Preparation of Biocomposites with Natural Reinforcements: The Effect of Native Starch and Sugarcane Bagasse Fibers.

Biocomposites were prepared from poly(lactic acid) and two natural reinforcements, a native starch and sugarcane bagasse fibers. The strength of interfacial adhesion was estimated by model calculations, and local deformation processes were followed by acoustic emission testing. The results showed that the two additives influence properties differently. The strength of interfacial adhesion and thus the extent of reinforcement are similar because of similarities in chemical structure, the large number of OH groups in both reinforcements. Relatively strong interfacial adhesion develops between the components, which renders coupling inefficient. Dissimilar particle characteristics influence local deformation processes considerably. The smaller particle size of starch results in larger debonding stress and thus larger composite strength. The fracture of the bagasse fibers leads to larger energy consumption and to increased impact resistance. Although the environmental benefit of the prepared biocomposites is similar, the overall performance of the bagasse fiber reinforced PLA composites is better than that offered by the PLA/starch composites.

Improved Release of a Drug with Poor Water Solubility by Using Electrospun Water-Soluble Polymers as Carriers.

In an attempt to improve the solubility of valsartan, a BCS II drug, fibers containing the drug were prepared from three water-soluble polymers, hydroxypropyl-methyl-cellulose (HPMC), polyvinyl-pyrrolidone (PVP), and polyvinyl-alcohol (PVA). Fiber spinning technology was optimized for each polymer separately. The polymers contained 20 wt% of the active component. The drug was homogenously distributed within the fibers in the amorphous form. The presence of the drug interfered with the spinning process only slightly, the diameters of the fibers were in the same range as without the drug for the HPMC and the PVA fibers, while it doubled in PVP. The incorporation of the drug into the fibers increased its solubility in all cases compared to that of the neat drug. The solubility of the drug itself depends very much on pH and this sensitivity remained the same in the HPMC and PVP fibers; the release of the drug is dominated by the dissolution behavior of valsartan itself. On the other hand, solubility and the rate of release were practically independent of pH in the PVA fibers. The different behavior is explained by the rate of the dissolution of the respective polymer, which is larger for HPMC and PVP, and smaller for PVA than the dissolution rate of the drug. The larger extent of release compared to neat valsartan can be explained by the lack of crystallinity of the drug, its better dispersion, and the larger surface area of the fibers. Considering all facts, the preparation of electrospun devices from valsartan and water-soluble polymers is beneficial, and the use of PVA is more advantageous than that of the other two polymers.

Poly-ε-Caprolactone/Halloysite Nanotube Composites for Resorbable Scaffolds: Effect of Processing Technology on Homogeneity and Electrospinning.

Polycaprolactone (PCL)/halloysite composites were prepared to compare the effect of homogenization technology on the structure and properties of the composites. Halloysite content changed from 0 to 10 vol% in six steps and homogeneity was characterized by various direct and indirect methods. The results showed that the extent of aggregation depends on technology and on halloysite content; the size and number of aggregates increase with increasing halloysite content. Melt mixing results in more homogeneous composites than the simple compression of the component powders or homogenization in solution and film casting. Homogeneity and the extent of aggregation determines all properties, including functionality. The mechanical properties of the polymer deteriorate with increasing aggregation; even stiffness depends on homogeneity. Strength and deformability decreases drastically as the number and size of aggregates increase. Not only dispersed structure, but also the physical state and crystalline structure of the polymer influence homogeneity and properties. The presence of the filler affects the preparation of electrospun fiber scaffolds as well. A part of the filler is excluded from the fibers while another part forms aggregates that complicates fiber spinning and deteriorates properties. The results indicate that spinning is easier and the quality of the fibers is better if a material homogenized previously by melt mixing is used for the production of the fibers.

Electrospun PLA Fibers Containing Metronidazole for Periodontal Disease.

PURPOSE: Electrospun PLA fiber devices were investigated in the form of fiber mats and disks. Metronidazole was used as an active agent; its concentration was 12.2 and 25.7 wt% in the devices. METHODS: The structure was studied by X-ray diffraction and scanning electron microscopy, drug release by dissolution measurements, while the antimicrobial efficiency was tested on five bacterial strains. RESULTS: The XRD study showed that the polymer was partially crystalline in both devices, but a part of metronidazole precipitated and was in the form of crystals among and within the fibers. Liquid penetration and dissolution were different in the two devices, they were faster in disks and slower in fiber mats, due to the morphology of the device and the action of capillary forces. Disks released the drug much faster than fiber mats. Although the release study indicated fast drug dissolution, the concentration achieved a plateau value in 24 hrs for the disks; the inhibition effect lasted much longer, 13 days for bacteria sensitive to metronidazole. The longer inhibition period could be explained by the slower diffusion of metronidazole located inside the fibers of the device. CONCLUSION: The results suggest that the devices may be effective in the treatment of periodontitis.