In this work, we report the room-temperature synthesis of pure calcium tungstate (CaWO4) and copper-doped calcium tungstate solid solution (Ca0.99Cu0.01WO4) by using a sonochemistry method. These materials were structurally characterized by X-ray diffraction (XRD) and Raman spectroscopy. The obtained XRD patterns were submitted to a Rietveld refinement showing, in both materials, a tetragonal phase with space group and point group of I41/a and C4h6, respectively. Microscopy images of both materials, obtained by field emission scanning electron microscopy, showed spherical agglomerated structures composed by spherical nanoparticles, while calcium and tungstate elements were identified by energy-dispersive X-ray spectroscopy for pure calcium tungstate and copper, calcium, and tungstate for Ca0.99Cu0.01WO4 solid solution. The decrease of optical band gap (Egap) from 4.0 eV (CaWO4) to 3.45 eV (Ca0.99Cu0.01WO4) confirmed the substitution of calcium atoms for copper atoms in the clusters [CaO8]. Maximum photoluminescence (PL) emission was shifted from 522 nm in the pure CaWO4 to 475 nm in the Ca0.99Cu0.01WO4 solid solution. Consequently, there was an increase of PL emissions intensity in the blue and green regions of the visible spectrum, due to electronic transitions between the orbitals O 2p, Cu 3d, and W 5d.
RESUMO
In this work, we investigated the effects of chemical substitution on the structural, electronic, and optical properties of α-Ag2-2xNixWO4 (0 ≤ x ≤ 0.08) solid solutions prepared by a facile microwave-assisted hydrothermal method. The results showed that the increase of Ni concentration in α-Ag2WO4 microcrystals as a host matrix caused a morphological transformation and a shift of the electronic and optical properties. Based on first principles calculations and using Wulff's construction, particle shapes and their transformations in α-Ag2WO4 and α-Ag2-2xNixWO4 can be affected by controlling the ratios of surface energy values between the different facets. In addition, theoretical calculations revealed that Ni substitution in α-Ag2WO4 is more favorable in the Ag2 and Ag4 positions, in which the local coordination of Ag atoms corresponds to clusters with coordination numbers of seven and four, respectively. This behavior could be related to the degree of medium-range structural disorder in α-Ag2-2xNixWO4 crystals. The experimental results were correlated with theoretical simulations to achieve a deeper understanding of the relationship between morphology and properties. These results provide the basis for a rational design for the compositional modulation of structural and optical properties.