RESUMO
The current work concentrates on the fabrication of Ga doped Co0.6Cu0.4Fe2O4 nanocatalysts via sol-gel auto-combustion (SGA) for the production of green and sustainable source of energy i.e., hydrogen through photocatalytic and electrocatalytic routes. Single-phased cubic crystal structure with Fd3m geometry was observed through XRD patterns. FESEM images show the aggregated and spherical shaped grains with distinct grain boundaries and average grain size of 1.04 and 1.39 µm for the Co0.6Cu0.4Fe2O4, and Co0.6Cu0.4Ga0.02Fe1.98O4 nanomaterials. Soft magnetic behaviour with a coercivity (Hc) and saturation magnetization (Ms) of 235.32-357.26 Oe and 54.65-61.11 emu/g was obtained for the produced nanomaterials. The estimation of photocatalytic nature for generating H2 was conducted using the sacrificial agents i.e., 0.128 M Na2S and 0.079 M Na2SO3. The analysis focused on measuring the maximum H2 generation was achieved by photocatalysts throughout three consecutive 4-h cycles. Out of all compositions, Co0.6Cu0.4Ga0.02Fe1.98O4 nanomaterial have the highest photocatalytic activity of 16.71 mmol gcat-1. However, the electrocatalytic behaviour of prepared Co0.6Cu0.4GaxFe2-xO4 (x = 0.00-0.03) electrocatalysts were determined for HER (Hydrogen evolution reaction) reaction. The overpotential values of Co0.6Cu0.4Fe2O4, Co0.6Cu0.4Ga0.01Fe1.99O4, Co0.6Cu0.4Ga0.02Fe1.98O4, and Co0.6Cu0.4Ga0.03Fe1.97O4 catalysts at 10 mA cm-2 were -0.81, -0.85, -1.03, and 1.21 V, correspondingly. Thus, at cathode current density of 10 mA/cm-2, an elevation in overpotential was noted, which indicates that the undoped Co0.6Cu0.4Fe2O4 (x = 0.00) electrocatalyst have remarkable electrocatalytic HER activity. Consequently, owing to photo/electro catalytic water splitting traits, the prepared catalysts are highly efficient for the green hydrogen generation.
Assuntos
Hidrogênio , Nanoestruturas , Catálise , Eletrodos , FenótipoRESUMO
Copper and dysprosium doped NiFe2O4 magnetic nanomaterials, Ni1-xCuxDyyFe2-yO4 (x = y = 0.00, 0.01, 0.02, 0.03), was prepared by utilizing sol-gel auto-combustion approach to inspect the photodegradation of methylene blue (MB) pollutant and also, to perform the electrocatalytic water splitting and antibacterial studies. The XRD analysis reveal the growth of a single-phase spinel cubic structure for produced nanomaterials. The magnetic traits show an increasing trend in saturation magnetization (Ms) from 40.71 to 47.90 emu/g along with a decreasing behaviour of coercivity from 158.09 to 156.34 Oe at lower and higher Cu and Dy doping content (x = 0.0-0.01). The study of optical band gap values of copper and dysprosium-doped nickel nanomaterials decreased from 1.71 to 1.52 eV. This will increase the photocatalytic degradation of methylene blue pollutant from 88.57% to 93.67% under natural sunlight, respectively. These findings clearly show that under natural sunlight irradiation for 60 min, the produced N4 photocatalyst displays the greatest photocatalytic activity with a maximum removal percentage of 93.67%. The electrocatalytic characteristics of produced magnetic nanomaterials for both HER and OER were examined with a Calomel electrode taking as a reference in a 0.5 N H2SO4 and 0.1 N KOH electrolyte. The N4 electrode demonstrated considerable 10 and 0.024 mA/cm2 of current density, with onset potentials of 0.99 and 1.5 V for HER and OER and also, have tafel slopes of 58.04 and 295 mV/dec, respectively. The antibacterial activity for produced magnetic nanomaterials was examined against various bacteria (Bacillus subtilis, Staphylococcus aureus, S. typhi, and P. aeruginosa) in which N3 sample produced significant inhibition zone against gram-positive bacteria (Bacillus subtilis and Staphylococcus aureus) but no zone of inhibition against gram-negative bacteria (S. typhi and P. aeruginosa). With all these superior traits, the produced magnetic nanomaterials are highly valuable for the wastewater remediation, hydrogen evolution, and biological applications.