Effects of proanthocyanidin-functionalized hydroxyapatite nanoparticles on dentin bonding.

OBJECTIVES: To evaluate the effect of proanthocyanidin-functionalized hydroxyapatite nanoparticles (nHAp_PA) used as pretreatment at different concentrations on the microtensile bond strength (µTBS) and endogenous enzymatic activity (MMPs) on pH-cycled dentin after 24 h and 6 months of artificial aging. MATERIALS AND METHODS: Fifty human sound dentin blocks were randomly assigned to 5 groups (n = 10): (i) negative control (no treatment); (ii) positive control (pH-cycling); (iii) pH-cycling + 2% nHAp_PA for 60s; (iv) pH-cycling + 6.5% nHAp_PA for 60s; (v) pH-cycling + 15% nHAp_PA for 60s. A self-etch adhesive was used for bonding procedures before resin composite build-ups. Specimens were tested with the µTBS test after 24 h and 6 months of laboratory storage. The proteolytic activity in each group was evaluated with gelatin zymography and in situ zymography. Data were statistically analyzed (p < 0.05). RESULTS: At 24 h, the µTBS of the experimental groups were significantly higher than the controls (p ≤ 0.001), and no differences were observed between different concentrations (p > 0.05). Artificial aging significantly decreased bond strength in all groups (p ≤ 0.008); however, nHAp_PA 2% still yielded higher bonding values than controls (p ≤ 0.007). The groups pretreated with nHAp_PA exhibited lower MMP-9 and MMP-2 activities compared to the positive control group and almost the same enzymatic activity as the negative control group. In situ zymography showed that after 6 months of aging, nHAp_PA 2% and nHAp_PA 6,5% decreased enzymatic activity as well as the negative control. CONCLUSIONS: Dentin pretreatment with nHAp_PA increased the bonding performance of a self-etch adhesive and decreased MMP-2 and MMP-9 activities after 6 months.

Structurally compromised teeth. Part I: Clinical considerations and novel classification proposal.

OBJECTIVE: A comprehensive classification of structurally compromised teeth (SCT) was introduced. CLINICAL CONSIDERATIONS: Dental injuries or operative mismanagement undermine the structural integrity of the tooth abutment, reducing its biomechanical strength and rendering restorative procedures challenging. To standardize the overall pre-operative evaluations and determine the biological and mechanical features, a classification of the coronal and cervical tooth defects, as well as an attentive analysis of the most apical location of the residual cervical tooth structure along the whole perimeter and the most coronal location of the bucco/lingual residual structure was presented. Considering the residual cervical structure, five possible clinical scenarios were individuated with respect to the gingival margin, gingival sulcus, supracrestal tissue attachment and bone crest (BC). The latter prevents the isolation procedures rendering the adhesive restorations unfeasible. Instead, the location of the most apical portion of residual cervical structure within subgingival/intrasulcular depth (>1.5 mm above BC) can be considered restorable. CONCLUSIONS: This classification is threefold: to enclose all the possible clinically encountered tooth defects, to identify the apical problems of SCT to appropriately manage the perio-restorative interfaces, and to evaluate the tooth resistance capacity of SCT, as to plan and perform the most adequate biomechanical restorative approach. CLINICAL SIGNIFICANCE: The present classification is proposed to provide a complete perspective of structurally compromised teeth to standardize the biologic and biomechanical evaluations during planning of restorative procedures.

Structurally compromised teeth. Part II: A novel approach to peripheral build up procedures.

OBJECTIVE: To introduce the "Peripheral Build-Up technique - PBUt" as a foundation restoration strategy for structurally compromised teeth (SCT). CLINICAL CONSIDERATIONS: Several strategies have been proposed over time (cervical marginal relocation, doughnut, and preformed ring techniques) to enable the management of restorative procedures in challenging situations such as the presence of deep subgingival defects. The PBUt is a versatile, completely additive direct technique that share some strategical concepts with these techniques to approach critical clinical situations while supplying a wider field of application thanks to distinct operative expedients. The clamp insertion modality, the extension of the proximal wall and the matrix customization/stabilization strategies adopted in PBUt endorse the possibility to manage the most apical and peripheral border of the residual tooth structure when located up to >1.5 mm above the bone crest. The periodontal response has to be then monitored over time. Moreover, thanks to the peripheral and apically-extended addictive approach, it allows a massive preservation of residual sound tooth structure and improves the resistance and retentive physical/geometrical features of the abutment tooth. The PBUt operative workflow is herein explained. CLINICAL SIGNIFICANCE: The Peripheral-Build-Up technique (PBUt) advocates some innovative clinical restorative steps for the management of SCT with coronal and deep subgingival defects.

Effect of adhesive strategy on resin cement bonding to dentin.

OBJECTIVE: The cement bonding strategy and the polymerization mode can influence the prognosis of indirect restorations. The microtensile bond strength (µTBS) and dentin endogenous enzymatic activity of a dual-cure resin cement (PV5) used in combination with two dentin surface conditioners (accelerator-enhancer primer, TP or universal adhesive, UA) were evaluated. MATERIALS AND METHODS: PV5 was used to lute composite overlays after dentin treatment with TP or UA. The resin cement was self-cured, SC (1 h at 37 °C) or dual-cured, DC (20 s light-cure followed by 15 min self-cure at 37°C). The µTBS test, fractographic analysis, and the in situ zymography evaluations were performed after 24 h (T0 ) or 1 yr (T12 ) of artificial storage. Data were statistically analyzed (α = 0.05). RESULTS: TP/DC obtained the highest adhesive strengths (45 ± 9 and 36.6 ± 8), while UA/SC (17 ± 8 and 11 ± 4) the lowest, both at T0 and T12 , respectively. DC resulted in superior bonding values than the SC, independent of the dentin surface treatment (p < 0.05). The type of adhesive, curing mode and aging influenced the gelatinolytic activity (p < 0.05). CONCLUSIONS: The dual-cure resin cement used in combination with its accelerator-enhancer primer showed superior bonding performances with respect to universal adhesive. Dual-curing the resin cement was determinant to enhance bonding capability over time, independent of the adhesive strategy. CLINICAL RELEVANCE: Clinicians must be aware to faithfully follow manufacturer's recommendation regarding the adhesive strategy suggested with the resin cement used.

Selective adhesive luting: A novel technique for improving adhesion achieved by universal resin cements.

OBJECTIVE: We aimed to introduce the concept of "Selective adhesive luting-SAL" which is explained through clinical steps and supported by preliminary laboratory evidence. CLINICAL CONSIDERATIONS: Cementation with rubber dam is difficult to perform in case of short abutment teeth and/or subgingival crown margins. By means of universal resin cements/universal adhesive systems, which can be employed in self-adhesive as well as adhesive luting procedures, this paper presents a novel technique allowing clinicians to perform reliable cementation where rubber dam isolation is difficult. The SAL technique entails the application of a universal adhesive system only on easily accessible abutment surfaces, enabling simultaneous adhesive and self-adhesive luting in different portions of the abutment. The SAL clinical workflow is explained through prosthodontic rehabilitation of maxillary right central incisor affected by microdontia and restored with a lithium-disilicate crown. Furthermore, our laboratory microshear bond strength study supports the rationale behind SAL application demonstrating higher bond strength even when the adhesive resin is placed only on one portion of the cementation substrate. CLINICAL SIGNIFICANCE: This article advocates the application of SAL technique in clinical situations where effective adhesive luting is uncertain, since it can improve the adhesion between the tooth and universal resin cements.

Resin composite cements: Current status and a novel classification proposal.

OBJECTIVES: Currently, a classification of resin cements that includes relatively recently formulated ("universal") cements is lacking. Furthermore, the terminology used to define different resin cements in the scientific reports is inconsistent. Accordingly, this work aims to: (i) propose a novel classification of resin composite cements; (ii) disambiguate the term "universal cements" and (iii) present an overview of the properties of these cements. METHODS: An analysis of peer-reviewed literature (PubMed search), as well as market research on definitive resin composite cements were performed. RESULTS: A tendency toward simplified and versatile luting materials was observed both in the scientific literature and on the dental market with the advent of self-adhesive/one-step resin cements. However, additional priming procedures were necessary to improve their bonding performance in certain clinical situations. Hence, several cements that can be applied both in adhesive and self-adhesive mode were introduced. These cements are associated with a universal adhesive resin, that can be used as a tooth and/or restorative material primer, without the need for other priming systems, regardless of the substrate. These systems should be considered truly universal. Therefore, we hereby suggested a new classification of resin-based cements: (1) adhesive/multi-step; (2) self-adhesive/one-step; (3) universal cements (one- or multi-step). Despite promising in vitro results, clinical trials and long-track laboratory studies are necessary to confirm the reliability of the universal cements. CONCLUSIONS: This review presented the current advances in the field of resin-based cements, which are reflected in the proposed classification. The term "universal cement" was disambiguated, which will help standardize the terminology used in published research. CLINICAL SIGNIFICANCE: The classification of resin-based cements and a better understanding of the proper terminology will help standardize the terminology in published research, as well as improve the understanding of the clinical practitioners of the different indications and possible modalities of use of the available cements.

The effect of carbodiimide on push-out bond strength of fiber posts and endogenous enzymatic activity.

BACKGROUND: To investigate the effect of 0.3 M 1-ethyl-3(3-dimethylaminopropyl) carbodiimide (EDC) aqueous solution pretreatment on push-out bond strength (PBS) and matrix-metalloproteinases (MMPs) activity within radicular dentin when different post cementation strategies were employed. METHODS: One hundred and twenty monoradicular human teeth were endodontically treated and randomly divided into six groups, depending on the cementation strategy and root dentin pretreatment (n = 20): EAR: cementation with an etch-and-rinse adhesive (LuxaBond Total Etch, DMG) and resin cement (LuxaCore Z Dual, DMG); EAR/EDC: 1 min EDC pretreatment after etching + EAR; SE: cementation with a self-etch primer (Multilink Primer, Ivoclar Vivadent) and corresponding cement (Multilink Automix, Ivoclar Vivadent); SE/EDC: self-etch primer + EDC pretreatment + SE; SA: cementation with a universal self-adhesive cement (RelyX Universal, 3 M); SA/EDC: EDC pretreatment + SA. Slices were submitted to PBS test and interfacial nanoleakage evaluation 24 h after cementation or after thermocycling (40.000 cycles, 5-55 °C). To investigate the effect of EDC on MMPs activity, 4 additional first maxillary premolars per group were processed for in situ zymography analysis. Multivariate ANOVA and post hoc Tukey tests were used to analyze PBS values. The data from in situ zymography were analyzed with Kruskal-Wallis test and Dunn's pairwise multiple comparison procedures (α = 0.05). RESULTS: The variables "EDC pretreatment", "root region" and "thermocycling" significantly influenced PBS (p < 0.05), while the variable "cementation strategy" had no influence (p > 0.05). Thermocycling significantly reduced PBS in SE and SA groups (p < 0.05). EDC was effective in preserving PBS after artificial aging. EDC pretreatment significantly reduced enzymatic activity at baseline in EAR and SE groups, and in SA group after thermocycling (p < 0.05). CONCLUSIONS: The use of EDC prevents the reduction of bond-strength values after artificial aging and silences endogenous enzymatic activity within radicular dentin when different cementation strategies were employed.

Influence of the activation mode on long-term bond strength and endogenous enzymatic activity of dual-cure resin cements.

OBJECTIVE: To investigate the long-term microtensile bond strength (µTBS), interfacial nanoleakage expression (NL), and adhesive stability of dual-cure resin cements with/out light activation to dentin. MATERIALS AND METHODS: Composite overlays (N = 20) were luted to deep dentin surfaces with RelyX Ultimate (RXU, 3M) or Variolink EstheticDC (VAR, Ivoclar-Vivadent). A universal adhesive was used for bonding procedures (iBond universal, Heraeus Kulzer). The resin cements were either self-cured (SC; 1 h at 37 °C) or dual-cured (DC; 20s light-cure followed by 15 min self-cure at 37 °C). Specimens were submitted to µTBS immediately (T0) or after 1 year of laboratory storage (T12). The fracture pattern was evaluated using scanning electron microscopy (SEM). Data were statistically analyzed with two-way ANOVA/Tukey test. Further, the NL was quantified and analyzed (chi-square test) and in situ zymography was performed to evaluate the endogenous enzymatic activity within the hybrid layer (HL) at T0 and T12 (Mann-Whitney test). The significance level for all statistical tests was set at p = 0.05. RESULTS: DC resulted in higher bond strength and decreased fluorescence at the adhesive interface, irrespective of the material and the storage period (p < 0.05). Significantly lower bonding performances (p < 0.05) and higher endogenous enzymatic activity (p < 0.05) were observed within the HL at T12 compared to T0 in all tested groups. CONCLUSIONS: Light-curing the dual-cure resin cements, more than the cement materials, accounted for good bonding performances and higher HL stability over time when used with a universal adhesive. Clinical significance The curing condition influences the bonding performances of dual-cure resin cements to dentin when used with a universal adhesive.

Does immediate dentin sealing influence postoperative sensitivity in teeth restored with indirect restorations? A systematic review and meta-analysis.

OBJECTIVE: This study comprehensively reviewed clinical trials that investigated the effect of immediate dentin sealing (IDS) technique on postoperative sensitivity (POS) and clinical performance of indirect restorations. MATERIALS AND METHODS: The systematic review was conducted according to the preferred reporting items for systematic reviews and meta-analyses statement, and was guided by the PICOS strategy. Clinical trials in which adult patients received at least one indirect restoration cemented with IDS approach and one restoration cemented following the delayed dentin sealing (DDS) were considered. RESULTS: Following title screening and full-text reading, four studies met the inclusion criteria and were included for qualitative synthesis, while two studies were selected for quantitative synthesis. According to Risk of bias-2 tool, two studies were classified as "some concerns" for the outcome POS. No statistically significant differences were found between teeth restored with indirect restorations using the IDS and DDS approach for POS (p > 0.05), neither at the baseline (very low certainty of evidence according to GRADE) nor after 2 years of follow-up (low certainty of evidence according to GRADE). CONCLUSION: There is low-certainty evidence that IDS does not reduce POS in teeth restored with indirect restorations. CLINICAL SIGNIFICANCE: There is no clinical evidence to favor IDS over DDS when restoring teeth with indirect restorations.

The Influence of Different Bleaching Protocols on Dentinal Enzymatic Activity: An In Vitro Study.

This study aimed to investigate matrix metalloproteinase (MMP) activity in human dentin using in-situ and gelatin zymography, after at-home and in-office bleaching, related to their clinical exposure times. Dentin specimens (n = 5) were treated with 35% hydrogen peroxide (50 min per session/4 sessions), 10% carbamide peroxide (180 min/21 sessions), or no treatment. All were subjected to in-situ zymography. Dentin slices were, subsequently, obtained, covered with fluorescein-conjugated gelatin, and examined with confocal laser-scanning microscopy. The fluorescence intensity was quantified and statistically analyzed using one-way ANOVA and Bonferroni tests (α = 0.05). Furthermore, gelatin zymography was performed on protein extracts obtained from dentin powder (N = 8 teeth), treated with hydrogen peroxide or carbamide peroxide, with different exposure times (10/50 min for hydrogen peroxide; 252/1260 min for carbamide peroxide). The results of the in-situ zymography showed no statistical differences between the bleached specimens and the control group, with a medium level of gelatinolytic activity expressed in the dentin tubules. The results of gelatin zymography showed an increased expression of pro-MMP-9 in carbamide peroxide groups. The expression of pro-MMP-2 decreased in all the experimental groups. The bleaching treatments performed on the enamel of sound teeth do not influence dentinal enzymatic activity. However, when unprotected dentin tissue is bleached, matrix metalloproteinases are more expressed, particularly when carbamide peroxide is used, proportional to the exposure time.

Biochemical and immunohistochemical analysis of tissue inhibitor of metalloproteinases-1 in human sound dentin.

OBJECTIVES: Matrix metalloproteases (MMPs) are a family of enzymes that operate a proteolytic activity at the level of the extracellular matrix. MMPs are regulated by tissue inhibitors of metalloproteinases (TIMPs) that can ubiquitously bind different enzyme forms. The study aims to identify a morfo-functional association between TIMP-1 and MMP-2 and -9 in human dentin. MATERIALS AND METHODS: Proteins were extracted from demineralized human sound dentin powder and centrifuged to separate two aliquots with different molecular weights of proteins, higher and lower than 30 kDa. In each aliquot, the evaluation of the presence of TIMP-1/MMP-2 and TIMP-1/MMP-9 was performed using co-immunoprecipitation/immunoblotting analysis. The distribution of TIMP-1, in association with MMP-2 and -9, was investigated using a double immunohistochemical technique. Furthermore, the activity of TIMP-1 was measured by reverse zymography, where acrylamide gel was copolymerized with gelatin and recombinant MMP-2. RESULTS: Co-immunoprecipitation/immunoblotting analysis showed the association TIMP-1/MMP-2 and TIMP-1/MMP-9 in human sound dentin. Electron microscopy evaluation revealed a diffuse presence of TIMP-1 tightly associated with MMP-2 and -9. Reverse zymography analysis confirmed that TIMP-1 present in human dentin is active and can bind different MMPs isoforms. CONCLUSIONS: The strict association of TIMP-1 with MMP-2 and -9 in situ appeared a constant finding in the human sound dentin. CLINICAL RELEVANCE: Considering the role of TIMP-1, MMP-2, and MMP-9 within the connective tissues, clinically applicable protocols could be developed in the future to increase or decrease the level of TIMPs in human dentin to regulate the activity of MMPs, contributing to reduce caries progression and collagen degradation.

The effect of chlorhexidine primer application on the clinical performance of composite restorations: a literature review.

To discuss the effectiveness of chlorhexidine (CHX) used as therapeutic dentin primer in adhesively bonded composite restorations. OVERVIEW: An electronic search in MEDLINE database, accessed through PubMed was conducted. No restrictions of languages and date of publication were made. The following key words were used: "chlorhexidine", "composite" and "composite resins." Clinical studies in which CHX was used during bonding procedures were included in this review. Six studies met the inclusion criteria. Of these, five studies were carried out on noncarious cervical lesions (NCCL). Only one study was carried out on class II preparation of permanent molars. In all studies, either etch-and-rinse and self-etch adhesive systems were used during bonding procedures. On the basis of the reviewed clinical trials, it can be concluded that CHX primer application does not seem to influence clinical outcome of composite restorations. CLINICAL SIGNIFICANCE: Current scientific evidence cannot neither strongly recommend nor discourage the application of CHX as therapeutic primer in composite restorations. Studies with longer follow-up periods with adhesive restorations placed on dentin after caries removal, rather than only on NCCL, are desirable to further investigate the therapeutic effect of CHX during bonding procedures.

Endogenous Enzymatic Activity in Dentin Treated with a Chitosan Primer.

The aim of this study was to evaluate the effect of different concentrations of chitosan polymer on dentinal enzymatic activity by means of gelatin and in situ zymography. Human dentin was frozen and ground in a miller. Dentin powder aliquots were demineralized with phosphoric acid and treated with three different concentrations of lyophilized chitosan polymer (1, 0.5 and 0.1 wt%) dissolved in distilled water. Dentin proteins were extracted from each experimental group and electrophoresed under non-reducing conditions in 10% SDS-PAGE containing fluorescein-labeled gelatin. After 48 h in the incubation buffer at 37 °C, proteolytic activity was registered under long-wave UV light scanner and quantified by using Image J software. Furthermore, additional teeth (n = 4) were prepared for the in situ zymographic analysis in unrestored as well as restored dentin pretreated with the same chitosan primers. The registered enzymatic activity was directly proportional to the chitosan concentration and higher in the restored dentin groups (p < 0.05), except for the 0.1% chitosan primer. Chitosan 0.1% only showed faint expression of enzymatic activity compared to 1% and 0.5% concentrations. Chitosan 0.1% dissolved in water can produce significant reduction in MMPs activity and could possibly contribute to bond strength preservation over time.

Effect of Chitosan as a Cross-Linker on Matrix Metalloproteinase Activity and Bond Stability with Different Adhesive Systems.

The aim of the present study was to evaluate the effect of 0.1% chitosan (Ch) solution as an additional primer on the mechanical durability and enzymatic activity on dentine using an etch-and-rinse (E&R) adhesive and a universal self-etch (SE) adhesive. Microtensile bond strength and interfacial nanoleakage expression of the bonded interfaces for all adhesives (with or without pretreatment with 0.1% Ch solution for 1 min and air-dried for 5 seconds) were analyzed immediately and after 10,000 thermocycles. Zymograms of protein extracts from human dentine powder incubated with Optibond FL and Scotchbond Universal on untreated or Ch-treated dentine were obtained to examine dentine matrix metalloproteinase (MMP) activities. The use of 0.1% Ch solution as an additional primer in conjunction with the E&R or SE adhesive did not appear to have influenced the immediate bond strength (T0) or bond strength after thermocycling (T1). Zymography showed a reduction in MMP activities only for mineralized and demineralized dentine powder after the application of Ch. Application of 0.1% Ch solution does not increase the longevity of resin-dentine bonds. Nonetheless, the procedure appears to be proficient in reducing dentine MMP activities within groups without adhesive treatments. Further studies are required to comprehend the cross-linking of Ch with dentine collagen.

The influence of bone mineral density and bisphosphonate therapy on the determinants of oral health and changes on dental panoramic radiographs in postmenopausal women.

OBJECTIVES: The aim of this study was to assess the determinants of oral health including the number of decayed, missing, and filled teeth (DMFT) and periodontal indices in postmenopausal women with osteoporosis, osteoporosis treated with bisphosphonate therapy, and control group and to examine the correlation between dental panoramic indices (Mental Index-MI, Mandibular Cortical Index-MCI) and bone mineral density in these three groups of patients. MATERIALS AND METHODS: The presented non-interventional study involved 120 postmenopausal women: women with osteoporosis (O) (n = 45), women with osteoporosis treated with bisphosphonates (OBP) (n = 45), and control group (C) (n = 30). DMFT, plaque, gingival and papilla bleeding index, pocket depth, clinical attachment loss, and the presence of periodontitis were evaluated for each patient. MI and MCI of all participants were measured on a dental panoramic radiograph. RESULTS: Group OBP showed significantly higher gingival, bleeding index and deeper pocket depth than C and/or O group. No significant differences were found in MI (p = .303) or MCI (p = .06) in all the examined groups. Also, there were no significant differences between the three groups in the presence of periodontitis as well as in the DMFT index. CONCLUSION: BP therapy could have a negative influence on periodontal health. Further, MI and MCI are not precise diagnostic tools for diagnosing low BMD in postmenopausal women. CLINICAL RELEVANCE: BP therapy could have a negative influence on the determinants of oral health in postmenopausal women with osteoporosis.

Bond Strength to Lithium-Disilicate Ceramic after Different Surface Cleaning Approaches.

PURPOSE: To evaluate the effect of different lithium-disilicate (LiSi) glass-ceramic surface decontamination procedures on the shear bond strength (SBS) to resin cement. MATERIALS AND METHODS: Seventy CAD/CAM LiSi ceramic specimens (IPS e.max CAD, Ivoclar) were cut and sintered. Fifty specimens were treated with 5% hydrofluoric acid (HF) for 20 s, while 20 were left untreated. All 70 specimens were then contaminated with human saliva and try-in silicone paste. The following surface cleaning methods were investigated (n = 10): C: water rinsing (control); PA: 37% H3PO4 etching for 20 s; E: 70% ethanol applied for 20 s; CP: cleaning paste (Ivoclean, Ivoclar) brushed for 20 s; HFSEP: self-etching ceramic primer (Monobond Etch&Prime, Ivoclar) rubbed for 20 s; HF: 5% HF applied for 20 s or no HF etching prior to contamination; SEP: self-etching ceramic primer rubbed for 20 s and no HF etching prior to contamination. Composite cylinders were created and luted with an adhesive resin cement to the decontaminated surfaces. After storage for 24 h at 37°C, the SBS test was conducted. Two fractured specimens per group were observed under SEM to perform fractographic analysis. The data were statistically analyzed with p set at <0.05. RESULTS: The type of surface cleaning approach influenced bond strength (p < 0.001). HFSEP, SEP, and HF attained higher SBS (p < 0.001) compared to other groups. None of the approaches were able to completely remove contaminants from the ceramic surfaces. SEM images showed residual traces of contaminants on CP-treated surfaces. CONCLUSIONS: The self-etching ceramic primer enhanced bond strength to contaminated LiSi ceramic surfaces, irrespective of previous treatment with hydrofluoric acid.

Cytotoxicity and microbiological behavior of universal resin composite cements.

OBJECTIVES: To investigate the cytotoxicity on human dental pulp cells (HDPCs) and Streptococcus mutans (S.mutans) biofilm formation on universal resin composite cements (UCs). METHODS: Three UCs (RelyX Universal, 3 M Oral Care - RXU; Panavia SA Cement Universal, Kuraray Noritake - PSAU; SoloCem, Coltene - SCM) and one 'gold-standard' multi-step cement (Panavia V5, Kuraray Noritake - PV5) were used following two polymerization protocols (light-cured - LC; self-cured - SC). Cytotoxicity (MTT) tests were performed after 1, 3 and 7 days of direct contact. Carboxy-2',7'-dichlorodihydrofluorescein diacetate was used to detect the release of reactive oxygen species (ROS), and interleukin 6 (IL-6) expression was analyzed by IL-6 proquantum high sensitivity immunoassay. S. mutans biofilms were grown on UCs samples in a bioreactor for 24 h, then adherent viable biomass was assessed using MTT assay. For microbiological procedures, half of UCs samples underwent accelerated aging. Data were statistically analyzed (α = 0.05). RESULTS: The highest cytotoxicity was observed for PSAU SC, RXU SC, and PV5 SC at day 1, then for SC RXU after 3 days, and SC PSAU, LC PV5 and SCM after 1-week (p < 0.05). There was no increase in IL-6 expression after 1 day, while it increased depending on the group at 3 and 7 days. The highest ROS expression after 12 h was recorded for PSAU SC, PV5 SC and PV5 LC. Biofilm formation was as follows: RXU > > PSAU = PV5 > SCM, while light-curing systematically decreased biofilm formation (≈-33 %). Aging leveled out differences between UCs and between polymerization protocols. SIGNIFICANCE: The choice of cement brand, rather than category, and polymerization protocol influence cell viability and microbiological behavior. Light-curing is beneficial for reducing the harmful pulpal effect that UCs may possess.

The influence of finishing line and luting material selection on the seating accuracy of CAD/CAM indirect composite restorations.

OBJECTIVES: This study aimed to assess the seating accuracy of resin composite CAD/CAM overlay restorations, employing various preparation designs and luting materials (pre-heated composite (HC) or resin cement (RC)). METHODS: A human molar's STL file was utilized to create 100 3D-printed resin tooth replicas, randomly distributed into 5 groups (n = 20) based on finishing line preparation designs: 1) Rounded shoulder above the dental equator - DE (SA); 2) Chamfer above the DE (CA); 3) Butt joint above the DE (BJ); 4) Rounded shoulder below the DE (SB); 5) Chamfer below the DE (CB). Digital impressions were acquired for all replicas, and restorations milled using Tetric CAD (Ivoclar Vivadent). The restorations were luted with HC (Tetric Prime, Ivoclar Vivadent) or RC (RelyX Universal, 3 M). Seating accuracy was evaluated through digital scans during try-in without any luting agent and post-cementation using a 3D analysis software (Geomagic wrap, 3D Systems). Data were statistically analyzed using Two-Way ANOVA (p < 0.05). RESULTS: The type of luting material (RC vs HC), preparation design, and their interactions significantly impacted 3D seating of the restorations (p < 0.001). HC exhibited higer volumetric increase than RC. BJ and CA designs consistently demonstrated superior seating accuracy, irrespective of the luting material used. CONCLUSIONS: The utilization of pre-heated composite resin could negatively influence the seating of overlay restorations, probably due to its higher viscosity when compared to the resin cement. However, when HC is selected as luting agent, preparation designs lacking internal angles are recommended for enhancing the precision of overlays seating.

Stresses in Premolars Restored Using Different Post-and-Core and Crown Materials: An FEA Study.

PURPOSE: The aim of the present study was to investigate the influence of three post-and-core systems and two crown materials on stresses in restored premolars using Finite Element Analysis (FEA). MATERIALS AND METHODS: A maxillary second premolar 3D model was created in SolidWorks 2014 (Dassault Systémés). Severe loss of tooth structure was simulated with six restorative options: 1) glass-fiber-reinforced composite post and composite core (GFRC)+CAD/CAM leucite-reinforced glass-ceramic crown (LRC); 2) carbon-fiberreinforced composite post and composite core (CFRC)+LRC; 3) metal cast post-and-core (MPC)+LRC 4) GFRC+CAD/CAM composite resin crown (CC); 5) CFRC+CC; 6) MPC+CC. Three-point occlusal loading (150N) was simulated and von Misses and maximum principal stresses calculated. RESULTS: Although maximum von Mises stresses in the crown and dentin were similar across groups (137.9-139.2MPa crown; 17.2-19.6 dentin), there were important differences in stress distribution in dentin. Only in MPC+CC group the maximum stresses were on the bottom of the post preparation cavity. Stress values within the posts were: CFRC(4.8MPa)>GFRC(6.7MPa)>MPC(10.3MPa). CC-restored models presented higher von Mises stresses within the post-and-core compared to the LRC groups. Maximum principal stresses were lower compared to von Mises stresses, following the same trend, and were distributed similarly in all the groups. CONCLUSIONS: Both GFRC and CFRC showed favourable stresses distribution in the dentin and restorative materials, while MPC increased stresses in core, post and post cement. The more rigid crown material seems to transmit less stresses to the underlying core and crown cement compared to CC.

Comparisons of ammonia- and water-based silver-containing solutions on dentin bonding and enzymatic activity: 1-yr evaluation.

OBJECTIVE: To evaluate the effects of an ammonia-based and a water-based silver-containing solutions on bonding performance and matrix-metalloproteinases (MMPs) activity of a universal adhesive to dentin after 1 year of artificial aging. METHODS: Mid-coronal dentin surfaces of 60 sound human molars were exposed and the following groups were formed according to the surface pre-treatment and etching mode of the universal adhesive (Zipbond Universal, SDI) (n = 10): G1) Zipbond in the self-etch mode (ZSE); G2) Riva Star (SDI) applied before ZSE; G3) Riva Star Aqua (SDI) applied before ZSE; G4) Zipbond in the etch-and-rinse mode (ZER); G5) Riva Star applied before ZER; G6) Riva Star Aqua applied before ZER. The specimens were sectioned and subjected to microtensile bond strength (µTBS) test at baseline (T0) and after 12 months (T12) of artificial storage. Scanning electron microscope (SEM) and energy dispersive spectroscopy analysis (EDS) were also conducted. Three additional molars per group were processed for the in situ zymography analysis at T0 and T12. Data were statistically analyzed (p < 0.05). RESULTS: Dentin pre-treatments and aging decreased bonding values, regardless of the etching mode (p < 0.05). No differences in µTBS were observed between the two silver-containing solutions, both at T0 and T12. Riva Star Aqua and etching significantly increased the MMPs activity, independent of the storage period (p < 0.05). SIGNIFICANCE: Dentin surface pre-treatment with silver-containing solutions negatively affects the bonding performances of resin composite restorations placed with a universal adhesive. However, the ammonia-based product Riva Star might show better stability in the long term, due to lower activation of MMPs.