Biochar can improve the mechanical properties of portland cement paste and concrete. In this work, we produced algal biochar-zinc (biochar-Zn) and algal biochar-calcium (biochar-Ca) nanocomposite particles and studied their effect on the hydration kinetics and compressive strength of cement paste. Results show that 3 wt % biochar-Zn delayed peak heat evolution during cement hydration from 8.3 to 10.0 h, while 3 wt % addition of biochar-Ca induced a minor acceleration of peak heat from 8.3 to 8.2 h. Both biochar-Zn and biochar-Ca nanocomposite particles increased the compressive strength of cement paste at 28 days by 22.6 and 17.0%, respectively. Data substantiate that retardation or minor acceleration of the reaction kinetics was due exclusively to the presence of Zn and Ca phases, respectively, while the enhanced strength was attributed to a nucleation effect induced by such phases and the internal curing effect of biochar.