Utilization of Additive Manufacturing Techniques for the Development of a Novel Scaffolds with Magnetic Properties for Potential Application in Enhanced Bone Regeneration.

This study focuses on designing and evaluating scaffolds with essential properties for bone regeneration, such as biocompatibility, macroporous geometry, mechanical strength, and magnetic responsiveness. The scaffolds are made using 3D printing with acrylic resin and iron oxides synthesized through solution combustion. Utilizing triply periodic minimal surfaces (TPMS) geometry and mask stereolithography (MSLA) printing, the scaffolds achieve precise geometrical features. The mechanical properties are enhanced through resin curing, and magnetite particles from synthesized nanoparticles and alluvial magnetite are added for magnetic properties. The scaffolds show a balance between stiffness, porosity, and magnetic responsiveness, with maximum compression strength between 4.8 and 9.2 MPa and Young's modulus between 58 and 174 MPa. Magnetic properties such as magnetic coercivity, remanence, and saturation are measured, with the best results from scaffolds containing synthetic iron oxides at 1% weight. The viscosity of the mixtures used for printing is between 350 and 380 mPas, and contact angles between 90° and 110° are achieved. Biocompatibility tests indicate the potential for clinical trials, though further research is needed to understand the impact of magnetic properties on cellular interactions and optimize scaffold design for specific applications. This integrated approach offers a promising avenue for the development of advanced materials capable of promoting enhanced bone regeneration.

Antibacterial and osteoinductive properties of wollastonite scaffolds impregnated with propolis produced by additive manufacturing.

Biocompatible ceramic scaffolds offer a promising approach to address the challenges in bone reconstruction. Wollastonite, well-known for its exceptional biocompatibility, has attracted significant attention in orthopedics and craniofacial fields. However, the antimicrobial properties of wollastonite have contradictory findings, necessitating further research to enhance its antibacterial characteristics. This study aimed to explore a new approach to improve in vitro biological response in terms of antimicrobial activity and cell proliferation by taking advantage of additive manufacturing for the development of scaffolds with complex geometries by 3D printing using propolis-modified wollastonite. The scaffolds were designed with a TPMS (Triply Periodic Minimal Surface) gyroid geometric shape and 3D printed prior to impregnation with propolis extract. The paste formulation was characterized by rheometric measurements, and the presence of propolis was confirmed by FTIR spectroscopy. The scaffolds were comprehensively assessed for their mechanical strength. The biological characterization involved evaluating the antimicrobial effects against Staphylococcus aureus and Staphylococcus epidermidis, employing Minimum Inhibitory Concentration (MIC), Zone of Inhibition (ZOI), and biofilm formation assays. Additionally, SaOs-2 cultures were used to study cell proliferation (Alamar blue assay), and potential osteogenic was tested (von Kossa, Alizarin Red, and ALP stainings) at different time points. Propolis impregnation did not compromise the mechanical properties of the scaffolds, which exhibited values comparable to human trabecular bone. Propolis incorporation conferred antibacterial activity against both Staphylococcus aureus and Staphylococcus epidermidis. The implementation of TPMS gyroid geometry in the scaffold design demonstrated favorable cell proliferation with increased metabolic activity and osteogenic potential after 21 days of cell cultures.

Calcium phosphate nanoparticles improve growth parameters and mitigate stress associated with climatic variability in avocado fruit.

The avocado cv. Hass is one of the most dynamic fruits in the world and is of particular significance in tropical areas, where climate variability phenomena have a high impact on productivity and sustainability. Nanotechnology-based tools could be an alternative to mitigate and/or adapt plants to these phenomena. Our approach was based on identifying changes in temperature and precipitation associated with climate variability in avocado areas in Colombia and proposing mitigation strategies based on the use of nanotechnology. This study had two objectives: (i) to identify variations in temperature and precipitation in avocado-producing areas in Colombia and (ii) to evaluate the effect of calcium phosphate nanoparticles (nano CP) as an alternative to reduce stress in avocados under simulate climatic variability condition. Climatic clusters were determined based on the spatial K-means method and with the climatic temporal series data (1981-2020), a time series analysis we carried out. Later changes in each cluster were simulated in growth chambers, evaluating physiological and developmental responses in avocado seedlings subjected to nanoCaP after adjusting the application form and dose. XRD diffraction shows that the calcium phosphate phases obtained by solution combustion correspond to a mixture of hydroxyapatite and witocklite nanoparticles with irregular morphologies and particle sizes of 100 nm. Three clusters explained ∼90% of the climate variation, with increases and decreases in temperature and precipitation in the range of 1-1.4 °C and 4.1-7.3% respectively. The best-fitted time series models were of stationary autoregressive integrated moving averages (SARIMA). The avocado seedlings had differential responses (P<0.05) depending on the clusters, with a decrease in physiological behavior and development between 10 and 35%. Additionally, the nanoCaP reduced the climatic stress (P< 0.05) in a range between 10 and 22.5%. This study identified the negative effect of climate variability on avocado seedlings and how nanoCaP can mitigate these phenomena.

Fabrication of polycaprolactone/calcium phosphates hybrid scaffolds impregnated with plant extracts using 3D printing for potential bone regeneration.

The increase in critical bone diseases and defects in the world's population increases the need for bone substitutes to restore form and function. Organic and inorganic scaffolds with antibacterial properties could provide advantages for bone regeneration. In this study, we obtained scaffolds of polycaprolactone (PCL) charged with calcium phosphates nanoparticles and impregnated with extracts of Colombian plants as an alternative for potential bone regeneration. Calcium phosphate nanoparticles were obtained via auto-combustion synthesis. The nanoparticles were incorporated into the PCL with a chemical dissolution-disperse process. The composite obtained was used to produce a filament to print Triply Periodic Minimal Surface (TPMS) based scaffolds. Such geometry facilitates cellular growth thanks to its interconnected porosity. The scaffolds were impregnated with extracts of Justicia cf colorifera (Acanthaceae), and Billia rosea (Sapindaceae) due to their ancestral medical applications. A physical and biological characterization was conducted. The process to print scaffolds with an enhanced geometry to facilitate the flux of biological fluids was successful. The scaffolds loaded with B. rosea showed strong antibacterial behavior, suggesting the presence of reported terpenoids with antibacterial properties. The approach used in this study evidenced promising prospects for bone defect repair.

Effects of Propolis Impregnation on Polylactic Acid (PLA) Scaffolds Loaded with Wollastonite Particles against Staphylococcus aureus, Staphylococcus epidermidis, and Their Coculture for Potential Medical Devices.

Several diseases and injuries cause irreversible damage to bone tissues, which may require partial or total regeneration or replacement. Tissue engineering suggests developing substitutes that may contribute to the repair or regeneration process by using three-dimensional lattices (scaffolds) to create functional bone tissues. Herein, scaffolds comprising polylactic acid and wollastonite particles enriched with propolis extracts from the Arauca region of Colombia were developed as gyroid triply periodic minimal surfaces using fused deposition modeling. The propolis extracts exhibited antibacterial activity against Staphylococcus aureus (ATCC 25175) and Staphylococcus epidermidis (ATCC 12228), which cause osteomyelitis. The scaffolds were characterized using scanning electron microscopy, Fourier-transform infrared spectroscopy, differential scanning calorimetry, contact angle, swelling, and degradation. Their mechanical properties were assessed using static and dynamic tests. Cell viability/proliferation assay was conducted using hDP-MSC cultures, while their bactericidal properties against monospecies cultures (S. aureus and S. epidermidis) and cocultures were evaluated. The wollastonite particles did not affect the physical, mechanical, or thermal properties of the scaffolds. The contact angle results showed that there were no substantial differences in the hydrophobicity between scaffolds with and without particles. Scaffolds containing wollastonite particles suffered less degradation than those produced using PLA alone. A representative result of the cyclic tests at Fmax = 450 N showed that the maximum strain reached after 8000 cycles is well below the yield strain (i.e., <7.5%), thereby indicating that even under these stringent conditions, these scaffolds will be able to work properly. The scaffolds impregnated with propolis showed a lower % of cell viability using hDP-MSCs on the 3rd day, but these values increased on the 7th day. These scaffolds exhibited antibacterial activity against the monospecies cultures of S. aureus and S. epidermidis and their cocultures. The samples without propolis loads did not show inhibition halos, whereas those loaded with EEP exhibited halos of 17.42 ± 0.2 mm against S. aureus and 12.9 ± 0.5 mm against S. epidermidis. These results made the scaffolds possible bone substitutes that exert control over species with a proliferative capacity for the biofilm-formation processes required for typical severe infectious processes.