The crystal structure and magnetic properties of a new ferrimagnetic semiconductor: Ca21Mn4Sb18.

Single crystals of the new transition metal Zintl phase, Ca(21)Mn(4)Sb(18), were prepared by high temperature melt synthesis. The crystal structure was determined by single crystal X-ray diffraction to be monoclinic in the space group C2/c. Crystal information was obtained at 90 K, and unit cell parameters were determined (a = 17.100(2) A, b = 17.073(2) A, c = 16.857(2) A, beta = 92.999(2) degrees, Z = 2, R1 = 0.0540, wR2 = 0.1437). The structure can be described as containing 4 discreet units per formula unit: 1 linear [Mn(4)Sb(10)](22-) anion, 2 dumbbell-shaped [Sb(2)](4-) anions, 4 individual Sb(3-) anions, and 21 Ca(2+) cations. The [Mn(4)Sb(10)](22-) anion contains four edge-shared MnSb(4) tetrahedra with distances between Mn ions of 3.388(4) A, 2.782(4) A, and 2.760(4) A. Electron counting suggests that the Mn are 2+. Temperature dependent magnetization shows a ferromagnetic-like transition temperature at approximately 52 K which is suppressed with increasing magnetic field. The paramagnetic regime is best fit to a ferrimagnetic model, providing a total effective moment of 4.04(2) mu(B), significantly less than that expected for 4 Mn(2+) ions (11.8 mu(B)). Temperature dependent resistivity shows that this compound is a semiconductor with an activation energy of 0.159(2) eV (100-300 K).

XMCD characterization of the ferromagnetic state of Yb14MnSb11.

X-ray magnetic circular dichroism (XMCD) measurements on Yb14MnSb11 provide experimental evidence of a moment of 5 microB on Mn, with partial cancellation by an opposing moment on the Sb4 cage surrounding each Mn ion. The compound is isostructural to Ca14AlSb11, with Mn occupying the Al site in the AlSb4(9-) discrete tetrahedral, anionic unit. Bulk magnetization measurements indicate a saturation moment of 3.90 +/- 0.02 microB/formula unit consistent with four unpaired spins and implying a Mn3+, high-spin d4 state. XMCD measurements reveal that there is strong dichroism in the Mn L23 edge, the Sb M45 edge shows a weak dichroism indicating antialignment to the Mn, and the Yb N45 edge shows no dichroism. Comparisons of the Mn spectra with theoretical models for Mn2+ show excellent agreement. The bulk magnetization can be understood as Mn with a moment of 5 microB and a 2+ configuration, with cancellation of one spin by an antialigned moment from the Sb 5p band of the Sb4 cage surrounding the Mn.

Determination of the antimony valence state in Eu10Mn6Sb13.

The antimony-121 Mössbauer spectra of Eu10Mn6Sb13 have been measured between 2 and 295 K. Although the Zintl formalism indicates that the nine crystallographically distinct antimony sites in Eu10Mn6Sb13 should have formal valence states of -2, -1, 0, and +1, the Mössbauer spectral isomer shifts reveal that the valence states of the different sites are all quite similar and correspond to an average electronic configuration for antimony of 5s(1.7)5p(4.0). This configuration corresponds to an excess of negative charge on the antimony of 0.7 or an average valence of -0.7, a valence which is rather consistent with the average antimony valence of -0.61 obtained from the Zintl formalism for the nine antimony sites in Eu10Mn6Sb13. The spectra obtained between 90 and 295 K are more consistent with the absence rather than the presence of any transferred magnetic hyperfine field at the antimony. In contrast, the spectra obtained at 2 and 5 K reveal the presence of an average transferred magnetic hyperfine field of ca. 8 T, a field that arises from the ferromagnetic ordering of the near-neighbor manganese(II) ions.

Eu10Mn6Sb13: a new ternary rare-Earth transition-metal Zintl phase.

A new transition-metal-containing Zintl compound, Eu(10)Mn(6)Sb(13), was prepared by a high-temperature Sn-flux synthesis. The structure was determined by single-crystal X-ray diffraction. Eu(10)Mn(6)Sb(13) crystallizes in the monoclinic space group C2/m with a = 15.1791(6) A, b = 19.1919(7) A, c = 12.2679(4) A, beta = 108.078(1)*, Z = 4 (R1 = 0.0410, wR2 = 0.0920), and T = 90(2) K. The structure of Eu(10)Mn(6)Sb(13) is composed of double layers of Mn-centered tetrahedra separated by Eu(2+) cations. The double layers are composed of edge- and corner-sharing Mn-centered tetrahedra which form cavities occupied by Eu(2+) cations and [Sb(2)](4-) dumbbells. Linear [Sb(3)](5-) trimers bridging two tetrahedra across the cavity are also present. Bulk susceptibility data indicate paramagnetic behavior with a ferromagnetic component present below 60 K. Temperature-dependent electrical resistivity measurements show semiconducting behavior above 60 K (E(a)() = 0.115(2) eV), a large and unusually sharp maximum in the resistivity at approximately 40 K, and metallic behavior below 40 K. (151)Eu Mössbauer spectra confirm that the europium is divalent with an average isomer shift of -11.2(1) mm/s at 100 K; the spectra obtained below 40 K reveal magnetic ordering of six of the seven europium sublattices and, at 4.2 K, complete ordering of the seven europium sublattices.