Simultaneous enhancement of strength and ductility via microband formation and nanotwinning in an L12-strengthened alloy.

Metallic alloys with high strength and large ductility are required for extreme structural applications. However, the achievement of ultrahigh strength often results in a substantially decreased ductility. Here, we report a strategy to achieve the strength-ductility synergy by tailoring the alloy composition to control the local stacking fault energy (SFE) of the face-centered-cubic (fcc) matrix in an L12-strengthened superlattice alloy. As a proof of concept, based on the thermodynamic calculations, we developed a non-equiatomic CoCrNi2(Al0.2Nb0.2) alloy using phase separation to create a near-equiatomic low SFE disordered CoCrNi medium-entropy alloy matrix with in situ formed high-content coherent Ni3(Al, Nb)-type ordered nanoprecipitates (∼ 12 nm). The alloy achieves a high tensile strength up to 1.6 GPa and a uniform ductility of 33%. The low SFE of the fcc matrix promotes the formation of nanotwins and parallel microbands during plastic deformation which could remarkably enhance the strain hardening capacity. This work provides a strategy for developing ultrahigh-strength alloys with large uniform ductility.

Fabrication of Porous Tantalum with Low Elastic Modulus and Tunable Pore Size for Bone Repair.

Porous tantalum (Ta) is a potential bone substitute due to its excellent biocompatibility and desirable mechanical properties. In this work, a series of porous Ta materials with interconnected micropores and varying pore sizes from 23 to 210 µm were fabricated using spark plasma sintering. The porous structure was formed by thermal decomposition of ammonium bicarbonate powder premixed in the Ta powder. The pore size and porosity were controlled by the categorized particle size of ammonium bicarbonate. The porous Ta has elastic moduli in the range of 2.1-3.2 GPa and compressive yield strength in the range of 23-34 MPa, which are close to those of human bone. In vitro, as-fabricated porous Ta demonstrates excellent biocompatibility by supporting adhesion and proliferation of preosteoblasts. In vivo studies also validate its bone repair capability after implantation in a rat femur defect model. The study demonstrates a facile strategy to fabricate porous Ta with controllable pore size for bone repair.

Occurrence of emerging bisphenol S analogues in urine from five occupational populations in South China.

Bisphenol S (BPS) and its 11 emerging analogues were investigated in 325 urine samples from five occupational populations in South China. Besides BPS, ten emerging BPS analogues were newly identified and detected in the urine. It should be noted that urinary concentrations of dominant BPS analogues of 2,4'-bis(hydroxyphenyl)sulfone (2,4-BPS), bis(3-allyl-4-hydroxyphenyl)sulfone (TGSA) and diphenylsulfone (DPS) were 1.1-2.3 times higher than that of BPS, with overall detection frequencies at 74-91 %. The median sum concentrations of the target 12 bisphenols (ng/mL) were found highest in urine from cashiers (1.12), followed by water plant staffs (0.994), teachers (0.552), doctors (0.408) and power plant staffs (0.333). The composition profile of the urinary dominant bisphenols was occupational-dependent, with 2,4-BPS accounting for 45-73 % in cashiers and power plant staffs, and with DPS and TGSA for 74-82 % among doctors, teachers and water plant staffs. Significant correlations were found among the most frequently detected bisphenols in cashiers, indicating their common application and emission pathways. The median exposures based on estimated daily intakes (EDIs, ng/kg bw/day) for the 12 bisphenols in cashiers and water plant staffs (31.6-35.6) were 1.8-3.4 times higher than those of teachers, doctors and power plant staffs (10.6-17.5). This is the first study to identify multiple emerging BPS analogues in urine from occupational populations, especially cashiers and water plant staffs.