Amplification of surface-initiated ring-opening metathesis polymerization of 5-(perfluoro-n-alkyl)norbornenes by macroinitiation.

This article reports the enhanced rate of the surface-initiated polymerization (SIP) of 5-(perfluoro-n-alkyl)norbornenes (NBFn) by combining two SIP techniques, namely surface-initiated atom-transfer polymerization (SI-ATRP) to grow a macroinitiator and surface-initiated ring-opening metathesis polymerization (SI-ROMP) to produce the final coating. This polymerization approach promotes the rapid growth of dense partially fluorinated coatings that are highly hydrophobic and oleophobic and yield thicknesses from 4-12 µm. Specifically, the growth rate and the limiting thickness of pNBFn with different side chain lengths (n = 4, 6, 8, and 10) at various monomer concentrations and temperatures are evaluated through two approaches: growing the polymer from an initiator-terminated monolayer (control) or from a modified poly(2-hydroxyethyl methacrylate) (PHEMA) macroinitiator. X-ray photoelectron spectroscopy (XPS) analysis shows that 38% of the hydroxyl termini in the macroinitiator react with a norbornenyl diacid chloride (NBDAC) molecule, and 7% of such anchored norbornenyl groups react with a catalyst molecule. The kinetic data have been modeled to determine the propagation velocity and the termination rate constant. The PHEMA macroinitiator provides thicker films and faster growth as compared to the monolayer, achieving a 12 µm thick coating of pNBF8 in 15 min. Increasing the monomer side chain length, n, from 4 to 10 improves the growth rate and the limiting polymer thickness. Performing the polymerization process at higher temperature increases the growth rate and the limiting thickness as evidenced by an increase in the film growth rate constant. Arrhenius plots show that the reactions involved in the macroinitiation process exhibit lower activation energies than those formed from a monolayer. Electrochemical impedance spectroscopy reveals that the films exhibit resistance against ion transport in excess of 1 × 10(10) Ω·cm(2).

Surface-initiated polymerization of superhydrophobic polymethylene.

We report a new surface-initiated polymerization strategy that yields superhydrophobic polymethylene (PM) films from initially smooth substrates of gold and silicon. The films are prepared by assembling a vinyl-terminated self-assembled monolayer, followed by exposure of the surface to a 0.1 M solution of borane, and polymerizing from the borane sites upon exposure to a solution of diazomethane at -17 degrees C. Surface-initiated polymethylenation (SIPM) presents rapid growth in relation to other surface-initiated reactions, producing PM films thicker than 500 nm after 2 min of reaction and 3 microm after 24 h of reaction. AFM and SEM images show the presence of micro- and nanoscale features that enable the entrapment of air when exposed to water. Consistent with this result, these films exhibit advancing water contact angles greater than 160 degrees, dramatically different than 103 degrees measured for smooth PM films, and hysteresis values ranging from 2 degrees to 40 degrees, depending on the substrate and polymerization time. The superhydrophobic character of the films results in the entrapment of air at the polymer/solution interface to provide remarkable resistances greater than 10(10) Omega x cm(2) against the transport of aqueous redox probes and cause the film to behave as a "perfect" capacitor.

Graphene: corrosion-inhibiting coating.

We report the use of atomically thin layers of graphene as a protective coating that inhibits corrosion of underlying metals. Here, we employ electrochemical methods to study the corrosion inhibition of copper and nickel by either growing graphene on these metals, or by mechanically transferring multilayer graphene onto them. Cyclic voltammetry measurements reveal that the graphene coating effectively suppresses metal oxidation and oxygen reduction. Electrochemical impedance spectroscopy measurements suggest that while graphene itself is not damaged, the metal under it is corroded at cracks in the graphene film. Finally, we use Tafel analysis to quantify the corrosion rates of samples with and without graphene coatings. These results indicate that copper films coated with graphene grown via chemical vapor deposition are corroded 7 times slower in an aerated Na(2)SO(4) solution as compared to the corrosion rate of bare copper. Tafel analysis reveals that nickel with a multilayer graphene film grown on it corrodes 20 times slower while nickel surfaces coated with four layers of mechanically transferred graphene corrode 4 times slower than bare nickel. These findings establish graphene as the thinnest known corrosion-protecting coating.

Transferable graphene oxide films with tunable microstructures.

This report describes methods to produce large-area films of graphene oxide from aqueous suspensions using electrophoretic deposition. By selecting the appropriate suspension pH and deposition voltage, films of the negatively charged graphene oxide sheets can be produced with either a smooth "rug" microstructure on the anode or a porous "brick" microstructure on the cathode. Cathodic deposition occurs in the low pH suspension with the application of a relatively high voltage, which facilitates a gradual change in the colloids' charge from negative to positive as they adsorb protons released by the electrolysis of water. The shift in the colloids' charge also gives rise to the brick microstructure, as the concurrent decrease in electrostatic repulsion between graphene oxide sheets results in the formation of multilayered aggregates (the "bricks"). Measurements of water contact angle revealed the brick films (79°) to be more hydrophobic than the rug films (41°), a difference we attribute primarily to the distinct microstructures. Finally, we describe a sacrificial layer technique to make these graphene oxide films free-standing, which would enable them to be placed on arbitrary substrates.