Formation of polyhydroxyalkanoates using agro and industrial waste as a substrate - a review.

In the present scenario, rising environmental concerns of non-biodegradable plastic pollution and depletion of petroleum based raw materials lead to the development of biopolymers. The biodegradability of biopolymers gives them a specific advantage for the environmental concerns. Polyhydroxyalkanoates (PHAs) are a type of biopolymers which are synthesized by microorganisms. Although there are different substrates available in pure forms which are currently used in the production of PHA, 40% of production cost depends on the expensive substrate which is a major disadvantage and make it far from many applications. The use of an inexpensive carbon source which is high in organic matter content such as waste streams of process industries can make this process viable and diminish PHA production cost. This study explores the current research initiatives on various agricultural and industrial waste feedstocks, formulations and processing conditions for producing PHA in a way that is both inexpensive and beneficial to the environment. The creation of fermentation conditions and metabolic engineering techniques for promoting microbial growth and PHA synthesis were also discussed in the review.

Structure analysis and thermal stability of PHB recovered from sugar industry waste.

The current article emphasized on cultural conditions for Alcaligenes sp. NCIM 5085 to synthesize Polyhydroxybutyrate (PHB) from sugar industry waste during batch fermentation. Alcaligenes sp. NCIM 5085 was found to grow best in conditions that included 40 g l-1 of cane molasses, 1 g l-1 of ammonium sulphate, 10% inoculum with neutral pH and 48 h of incubation time. Sudan Black B staining was employed to verify the PHB synthesis initially, and further TEM analysis was performed to confirm it. The structural analysis of recovered PHB was carried out by using GC-MS, FTIR, 1H NMR and 13C NMR analysis. The absorption peak at 1724.56 cm-1 revealed the presence of C=O (carbonyl) group by FTIR, which is an indicator of PHB presence. Furthermore, results of NMR and GC-MS analysis confirmed the recovered polymer was PHB. The thermal properties of recovered polymer were analyzed by TGA, DTG and DSC and showed thermal stability of PHB. The observed glass transient temperature (Tg) -2.8°C was within the normal PHB range of Tg. However, melting temperature of recovered PHB was 161.7°C, where the degree of crystallinity was lower than standard PHB that widens the application possibilities.