RESUMO
Unusual buckypapers, sheets of graphene nanocarbons (GNCs) such as carbon nanotubes, were formed with GNCs directly derived from CO2 via molten carbonate electrolysis. Examples are presented for buckypapers made from CO2 using either crushed or chemically washed GNCs, epoxy-infused CNTs, or GNCs pressed directly using a hot electrolyte to remove excess electrolyte.
RESUMO
An electrosynthesis is presented to transform the greenhouse gas CO2 into an unusually thin walled, smaller diameter morphology of Carbon Nanotubes (CNTs). The transformation occurs at high yield and coulombic efficiency of the 4-electron CO2 reduction in a molten carbonate electrolyte. The electrosynthesis is driven by an unexpected synergy between calcium and metaborate. In a pure molten lithium carbonate electrolyte, thicker walled CNTs (100-160 nm diameter) are synthesized during a 4 h CO2 electrolysis at 0.1 A cm-2. At this low current density, CO2 without pre-concentration is directly absorbed by the air (direct air capture) to renew and sustain the carbonate electrolyte. The addition of 2 wt% Li2O to the electrolyte produces thinner, highly uniform (50-80 nm diameter) walled CNTs, consisting of ~ 75 concentric, cylindrical graphene walls. The product is produced at high yield (the cathode product consists of > 98% CNTs). It had previously been demonstrated that the addition of 5-10 wt% lithium metaborate to the lithium carbonate electrolyte boron dopes the CNTs increasing their electrical conductivity tenfold, and that the addition of calcium carbonate to a molten lithium carbonate supports the electrosynthesis of thinner walled CNTs, but at low yield (only ~ 15% of the product are CNTs). Here it is shown that the same electrolysis conditions, but with the addition of 7.7 wt% calcium metaborate to lithium carbonate, produces unusually thin walled CNTs uniform (22-42 nm diameter) CNTs consisting of ~ 25 concentric, cylindrical graphene walls at a high yield of > 90% CNTs.
RESUMO
An electrosynthesis is presented to transform CO2 into an unusual nano and micron dimensioned morphology of carbon, termed Carbon Nano-Scaffold (CNS) with wide a range of high surface area graphene potential usages including batteries, supercapacitors, compression devices, electromagnetic wave shielding and sensors. Current CNS value is over $323 per milligram. The morphology consists of a series of asymmetric 20 to 100 nm thick flat multilayer graphene platelets 2 to 20 µm long orthogonally oriented in a 3D neoplasticism-like geometry, and appears distinct from the honeycomb, foam, or balsa wood cell structures previously attributed to carbon scaffolds. The CNS synthesis splits CO2 by electrolysis in molten carbonate and has a carbon negative footprint. It is observed that transition metal nucleated, high yield growth of carbon nanotubes (CNTs) is inhibited in electrolytes containing over 50 wt% of sodium or 30 wt% of potassium carbonate, or at electrolysis temperatures less than 700 °C. Here, it is found that a lower temperature of synthesis, lower concentrations of lithium carbonate, and higher current density promotes CNS growth while suppressing CNT growth. Electrolyte conditions of 50 wt% sodium carbonate relative to lithium carbonate at an electrolysis temperature of 670 °C produced over 80% of the CNS desired product at 85% faradaic efficiency with a Muntz brass cathode and an Inconel anode.