two different restorative protocols regarding shear bond strength (SBS). Seventy-five acrylic blocks were randomly divided into five groups (n = 15). Specimens were filled with either ProRoot MTA (Dentsply Tulsa Dental) or Biodentine (Septodont). The restoration was performed at an immediate (12 min) or delayed (seven days) timeframe, using a resin-based flowable composite (SDR) (bonded to the CSC using a universal bonding system) or glass ionomer cement (GIC) as restorative materials. SBS was measured using a universal testing machine. Fractured surfaces were evaluated, and the pattern was registered. Statistical analysis was performed using the Dunnâ»Sidak post hoc test (P < 0.05). Biodentine/immediate SDR showed the highest mean SBS value (4.44 MPa), with statistically significant differences when compared to mineral trioxide aggregate (MTA)/GIC (1.14 MPa) and MTA/immediate SDR (1.33 MPa). MTA/GIC and MTA/immediate SDR did not present significant differences regarding SBS. No statistical differences were verified concerning mean SBS between both CSCs within the 7 day groups. MTA/delayed SDR (3.86 MPa) presented statistical differences compared to MTA/immediate SDR, whereas no differences were observed regarding Biodentine performance (Biodentine/immediate SDR and Biodentine/delayed SDR (3.09 MPa)). Bonding procedures directly on top of MTA might be preferably performed at a delayed timeframe, whereas Biodentine might allow for immediate restoration.
RESUMO
Este estudo in vivo destinou-se a analisar as alterações histológicas que ocorrem na interface osso/implante durante o período crítico após a colocação em carga imediata. O modelo experimental foi desenvolvido na mandíbula de seis cães Beagle, tendo sido colocados dois implantes cilíndricos no terceiro e quarto quadrantes, respetivamente (n=24 implantes). Os implantes no quarto quadrante, em cada animal, foram reabilitados dentro do período de 24 horas, e o outro par, do terceiro quadrante, foi usado como controle, sem reabilitação. As eutanásias ocorreram aos nove, 17 e 31 dias após a colocação em carga, tendo sido preparadas amostras por técnicas não descalcificadas. A relação entre as medições do contato ósseo no terceiro e quarto quadrantes e as forças de mastigação foram analisadas estatisticamente no tempo de experimentação. O contato osso/implante foi ligeiramente maior, sem ser signifi cativo, nos implantes em carga imediata (52,13%), do que nos implantes dos quadrantes utilizados como controle (47,6%). O contato ósseo mostrou uma tendência para um valor menor no segundo grupo, aos 17 dias, e maior no primeiro grupo. Na comparação de contato osso/implante entre os quadrantes, apenas o terceiro grupo apresentou aumento do contato osso/implante no quarto quadrante. Em conclusão, verificamos a presença de atividade osteogênica em todas as interfaces osso/implante e a carga imediata não afetou a osseointegração...
This in vivo study aimed to analyse the histological changes that occur in the bone-implant interface during the critical period following immediate loading. The experimental model was developed in the mandible of six Beagle dogs, having been placed two cylindrical implants in the 3rd and 4th quadrants, respectively (n=24 implants). The 4th quadrant implants, in each animal, were rehabilitated within a period of 24 hours and the other pair, the 3rd quadrant ones, was used as a control without prosthetic rehabilitation. Animals were sacrificed at 9th, 17th and 31st days after loading and samples prepared using non-decalcified techniques. The relationship between bone contact measurement at the 3rd and 4th quadrants, as well as masticatory forces, was statistically analysed in the time of the experiment. The bone-implant contact was slightly higher, without statistical signifi cance, on the immediate loaded implant group (52.13%) than in the quadrants used as controls (47.6%). The bone contact showed a trend towards lower values in the 2nd group (17 days), and higher in the 1st group. When comparing bone-implant contact between quadrants, only the 3rd group showed increased bone-implant contact at the 4th quadrant. In conclusion we found the presence of osteogenic activity in all bone-implant interfaces and immediate loading did not affect osseointegration...