Investigation of Superconductivity in Ce-Doped (La,Pr)OBiS2 Single Crystals.

Single crystals of Ce-doped (La,Pr)OBiS2 superconductors, the multinary rare-earth elements substituted ROBiS2, were successfully grown. The grown crystals typically had a size of 1-2 mm and a plate-like shape with a well-developed c-plane. The c-axis lattice constants of the obtained (La,Ce,Pr)OBiS2 single crystals were approximately 13.6-13.7 Å, and the superconducting transition temperature was 1.23-2.18 K. Valence fluctuations of Ce and Pr were detected through X-ray absorption spectroscopy analysis. In contrast to (Ce,Pr)OBiS2 and (La,Ce)OBiS2, the superconducting transition temperature of (La,Ce,Pr)OBiS2 increased with the increasing concentrations of the tetravalent state at the R-site.

Growth and Characterization of ROBiS2 High-Entropy Superconducting Single Crystals.

A series of high-entropy superconductors, ROBiS2 (R = La + Ce + Pr + Nd + Sm), have been successfully grown in the form of single crystals using CsCl flux. The obtained single crystals have a platelike shape with a size of 0.5-2.0 mm and a thickness of 70-450 µm, and they are cleavable along the c-plane. The c-axis lattice constants of the obtained ROBiS2 single crystals have similar values of 13.47-13.57 Å. The Ce in the obtained ROBiS2 single crystals was in a mixed-valence state, comprising both Ce3+ and Ce4+. On the other hand, Pr and Sm showed only the trivalent state. The superconducting transition temperatures of ROBiS2 single crystals were approximately 2-4 K. The superconducting transition temperature and superconducting anisotropies of R-site mixed high-entropy samples increased with a decrease in the mean ionic radius of the R-site. Moreover, a deviation in the tendency to exhibit superconducting properties was observed based on the difference in the R-site mixed entropy. R-site mixed entropy in ROBiS2 superconductors may affect their superconducting properties.