Carbon dots for virus detection and therapy.

Recent experience with the COVID-19 pandemic should be a lesson learnt with respect to the effort we have to invest in the development of new strategies for the treatment of viral diseases, along with their cheap, easy, sensitive, and selective detection. Since we live in a globalized world where just hours can play a crucial role in the spread of a virus, its detection must be as quick as possible. Thanks to their chemical stability, photostability, and superior biocompatibility, carbon dots are a kind of nanomaterial showing great potential in both the detection of various virus strains and a broad-spectrum antiviral therapy. The biosensing and antiviral properties of carbon dots can be tuned by the selection of synthesis precursors as well as by easy post-synthetic functionalization. In this review, we will first summarize current options of virus detection utilizing carbon dots by either electrochemical or optical biosensing approaches. Secondly, we will cover and share the up-to-date knowledge of carbon dots' antiviral properties, which showed promising activity against various types of viruses including SARS-CoV-2. The mechanisms of their antiviral actions will be further adressed as well. Finally, we will discuss the advantages and distadvantages of the use of carbon dots in the tangled battle against viral infections in order to provide valuable informations for further research and development of new virus biosensors and antiviral therapeutics.

Microwave Energy Drives "On-Off-On" Spin-Switch Behavior in Nitrogen-Doped Graphene.

The established application of graphene in organic/inorganic spin-valve spintronic assemblies is as a spin-transport channel for spin-polarized electrons injected from ferromagnetic substrates. To generate and control spin injection without such substrates, the graphene backbone must be imprinted with spin-polarized states and itinerant-like spins. Computations suggest that such states should emerge in graphene derivatives incorporating pyridinic nitrogen. The synthesis and electronic properties of nitrogen-doped graphene (N content: 9.8%), featuring both localized spin centers and spin-containing sites with itinerant electron properties, are reported. This material exhibits spin-switch behavior (on-off-on) controlled by microwave irradiation at X-band frequency. This phenomenon may enable the creation of novel types of switches, filters, and spintronic devices using sp2 -only 2D systems.

Effect of Nitrogen Doping and Temperature on Mechanical Durability of Silicon Carbide Thin Films.

Amorphous silicon carbide (a-SiC) films are promising solution for functional coatings intended for harsh environment due to their superior combination of physical and chemical properties and high temperature stability. However, the structural applications are limited by its brittleness. The possible solution may be an introduction of nitrogen atoms into the SiC structure. The effect of structure and composition on tribo-mechanical properties of magnetron-sputtered a-SiCxNy thin films with various nitrogen content (0-40 at.%) and C/Si close to one deposited on silicon substrates were evaluated before and after exposure to high temperatures up to 1100 °C in air and vacuum. IR transmission spectroscopy revealed formation of multiple C-N bonds for the films with N content higher than 30 at.%. Improvement of the organization in the carbon phase with the increase of nitrogen content in the a-SiCN films was detected by Raman spectroscopy. Nanoindentation and scratch test point out on the beneficial effect of the nitrogen doping on the tribo-mechanical performance of a-SiCxNy coatings, especially for the annealed coatings. The improved fracture resistance of the SiCN films stems from the formation of triple C≡N bonds for the as deposited films and also by suppression of SiC clusters crystallization by incorporation of nitrogen atoms for annealed films. This together with higher susceptibility to oxidation of a-SiCN films impart them higher scratch and wear resistance in comparison to SiC films before as well as after the thermal exposure. The best tribo-mechanical performance in term of high hardness and sufficient level of ductility were observed for the a-Si0.32C0.32N0.36 film. The enhanced performance is preserved after the thermal exposure in air (up to 1100 °C) and vacuum (up to 900 °C) atmosphere. Annealing in oxidizing atmosphere has a beneficial effect in terms of tribological properties. Harder films with lower nitrogen content suffer from higher brittleness. FIB-SEM identified film-confined cracking as the initial failure event in SiC, while it was through-interface cracking for SiCN at higher loads. This points out on the higher fracture resistance of the SiCN films where higher strains are necessary for crack formation.