Oxygen Inhibition of Surface Composites and Its Correlation with Degree of Conversion and Color Stability.

This study investigated the effects of oxygen inhibition and finishing/polishing procedures on the composite resin properties. One bulk-fill and two conventional composite resins (nanoparticle and microhybrid) were evaluated. Specimens were prepared using 4 surface treatments: control, no treatment; Gly, oxygen inhibition with glycerin; FP, finishing and polishing; Gly + FP, glycerin followed by finishing and polishing. The degree of conversion (DC) was measured using Fourier Transformed Infrared Spectroscopy (FTIR) immediately and after 15 days (n=5). Color stability (ΔEab, and ΔE00) and opacity were evaluated using a spectrophotometer after 15 days of immersion in coffee, using the CIELAB system (n=5). Data were analyzed by two-way ANOVA and Tukey tests (α=0.05) and opacity by two-way repeated-measures ANOVA. Glycerin usage increased significantly the DC however had no influence on the ΔEab, ΔE00 and, opacity values. Finishing and polishing reduced ΔEab and ΔE00 values, regardless of composite resins. Microhybrid showed higher opacity, followed by the nanoparticle and bulk fill, regardless of surface treatment. Post-polymerization polishing procedures resulted in lower conversion than using an oxygen inhibitor agent (Gly condition), but similar staining caused by coffee.

Effect of different cements on the biomechanical behavior of teeth restored with cast dowel-and-cores-in vitro and FEA analysis.

PURPOSE: To test the hypothesis that the type of cement used for fixation of cast dowel-and-cores might influence fracture resistance, fracture mode, and stress distribution of single-rooted teeth restored with this class of metallic dowels. MATERIALS AND METHODS: The coronal portion was removed from 40 bovine incisors, leaving a 15 mm root. After endodontic treatment and standardized root canal relief at 10 mm, specimens were embedded in polystyrene resin, and the periodontal ligament was simulated with polyether impression material. The specimens were randomly divided into four groups (n = 10), and restored with Cu-Al cast dowel-and-cores cemented with one of four options: conventional glass ionomer cement (GI); resin-modified glass ionomer cement (GR); dual-cure resin cement (RC); or zinc-phosphate cement (ZP). Sequentially, fracture resistance of the specimens was tested with a tangential load at a 135 degrees angle with a 0.5 mm/min crosshead speed. Data were analyzed using one-way analysis of variance (ANOVA) and the Fisher test. Two-dimensional finite element analysis (2D-FEA) was then performed with representative models of each group simulating a 100 microm cement layer. Results were analyzed based on von Mises stress distribution criteria. RESULTS: The mean fracture resistance values were (in N): RC, 838.2 +/- 135.9; GI, 772.4 +/- 169.8; GR, 613.4 +/- 157.5; ZP, 643.6 +/- 106.7. FEA revealed that RC and GR presented lower stress values than ZP and GI. The higher stress concentration was coincident with more catastrophic failures, and consequently, with lower fracture resistance values. CONCLUSIONS: The type of cement influenced fracture resistance, failure mode, and stress distribution on teeth restored with cast dowel-and-cores.