Impact of the Loading Conditions and the Building Directions on the Mechanical Behavior of Biomedical ß-Titanium Alloy Produced In Situ by Laser-Based Powder Bed Fusion.

In order to simulate micromachining of Ti-Nb medical devices produced in situ by selective laser melting, it is necessary to use constitutive models that allow one to reproduce accurately the material behavior under extreme loading conditions. The identification of these models is often performed using experimental tension or compression data. In this work, compression tests are conducted to investigate the impact of the loading conditions and the laser-based powder bed fusion (LB-PBF) building directions on the mechanical behavior of ß-Ti42Nb alloy. Compression tests are performed under two strain rates (1 s-1 and 10 s-1) and four temperatures (298 K, 673 K, 873 K and 1073 K). Two LB-PBF building directions are used for manufacturing the compression specimens. Therefore, different metallographic analyses (i.e., optical microscopy (OM), scanning electron microscopy (SEM), energy-dispersive X-ray (EDX), electron backscatter diffraction (EBSD) and X-ray diffraction) have been carried out on the deformed specimens to gain insight into the impact of the loading conditions on microstucture alterations. According to the results, whatever the loading conditions are, specimens manufactured with a building direction of 45∘ exhibit higher flow stress than those produced with a building direction of 90∘, highlighting the anisotropy of the as-LB-PBFed alloy. Additionally, the deformed alloy exhibits at room temperature a yielding strength of 1180 ± 40 MPa and a micro-hardness of 310 ± 7 HV0.1. Experimental observations demonstrated two strain localization modes: a highly deformed region corresponding to the localization of the plastic deformation in the central region of specimens and perpendicular to the compression direction and an adiabatic shear band oriented with an angle of ±45 with respect to same direction.

Stress Concentration and Mechanical Strength of Cubic Lattice Architectures.

The continuous design of cubic lattice architecture materials provides a wide range of mechanical properties. It makes possible to control the stress magnitude and the local maxima in the structure. This study reveals some architectures specifically designed to reach a good compromise between mass reduction and mechanical strength. Decreased local stress concentration prevents the early occurrence of localized plasticity or damage, and promotes the fatigue resistance. The high performance of cubic architectures is reported extensively, and structures with the best damage resistance are identified. The fatigue resistance and S⁻N curves (stress magnitude versus lifetime curves) can be estimated successfully, based on the investigation of the stress concentration. The output data are represented in two-dimensional (2D) color maps to help mechanical engineers in selecting the suitable architecture with the desired stress concentration factor, and eventually with the correct fatigue lifetime.

Variations of the Elastic Properties of the CoCrFeMnNi High Entropy Alloy Deformed by Groove Cold Rolling.

The variations of the mechanical properties of the CoCrFeMnNi high entropy alloy (HEA) during groove cold rolling process were investigated with the aim of understanding their correlation relationships with the crystallographic texture. Our study revealed divergences in the variations of the microhardness and yield strength measured from samples deformed by groove cold rolling and conventional cold rolling processes. The crystallographic texture analyzed by electron back scattered diffraction (EBSD) revealed a hybrid texture between those obtained by conventional rolling and drawing processes. Though the groove cold rolling process induced a marked strengthening effect in the CoCrFeMnNi HEA, the mechanical properties were also characterized by an unusual decrease of the Young's modulus as the applied groove cold rolled deformation increased up to about 0.5 before reaching a stabilized value. This decrease of the Young's modulus was attributed to the increased density of mobile dislocations induced by work hardening during groove cold rolling processing.