Laser induced damage in coatings for cryogenic Yb:YAG active mirror amplifiers.

We report results of a study of the laser induced damage threshold (LIDT) behavior of ion beam sputtered HfO2/SiO2 multilayer coatings on Yb:YAG using 1-on-1 and N-on-1 test protocols. The tests were conducted at ambient, vacuum, and cryogenic conditions using 280 ps pulses at λ=1030nm. The 1-on-1 LIDT of antireflection (AR) stacks is found to be only slightly reduced under vacuum and cryogenic conditions, while that of high reflectivity (HR) stacks is insensitive to environmental conditions within the uncertainty of the measurements. Cryogenic N-on-1 tests show the LIDT of the HR coating is almost the same as in the 1-on-1 tests. Conversely, the cryogenic N-on-1 test of the AR coating shows damage at ∼13J/cm2, a fluence lower than the 20.4J/cm2 of 1-on-1 tests. The AR damage behavior is found to be affected by imperfections at the Yb:YAG surface. These findings show that high surface quality is required to increase energy extraction from active mirror laser amplifiers.

1.1 J Yb:YAG picosecond laser at 1 kHz repetition rate.

We demonstrate the generation of 1.1 J pulses of picosecond duration at 1 kHz repetition rate (1.1 kW average power) from a diode-pumped chirped pulse amplification Yb:YAG laser. The laser employs cryogenically cooled amplifiers to generate λ=1030nm pulses with average power of up to 1.26 kW prior to compression with excellent beam quality. Pulses are compressed to 4.5 ps duration with 90% efficiency. This compact picosecond laser will enable a variety of applications that require high energy ultrashort pulses at kilohertz repetition rates.